Waterproof bentonite modified polyphenyl ether material for automobile plastic parts

A technology of polyphenylene ether and plastic parts, which is applied in the field of waterproof bentonite modified polyphenylene ether materials for automotive plastic parts and its preparation, can solve the problems of poor fluidity, high melt viscosity, and unusability, and achieve improved performance, Effects of chemical solvent resistance, good processability and mechanical properties

Inactive Publication Date: 2014-07-23
安徽省中日农业环保科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PPO is an amorphous polymer material. Its melt viscosity is very high and its fluidity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0009] Example

[0010] The material of this embodiment is made of the following raw materials in parts by weight: polyphenylene ether 100, p-chloro-m-xylenol 3, propyl methacrylate 10, stearic acid 5, straw ash 4, lanthanum oxide 3, bentonite 15, kaolin 4. Desulfurization gypsum 5. Epoxy linseed oil 8. Accelerator M 2. Additive 15. The polyphenylene ether is a polyphenylene ether resin with a viscosity in the range of 0.35 to 0.65 Pa·s.

[0011] The auxiliary agent is made of the following raw materials in parts by weight: clay 300, alum 5, polytetrafluoroethylene 5, silane coupling agent KH-550 2, hydroxyethyl methacrylate 8, iron slag powder 5, squid Bone powder 6, titanium diboride 2, aluminum nitride powder 4, aluminum hydroxide 8, 2,6-di-tert-butyl-p-cresol 2, clove oil 1, antioxidant 1035 1; the preparation method is to put clay into Calcined in a calciner at 740°C for 4 hours, cooled, soaked in a 12% hydrochloric acid solution for 2 hours, filtered out, washed with water,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of the high polymer materials and specifically relates to a waterproof bentonite modified polyphenyl ether material for automobile plastic parts. The material is prepared from the following raw materials in parts by weight: 100 parts of polyphenyl ether, 2-3 parts of parachlormetaxylenol, 8-10 parts of propyl methacrylate. 3-5 parts of stearic acid, 3-4 parts of straw ash, 2-3 parts of lanthanum oxide, 12-15 parts of bentonite, 2-4 parts of kaoline, 3-5 parts of flue gas desulfurization gypsum, 6-9 parts of epoxy linseed oil, 1-2 parts of accelerator M and 12-15 parts of auxiliaries. The polyphenyl ether is modified by using raw materials such as bentonite, so that the properties of the polyphenyl ether material are improved, and consequently, the polyphenyl ether material has excellent processability and mechanical property; the prepared material is high in strength, firm, wearable, waterproof and moisture-proof, easy to dye, can resist chemical solvent corrosion, is beautiful, durable, and safe and reliable to use, and thus can be widely applied to manufacturing of various automobile plastic parts, particularly plastic parts for automobile parts such as window wipers, roofs and doors.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a waterproof bentonite-modified polyphenylene ether material for automobile plastic parts and a preparation method thereof. Background technique [0002] Polyphenylene oxide (PPO) is one of the five major engineering plastics, with excellent physical and mechanical properties, heat resistance and electrical insulation, low moisture absorption and excellent creep resistance. It is widely used in auto parts and other fields. PPO is an amorphous polymer material. Its melt viscosity is very high and its fluidity is very poor. If it is not modified, it cannot be used because it cannot be processed. [0003] In order to improve the performance of polyphenylene oxide (PPO) materials and broaden the scope of use of materials, it is necessary to improve the formula of polyphenylene oxide (PPO) materials and modify the materials so that they can be widely used in various parts...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L71/12C08K13/06C08K9/06C08K9/04C08K9/00C08K9/02C08K3/34C08K5/136C08K5/101C08K5/09C08K3/22C08K3/30C08K5/1515
Inventor 章云
Owner 安徽省中日农业环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap