Novel green environmentally-friendly anti-scaling filtering material and preparation method thereof

A green, environmentally friendly and scale-inhibiting technology, which is applied to chemical instruments and methods, scale removal and water softening, and special treatment targets, can solve the problems of poor comprehensive performance, low cost, and high strength, so as to improve availability and prevent Powder shedding, high strength effect

Inactive Publication Date: 2018-10-02
QUANZHOU WANLIDE ENERGY SAVING TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the filter materials used in the fields of industrial wastewater and seawater desalination generally cannot meet the requirements of phosphorus-free, non-toxic, pol

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel green environmentally-friendly anti-scaling filtering material and preparation method thereof
  • Novel green environmentally-friendly anti-scaling filtering material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example 1

[0025] Preparation of a new type of green and environmentally friendly scale-inhibiting filter material

[0026] Prepare 200 mesh 5000g of powdery attapulgite (the attapulgite decolorizing adsorbent is purchased from Mingguang Guoxing Attapulgite Co., Ltd., model is GF-1 type), 200 mesh 4500g powdery humic acid (purchased from Lingshou County Chengheng Mineral powder factory, model FZ-1), montmorillonite powder of 600 orders 1000g (purchased from Lingshou County Jushi Mineral Products Processing Plant), powdered zeolite of 200 orders 1500g (purchased from Xinyang Xinfu Fine Bentonite Co., Ltd.), Then put the prepared powdery attapulgite, powdery humic acid, powdery montmorillonite and powdery zeolite into the mixer hopper and mix and stir evenly to obtain mixture I, then prepare 6000g liquid binder (water glass and hydroxypropyl The mass ratio of hydroxypropyl methylcellulose is 10:2, water glass is purchased from Guangzhou Baisui Chemical Co., Ltd., and th...

Example Embodiment

[0027] Example 2

[0028] Preparation of a new type of green and environmentally friendly scale-inhibiting filter material

[0029] Prepare 600 mesh 3000g powdery attapulgite (the attapulgite decolorizing adsorbent is purchased from Mingguang Guoxing Attapulgite Co., Ltd., the model is GF-2 type), 600 mesh 3500g powdery humic acid (purchased from Lingshou County Chengheng Mineral powder factory, model FZ-1), 200 mesh 500g powdered montmorillonite (purchased from Lingshou County Jushi Mineral Products Processing Plant), 600 mesh 1000g powdered zeolite (purchased from Xinyang Xinfu Fine Bentonite Co., Ltd. ), then the prepared powdery attapulgite, powdery humic acid, powdery montmorillonite and powdery zeolite are dropped into the mixer hopper and mixed and stirred evenly, to obtain mixture I, prepare 4000g liquid binder (water glass and and The mass ratio of hydroxypropyl methylcellulose is 10:4, the water glass is purchased from Guangzhou Baisui Chemical Co., Ltd., and the CA...

Example Embodiment

[0030] Example 3

[0031] Preparation of a new type of green and environmentally friendly scale-inhibiting filter material

[0032] Prepare 600 mesh 3500g powdery attapulgite (the attapulgite decolorizing adsorbent is purchased from Mingguang Guoxing Attapulgite Co., Ltd., model is GF-1 type), 600 mesh 3000g powdery humic acid (purchased from Lingshou County Chengheng Mineral powder factory, model FZ-1), 200 mesh 500g powdered montmorillonite (purchased from Lingshou County Jushi Mineral Products Processing Plant), 600 mesh 1000g powdered zeolite (purchased from Xinyang Xinfu Fine Bentonite Co., Ltd. ), then the prepared powdery attapulgite, powdery humic acid, powdery montmorillonite and powdery zeolite are dropped into the blender hopper and mixed evenly, then prepare 4000g liquid binder (water glass and hydroxypropyl methyl The mass ratio of cellulose is 10:3, the water glass is purchased from Guangzhou Baisui Chemical Co., Ltd., the CAS number is 1344-09-8, and the hydrox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a novel green environmentally-friendly anti-scaling filtering material and a preparation method thereof. The novel green environmentally-friendly anti-scaling filtering materialcomprises 30-50wt.% of powdered attapulgite with 200-600 meshes, 35-45wt.% of powdered humic acid with 200-600 meshes, 5-10% of powdered montmorillonite with 200-600 meshes, 10-15wt.% of powdered zeolite, and 40-60wt.% of a liquid adhering agent. According to the novel green environmentally-friendly anti-scaling filtering material, the raw materials collaborate with each other, so that the novelgreen environmentally-friendly anti-scaling filtering material is free from phosphorus, nontoxic, and nuisanceless, can be completely biologically degraded, is high in adhesion capacity, shows extremely high chelating capacity to ions, and is high in corrosion inhibition function, anti-scaling function, bacteria inhibiting function, smell removing function and other performance; powder is hard tofall off and dissolving is greatly prevented during use; the strength is high; and the novel green environmentally-friendly anti-scaling filtering material can be widely applied to the fields of industrial water treatment, seawater desalting, and the like; the environment is protected; and the cost is low.

Description

technical field [0001] The invention relates to a filter material, in particular to a novel green and environment-friendly scale-resisting filter material and a preparation method thereof. Background technique [0002] At present, the filter materials used in the fields of industrial wastewater and seawater desalination generally cannot meet the requirements of phosphorus-free, non-toxic, pollution-free, fully biodegradable, corrosion inhibition, scale inhibition, bacteriostasis, odor removal, high strength, and low cost. Performance requirements, poor overall performance. Contents of the invention [0003] In order to solve the disadvantages of the above-mentioned prior art, the object of the present invention is to provide a novel green and environmentally friendly anti-scaling filter material to overcome the defects in the prior art. [0004] According to the first aspect of the present invention, the present invention provides a new type of green environmental protect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F5/10C02F103/08
CPCC02F1/281C02F5/105C02F2103/08C02F2303/02C02F2303/04C02F2303/08
Inventor 汤艺文
Owner QUANZHOU WANLIDE ENERGY SAVING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap