Cleaning agent special for aluminum frame dies and preparation method thereof

A cleaning agent and mold technology, applied in the field of cleaning agents, can solve problems affecting the quality of aluminum frames, affecting the use effect, affecting production, etc., and achieve the effect of improving decontamination, metal brightness, and strong stability

Inactive Publication Date: 2018-10-02
河南颇文商贸有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the process of preparing the aluminum frame mold, it is often necessary to come into contact with a lot of impurities, including not only particle impurities, but also some impurities such as oil, which will have a certain impact on the aluminum frame mold, not only affecting its use effect, but also It will also affect the quality of the aluminum frame made, which will have a certain impact on production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] This embodiment relates to a special cleaning agent for aluminum frame molds, which includes the following raw materials in parts by weight: 15 parts of isopropanol, 8 parts of sodium silicate, 6 parts of cocamidopropyl betaine, and 7 parts of alkylbenzene sulfonate , 10 parts of stearic acid triethanolamine quaternary ammonium salt, 15 parts of organic acid, 4 parts of fatty amine polyoxyethylene ether, 2 parts of silicon dioxide, 7 parts of sodium lauryl sulfate, 3 parts of sodium oleate, 8 parts of glycerin Parts, 30 parts of softened water, 6 parts of modified sepiolite powder, 1 part of defoamer, 2 parts of lubricant, 1 part of bactericide.

[0027] Wherein, the preparation method of the modified sepiolite powder is as follows:

[0028] (1) After grinding the sepiolite into powder, mix it with 10 times the mass of water and put it into an autoclave, stir at 120°C for 1 hour, filter with suction, dry at 120°C, and crush to obtain hydrothermally modified sepiolite;

[0029...

Embodiment 2

[0038] This embodiment relates to a special cleaning agent for aluminum frame molds, including the following raw materials in parts by weight: 25 parts of isopropanol, 14 parts of sodium silicate, 13 parts of cocamidopropyl betaine, and 12 parts of alkylbenzene sulfonate , 20 parts of stearic acid triethanolamine quaternary ammonium salt, 30 parts of organic acid, 9 parts of fatty amine polyoxyethylene ether, 6 parts of silicon dioxide, 11 parts of sodium lauryl sulfate, 5 parts of sodium oleate, 14 parts of glycerin Parts, 40 parts of softened water, 12 parts of modified sepiolite powder, 2 parts of defoamer, 4 parts of lubricant, 3 parts of bactericide.

[0039] Wherein, the preparation method of the modified sepiolite powder is as follows:

[0040] (1) After grinding sepiolite into powder, mix it with 10 times the mass of water and put it into an autoclave, stir at 220°C for 3 hours, filter with suction, dry at 120°C, and crush to obtain hydrothermally modified sepiolite;

[0041...

Embodiment 3

[0050] This embodiment relates to a special cleaning agent for aluminum frame molds, which includes the following raw materials in parts by weight: 18 parts of isopropanol, 9 parts of sodium silicate, 7 parts of cocamidopropyl betaine, and 9 parts of alkylbenzene sulfonate , 12 parts of stearic acid triethanolamine quaternary ammonium salt, 20 parts of organic acid, 5 parts of fatty amine polyoxyethylene ether, 3 parts of silicon dioxide, 8 parts of sodium lauryl sulfate, 3.5 parts of sodium oleate, 9 parts of glycerin Parts, 34 parts of softened water, 9 parts of modified sepiolite powder, 1.2 parts of defoamer, 2.5 parts of lubricant, 1.4 parts of bactericide.

[0051] Wherein, the preparation method of the modified sepiolite powder is as follows:

[0052] (1) After grinding the sepiolite into powder, mix it with 10 times the mass of water and put it into an autoclave, stir at 150°C for 1.5 hours, filter with suction, dry at 120°C, and crush to obtain hydrothermally modified sepi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cleaning agent special for aluminum frame dies. The cleaning agent comprises the following raw materials by weight: 15-25 parts of isopropanol, 8-14 parts of sodium silicate,6-13 parts of cocamidopropyl betaine, 7-12 parts of alkylbenzene sulfonate, 10-20 parts of stearic acid triethanolamine ester quaternary ammonium salt, 15-30 parts of organic acid, 4-9 parts of fattyamine polyoxyethylene ether, 2-6 parts of silicon dioxide, 7-11 parts of sodium dodecyl sulfate, 3-5 parts of sodium oleate, 8-14 parts of glycerin, 30-40 parts of softened water, 6-12 parts of modified sepiolite powder, 1-2 parts of a defoamer, 2-4 parts of a lubricant, and 1-3 parts of a bactericide. The cleaning agent special for aluminum frame dies provided by the invention can effectively remove impurities and oil stains on aluminum frame surfaces, and greatly improves the cleanliness of aluminum frame dies, thereby improving the quality of the prepared aluminum frames.

Description

Technical field [0001] The invention belongs to the technical field of cleaning agents, and specifically relates to a special cleaning agent for aluminum frame molds and a preparation method thereof. Background technique [0002] In the process of preparing aluminum frames, aluminum frame molds often need to be exposed to many impurities, not only particulate impurities, but also some impurities such as oil stains, which will affect the aluminum frame mold to a certain extent, not only affecting its use effect, but also It will also affect the quality of the aluminum frame produced, which will have a certain impact on production. [0003] Therefore, to provide an aluminum frame mold cleaner that can effectively clean aluminum frame molds, effectively remove impurities and oil stains on the surface, and improve the quality of the aluminum frame produced, and a preparation method thereof are problems that the present invention urgently needs to solve. Summary of the invention [0004...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G1/24
CPCC23G1/24
Inventor 向晓霞
Owner 河南颇文商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap