Waterproof coating for decoration engineering and preparation method thereof

A waterproof coating and engineering technology, applied in the field of decorative materials, can solve the problems of difficult one-time thick film construction, high cost of waterproof coatings, harm to human health, etc., and achieve the effects of excellent bonding strength, good hydrophobic effect, and short dry time.

Inactive Publication Date: 2018-11-16
合肥语林装饰工程有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned waterproof coating also has problems such as high cost, complicated preparation process, low solid content, and more organic volatiles, which will bring difficulties to a thick film construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A waterproof coating for decoration engineering, comprising the following raw materials in parts by weight: 12 parts of modified butyl acrylate emulsion, 13 parts of ethyl silicate, 13 parts of castor oil, 14 parts of talcum powder, 11 parts of titanium dioxide, and 17 parts of graphene , 9 parts of absolute ethanol, 10 parts of dimethylethanolamine, 5 parts of dibutyltin dilaurate, 5 parts of polymerization inhibitor, 14 parts of defoamer, 12 parts of film-forming aid and 16 parts of deionized water.

[0032] A preparation method for waterproof paint for decorative engineering, comprising the following preparation steps:

[0033] a. Mix ethyl silicate and dibutyltin dilaurate into the reaction kettle, raise the temperature to 68°C, stir and react for 22min, then add graphene, talc powder and titanium dioxide in turn, raise the temperature to 76°C, and use 90r / min The reaction was stirred at a rotating speed for 15 minutes to obtain a mixture 1;

[0034] b. Add absolut...

Embodiment 2

[0043] A waterproof coating for decoration engineering, comprising the following raw materials in parts by weight: 17 parts of modified butyl acrylate emulsion, 11 parts of ethyl silicate, 15 parts of castor oil, 13 parts of talcum powder, 11 parts of titanium dioxide, and 11 parts of graphene , 10 parts of absolute ethanol, 8 parts of dimethylethanolamine, 7 parts of dibutyltin dilaurate, 5 parts of polymerization inhibitor, 14 parts of defoamer, 14 parts of film-forming aid and 16 parts of deionized water.

[0044] A preparation method for waterproof paint for decorative engineering, comprising the following preparation steps:

[0045] a. Mix ethyl silicate and dibutyltin dilaurate into the reaction kettle, raise the temperature to 68°C, stir and react for 22min, then add graphene, talc powder and titanium dioxide in turn, raise the temperature to 74°C, and use 90r / min The reaction was stirred at a rotating speed for 12 minutes to obtain a mixture 1;

[0046] b. Add absolut...

Embodiment 3

[0055] A waterproof coating for decoration engineering, comprising the following raw materials in parts by weight: 16 parts of modified butyl acrylate emulsion, 11 parts of ethyl silicate, 15 parts of castor oil, 13 parts of talcum powder, 8 parts of titanium dioxide, and 16 parts of graphene , 13 parts of absolute ethanol, 6 parts of dimethylethanolamine, 9 parts of dibutyltin dilaurate, 8 parts of polymerization inhibitor, 14 parts of defoamer, 12 parts of film-forming aid and 16 parts of deionized water.

[0056] A preparation method for waterproof paint for decorative engineering, comprising the following preparation steps:

[0057] a. Mix ethyl silicate and dibutyltin dilaurate into the reaction kettle, raise the temperature to 65°C, stir and react for 22min, then add graphene, talc powder and titanium dioxide in turn, raise the temperature to 76°C, and use 90r / min The reaction was stirred at a rotating speed for 12 minutes to obtain a mixture 1;

[0058] b. Add absolute...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a waterproof coating for decoration engineering and a preparation method thereof. The waterproof coating is prepared from the following components: a modified butyl acrylate emulsion, ethyl silicate, castor oil, talc powder, titanium dioxide, graphene, anhydrous ethanol, dimethylethanolamine, dibutyltin dilaurate, a polymerization inhibitor, a defoamer, a coalescing agent and deionized water. The waterproof coating prepared by the invention has excellent bonding strength, waterproof performance, impact resistance and stability.

Description

technical field [0001] The invention belongs to the technical field of decoration materials, and in particular relates to a waterproof coating for decoration engineering and a preparation method thereof. Background technique [0002] At present, there are two main types of waterproof materials: one is polyurethane waterproof coating, which is made of polyurethane as the basic component and additives such as coal tar and asphalt. This type of material has a dense coating film and good waterproof performance, but it contains many toxic solvents. When the smell is strong. The other is polymer cement-based waterproof coating, which is a waterproof coating composed of organic liquid material and inorganic powder. Excellent in stability, non-toxic and environmentally friendly. However, the current polymer cement-based waterproof coatings have poor impermeability and short impermeability time, are prone to aging, and are prone to leakage during use. [0003] The publication numb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/08C09D7/61C09D7/65C08F265/04C08F230/08C08F2/30C08F2/26
CPCC08F2/26C08F2/30C08F265/04C08K2003/2241C09D7/61C09D7/65C09D133/08C08L91/00C08K13/02C08K3/34C08K3/042C08K3/22C08F230/08
Inventor 孙康
Owner 合肥语林装饰工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap