Soybean oil-based environment-friendly offset rotary news ink and preparation process thereof

A preparation process and environment-friendly technology, applied in the field of printing ink, can solve the problems of the environment, air, ecological pollution, health hazards, high VOC emissions, etc., and achieve the effect of increasing bright color, saving energy and prolonging the preparation time

Inactive Publication Date: 2018-11-27
JIANGSU ZHONGRUN INK
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the mineral oil system offset rotary press inks currently on the market not only contain a high proportion of mineral oil, resulting in higher VOC emissions, but also cause serious pollution to the environment, atmosphere, and ecology, and the PAH (more Cycloaromatic hydrocarbons), a strong carcinogen, cause greater harm to health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soybean oil-based environment-friendly offset rotary news ink and preparation process thereof
  • Soybean oil-based environment-friendly offset rotary news ink and preparation process thereof
  • Soybean oil-based environment-friendly offset rotary news ink and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1. Preparation of high viscosity rosin modified phenolic resin

[0035]In a reaction kettle with condensation, reflux device and nitrogen protection at normal pressure, in parts by weight, slowly add 4 parts of p-tert-butylphenol and formaldehyde to 54.5 parts of melted rosin liquid at 200-230 °C for condensation 40.5 parts of condensate of p-tertoctylphenol and formaldehyde react with it; after about 1 hour, heat up to 235-245°C, add 3 parts of pentaerythritol and 0.5 part of glycerin, stir well and add 0.31 parts of p-toluenesulfonate dropwise Acid, the temperature rises to 245-250°C for esterification reaction; take a sample after two hours, when AV=30, add 1.5 parts of p-tertoctylphenol and formaldehyde condensate to continue the reaction until the acid value of the reactant: AV≤ 25mgKOH / g, at this time, the viscosity of the reactant is 12000-18000mpa s / 25°C, and the n-heptane tolerance is ≥11ml / 2g; the temperature is lowered to 130°C, and a high-viscosity rosin-mod...

Embodiment 2

[0046] 1. Preparation of high viscosity rosin modified phenolic resin

[0047] In the reaction kettle with condensation, reflux device and nitrogen protection at normal pressure, in parts by weight, slowly add 5.4 parts of nonylphenol and formaldehyde condensate, 33.7 parts of rosin liquid at 200-230 °C in parts by weight react with the condensate of p-tert-octylphenol and formaldehyde; after about 1 hour, raise the temperature to 235-245°C, add 3 parts of glycerol and 0.5 part of glycerin, stir evenly, add 0.31 parts of methane dropwise, and the temperature rises to Carry out esterification reaction at 245-250°C; take a sample after two hours, when AV=30, add 2.5 parts of p-tertoctylphenol and formaldehyde condensate to continue the reaction, take a sample after 4 hours and measure until the acid value of the reactant is: AV≤25mgKOH / g, at this time, the viscosity of the reactant is 12000-18000mpa s / 25°C, the n-heptane tolerance is ≥11ml / 2g, the temperature is lowered to 130°C...

Embodiment 3

[0058] 1. Preparation of high viscosity rosin modified phenolic resin

[0059] In a reaction kettle equipped with condensation, reflux device and nitrogen protection at normal pressure, in parts by weight, slowly add 4.5 parts of condensation products of dodecylphenol and formaldehyde to 54 parts of melted rosin liquid at 200-230 °C , 33.7 parts of the condensate of p-tert-octylphenol and formaldehyde react with it; after about 1 hour, the temperature is raised to 235-245 °C, and 2.7 parts of trimethylolpropane and 0.5 parts of glycerin are added, and 0.31 parts are added dropwise after stirring Ethane, the temperature rises to 245-250 °C for esterification; take a sample after two hours, when AV=30, add 0.5 parts of p-tertoctylphenol and formaldehyde condensate to continue the reaction, take a sample after 4 hours, Until the acid value of the reactant: AV≤25mgKOH / g, the viscosity of the reactant at this time is 12000-18000mpa s / 25°C, the tolerance of n-heptane is ≥11ml / 2g, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flash pointaaaaaaaaaa
flash pointaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses soybean oil-based environment-friendly offset rotary news ink and a preparation process thereof. The ink comprises the following raw materials in parts by weight: 15.6-17.2 parts of an organic pigment, 28.8-33.5 parts of high-viscosity soybean oil-based resin oil, 35.5-41.8 parts of low-viscosity soybean oil-based resin oil, 3.5-8.2 parts of stuffing and 3.5-5.5 parts of anauxiliary, wherein the high-viscosity soybean oil-based resin oil comprises the following raw materials: 40-40.5 parts of high-viscosity rosin modified phenolic resin and 59-60 parts of soybean oil;and the low-viscosity soybean oil-based resin oil comprises the following raw materials: 33-37 parts of low-viscosity rosin modified phenolic resin and 65-68 parts of soybean oil. The ink disclosed bythe invention is low in cost, good in oil solubility, economic and practical, and is capable of reducing the waste discharge of various processes, decreasing the volatile organic compound componentsof printing ink, reducing the pollution to the atmospheric environment, reducing the cost of ink formula.

Description

technical field [0001] The invention relates to the technical field of printing inks, in particular to a soybean oil-based environment-friendly offset rotary news ink and a preparation process thereof. Background technique [0002] For existing printing inks, it is not only necessary to pursue high efficiency and high selectivity, but also to pursue the "greening" of the product in the reaction process. This "green and environmentally friendly product" should promote the high reaction rate of chemical products. ; Fewer by-products, low energy consumption, lower raw materials, but also require reaction conditions, reaction medium and the generated products are low or non-toxic, so it is of great significance to solve environmental pollution. [0003] However, the mineral oil system offset rotary press inks currently on the market not only contain a high proportion of mineral oil, resulting in higher VOC emissions, but also cause serious pollution to the environment, atmospher...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/06C09D11/103C08G8/34C08G8/32C09D11/033
CPCC08G8/32C08G8/34C09D11/033C09D11/06C09D11/103
Inventor 刘志慧
Owner JIANGSU ZHONGRUN INK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap