A kind of high dielectric X8R ceramic dielectric material and preparation method thereof

A ceramic dielectric and high dielectric technology, applied in the field of ceramic dielectric materials, can solve the problems of high sintering temperature, low dielectric constant and high loss, and achieve the effect of high dielectric constant, high dielectric constant and low dielectric loss

Active Publication Date: 2021-04-23
TAIYUAN UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, more X8R ceramic capacitor materials are reported, including tungsten bronze structure ceramic system, lead-based relaxor ferroelectric ceramic system and BaTiO 3 The base ferroelectric ceramic system is a dielectric ceramic material, but these ceramic materials contain a large amount of heavy metal lead, high sintering temperature, low dielectric constant and high loss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high dielectric X8R ceramic dielectric material and preparation method thereof
  • A kind of high dielectric X8R ceramic dielectric material and preparation method thereof
  • A kind of high dielectric X8R ceramic dielectric material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A preparation method of high dielectric X8R ceramic dielectric material, comprising the following steps:

[0026] (1) the raw material K 2 CO 3 , SrCO 3 and Nb 2 o 5 According to formula K 2 Sr 4 Nb 6 o 20 , carry out batching ball milling, heat up to 1100°C, keep warm for 2-4 hours, and obtain frit A;

[0027] (2) According to the mass percentage, 5-20% Sc 2 o 3 Carry out secondary batching with 80-95% frit A to obtain batching B;

[0028] (3) Ball mill ingredient B, add 5-8wt% binder of ingredient B to granulate, press into a green body, raise the temperature to 400-500°C, then raise the temperature to 1220°C-1250°C for 1 hour, and cool it to obtain High dielectric X8R ceramic dielectric material.

[0029] In the present invention, the binder added in step (3) will volatilize in the subsequent heating process, and the sintering process in step (3) of the present invention is mainly for the purpose of making the ceramic dielectric material dense.

[0030] ...

Embodiment 1

[0046] K 2 CO 3 , SrCO 3 and Nb 2 o 5 According to formula K 2 Sr 4 Nb 6 o 20 , for batching, ball milling on a ball mill with a rotating speed of 400r / min for 6 hours, drying in a 3.3kw ordinary oven at 100°C, and passing through 250 holes / cm 2 Sieve the sample, raise the temperature to 1100°C at 5°C / min, and keep the temperature at 1100°C for 3 hours to obtain frit A.

[0047] For secondary batching, follow 95% frit A and 5% Sc 2 o 3 Mix evenly, add deionized water, mill on a ball mill at a speed of 400r / min for 8 hours, dry at 120°C, pass through 250 holes / cm 2 Sieve the sample, add 8wt% paraffin to granulate, press into a green body, first heat up to 450°C at a heating rate of 2°C / min, then heat to 1220°C at a heating rate of 10°C / min for firing, and keep warm for 1 hour. After cooling, a ceramic dielectric material is obtained.

[0048] The test result (test frequency is 1KHz) of the dielectric property of above-mentioned embodiment ceramic dielectric material...

Embodiment 2

[0052] K 2 CO 3 , SrCO 3 and Nb 2 o 5 According to formula K 2 Sr 4 Nb 6 o 20 , for batching, ball milling on a ball mill with a rotating speed of 400r / min for 6 hours, drying in a 3.3kw ordinary oven at 100°C, and passing through 250 holes / cm 2 Sieve the sample, raise the temperature to 1100°C at 5°C / min, and keep the temperature at 1100°C for 3 hours to obtain frit A.

[0053] For secondary batching, according to 90% frit A and 10% Sc 2 o 3 Mix evenly, add deionized water, mill on a ball mill at a speed of 400r / min for 8 hours, dry at 120°C, pass through 250 holes / cm 2 Sieve the sample, add 8wt% paraffin wax to granulate, press into a green body, first heat up to 450°C at a heating rate of 2°C / min, then heat to 1230°C at a heating rate of 10°C / min for firing, and keep warm for 1 hour. After cooling, a ceramic dielectric material is obtained.

[0054] The test result (test frequency is 1KHz) of above-mentioned embodiment dielectric property sees table 2 and figu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
dielectric lossaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of ceramic dielectric materials, in particular to a high-dielectric X8R ceramic dielectric material and a preparation method thereof. is composed of 5‑20% by weight Sc 2 o 3 and 80‑95% by weight of K 2 Sr 4 Nb 6 o 20 consist of. High dielectric X8R ceramic dielectric material provided by the present invention, K 2 Sr 4 Nb 6 o 20 The dielectric ceramic has a moderate sintering temperature, generally around 1250°C, a high dielectric constant, adjustable capacity temperature coefficient and low loss, and is a dielectric ceramic material with excellent performance. The present invention chooses K 2 Sr 4 Nb 6 o 20 system, take the addition of Sc 2 o 3 The method of doping modification makes it meet the performance X8R standard, and at the same time has the advantages of high dielectric constant, low dielectric loss, lead-free and environmental protection.

Description

technical field [0001] The invention relates to the field of ceramic dielectric materials, in particular to a high-dielectric X8R ceramic dielectric material and a preparation method thereof. Background technique [0002] With the development of integrated circuits, electronic communication equipment terminals are developing towards miniaturization. Chip multilayer ceramic capacitors can well adapt to this trend, and thus have been widely used. And with the development of technology, its superior performance is becoming more and more obvious, and there is a tendency to gradually replace tantalum capacitors and electrolytic capacitors. The world's annual market sales are hundreds of billions, widely used in various surface mount circuits of electronic information products [0003] The military and aerospace fields have always been the main battlefield for advanced countries to demonstrate their strength, and it is also the place where high and new technologies are first appl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01B3/12C04B35/495
CPCC04B35/495C04B2235/3224C04B2235/442C04B2235/96
Inventor 张永刚张永强
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap