Set retarding reinforcing agent for permeable concrete and method for preparing set retarding reinforcing agent

A technology of permeable concrete and reinforcing agent, applied in the field of concrete, can solve the problems of impaired fluidity of concrete, loss of working performance of slurry, large time loss of concrete moisture, etc., to ensure strength, enhance viscosity, and reduce moisture. effect of loss

Inactive Publication Date: 2019-03-19
江苏光大生态工程技术有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the permeable concrete in this invention is transported over a long distance and stirred for a long time, the water content of the concrete that has been stirred for a long time will lose a lot, the heat of hydration time will be prolonged, the slurry of the concrete will be thickened, and the fluidity of the concrete will be severely damaged. , the slurry itself loses its working performance and will gradually sink to the bottom

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Set retarding reinforcing agent for permeable concrete and method for preparing set retarding reinforcing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A retarding enhancer for permeable concrete, consisting of the following mass fractions: polycarboxylate superplasticizer 5%, methyl cellulose ether 3%, mineral powder 10%, lignocellulose 15%, fly ash 9 %, wood resin salt 6%, silicon dioxide 15%, maltodextrin 7%, spherical inorganic material 30%, among which, spherical inorganic material is composed of the following mass fractions: calcium oxide 58%, silicon dioxide 22% %, quartz sand 11%, alumina 5.5% and sodium oxide 3.5%.

Embodiment 2

[0020] A retarding enhancer for permeable concrete, consisting of the following mass fractions: 7% naphthalene-based water reducer, 4% ethyl cellulose ether, 12% mineral powder, 15% lignocellulose, and 9% fly ash , 5% synthetic detergent, 17% silicon dioxide, 6% water-soluble starch, and 25% spherical inorganic materials, among which, the spherical inorganic materials are composed of the following mass fractions: calcium oxide 58%, silicon dioxide 22% , 11% quartz sand, 5.5% alumina and 3.5% sodium oxide.

Embodiment 3

[0022] A retarding enhancer for permeable concrete, consisting of the following mass fractions: 8% sulfamic acid water reducer, 5% polyvinyl alcohol, 13% mineral powder, 15% lignocellulose, 9% fly ash, 8% lignosulfonate, 16% silicon dioxide, 6% sodium humate, 20% spherical inorganic material, among which, the spherical inorganic material is composed of the following mass fractions: calcium oxide 58%, silicon dioxide 22%, quartz sand 11%, alumina 5.5% and sodium oxide 3.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a set retarding reinforcing agent for permeable concrete. The set retarding reinforcing agent is characterized in that the set retarding reinforcing agent comprises, by weight,5-8% of water reducing agents, 3-5% of set retarders, 10-15% of mineral powder, 20-28% of anti-crack components, 5-8% of air entraining agents, 15-20% of silicon dioxide, 5-8% of water-retaining agents and 20-30% of spherical inorganic substance materials; the spherical inorganic substance materials comprise, by weight, 58% of calcium oxide, 22% of silicon dioxide, 5.5% of aluminum trioxide, 3.5%of sodium oxide and 11% of quartz sand. The set retarding reinforcing agent has the advantages that the excellent flowability and workability of permeable concrete grout can be kept in the time of approximately 2.5 h when the set retarding reinforcing agent is used, and long-acting water retention effects can be realized.

Description

technical field [0001] The invention belongs to the technical field of concrete, and in particular relates to a retarding enhancer for permeable concrete and a preparation method thereof. Background technique [0002] Permeable concrete has good water permeability, high water storage capacity and good decoration. It is a new type of material worth promoting in the construction of "sponge city". Permeable concrete is not mixed with fine aggregate, and is made by mixing cementitious material, coarse aggregate, admixture and water in a certain proportion, and is called sand-free permeable concrete. The characteristic of permeable concrete is that it does not contain fine aggregate, and single-size coarse aggregate is used as the skeleton. A thin layer of cement slurry is wrapped on the surface of the coarse aggregate particles, which acts as a cementing layer between the aggregate particles to form a skeleton-pore structure. porous concrete material. For example, patent 10816...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/38C04B103/22
CPCC04B40/0039C04B2103/22C04B2103/302C04B24/383C04B18/141C04B18/08C04B24/24C04B14/06C04B22/064C04B14/303C04B22/062C04B2103/0068C04B24/38C04B24/2623C04B24/18
Inventor 谢波
Owner 江苏光大生态工程技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap