A technology of grouting materials and coagulation accelerators, which is applied in the field of building materials, can solve problems such as long coagulation time, and achieve the effects of improving the cohesive force of the hole wall, good economic benefits, and improving compressive strength

Inactive Publication Date: 2019-04-12
SHENZHEN WEITENAI NEW MATERIAL CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to solve these problems, people adopt grouting technology for reinforcement and plugging. However, the e

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick-setting type adjustable gel grouting material and application thereof
  • Quick-setting type adjustable gel grouting material and application thereof
  • Quick-setting type adjustable gel grouting material and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Add 30 parts of water and 70 parts of river sand / artificial sand / quartz sand to a fast-setting adjustable grouting material of the present invention to obtain a sand-containing slurry body, which specifically includes the following components in parts by weight:

[0025]

[0026]

[0027] In this real-time example, the water reducer is a polycarboxylate water reducer, a melamine water reducer or a naphthalene-based water reducer.

[0028] The thickener is hydroxypropylmethylcellulose or hydroxymethylpropylcellulose.

[0029] The coagulant is lithium carbonate or calcium formate.

[0030] The retarder is boric acid or citric acid or tartaric acid.

[0031] The tackifier is glue essence (PVA or PVE).

[0032] The water retaining agent is polyacrylamide.

[0033] Table 1 shows the test results of various indicators of a fast-setting adjustable-setting grouting material in Example 1.

[0034]

Embodiment 2

[0036] Add 30 parts of water and 70 parts of river sand / artificial sand / quartz sand to a fast-setting adjustable grouting material of the present invention to obtain a sand-containing slurry body, which specifically includes the following components in parts by weight:

[0037]

[0038] The cement is sulphoaluminate cement.

[0039] The water reducer is polycarboxylate water reducer, melamine water reducer or naphthalene water reducer.

[0040] The thickener is hydroxypropylmethylcellulose or hydroxymethylpropylcellulose.

[0041] The coagulant is lithium carbonate or calcium formate.

[0042] The retarder is boric acid or citric acid or tartaric acid.

[0043] The tackifier is glue essence (PVA or PVE).

[0044] The water retaining agent is polyacrylamide.

[0045] Table 2 shows the test results of various indicators of the fast-setting anchor grouting material in Example 2.

[0046]

Embodiment 3

[0048] Add 30 parts of water and 70 parts of river sand / artificial sand / quartz sand to a fast-setting adjustable grouting material of the present invention to obtain a sand-containing slurry body, which specifically includes the following components in parts by weight:

[0049]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a quick-setting type adjustable gel grouting material and application thereof. The quick-setting type adjustable gel grouting material comprises the following components in parts by weight: 100 parts of cement, 0.05-0.8 part of a water reducer, 0.05-0.8 part of a thickening agent, 0.06-0.8 part of a coagulant, 0.07-0.9 part of a retarder, 0.05-0.8 part of a tackifier and 0.01-1 part of a water-retaining agent, wherein the cement is a sulfur-lithium-acid salt cement; the water reducing agent is a polycarboxylate water reducer, a melamine water reducer or a naphthalene water reducer; wherein the thickening agent is hydroxypropyl methyl cellulose or hydroxymethyl propyl cellulose; the coagulant is aluminum carbonate or calcium formate; the retarder is boric acid or citric acid or tartaric acid; and the tackifier is glue essence ( with the component of PVA or PVE). According to the anchor rod grouting material disclosed by the invention, the initial setting can be realized within 20 minutes, and middle setting can be realized within 25-40 minutes, so that blasting operation and engineering construction in a tunnel are synchronously carried out, the constructionprogress is improved, and good economic benefits are achieved.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a fast-setting adjustable setting grouting material and its application. Background technique [0002] my country is the country with the largest tunnel project scale, the largest number and the fastest construction speed in the world. By the end of 2016, 14,040km / 15,181 road tunnels had been built, and by the end of 2017, 15,781km / 14,700 railway tunnels had been built. By 2020, the mileage of my country's high-speed railways will reach 30,000 kilometers (the existing 22,000 kilometers). Kilometers; 150,000 kilometers of highways will be built (the existing 131,000 kilometers), and 19,000 kilometers will need to be added. In addition, the plan also pointed out that the transportation development in the central and western regions has obvious shortcomings and is relatively lagging behind, and the construction of corridors in the central and western regions should be str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/06C04B111/70
CPCC04B28/065C04B2111/70C04B2201/52C04B14/06C04B14/068C04B2103/302C04B24/383C04B2103/12C04B2103/22C04B2103/44C04B24/2652
Inventor 林英男
Owner SHENZHEN WEITENAI NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap