A kind of high-efficiency energy storage linear dielectric ceramic material and preparation method thereof

A dielectric ceramic and linear electric technology, applied in the field of linear dielectric ceramic materials, can solve the problem of low breakdown strength

Active Publication Date: 2021-08-20
SHAANXI UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the ceramic dielectric material has a high dielectric constant, but the breakdown strength is generally low, and in a single material, it is generally difficult to obtain high dielectric constant and high breakdown strength at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-efficiency energy storage linear dielectric ceramic material and preparation method thereof
  • A kind of high-efficiency energy storage linear dielectric ceramic material and preparation method thereof
  • A kind of high-efficiency energy storage linear dielectric ceramic material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The chemical formula of the linear dielectric ceramic material is: Ca 0.6 Sr 0.4 Ti 1-x Zr xo 3 , wherein x represents the mole percentage, and x=0.

[0033] The above Zr-doped Ca 0.6 Sr 0.4 TiO 3 A preparation method for a linear dielectric ceramic material, comprising the following steps:

[0034] (1) According to the chemical formula Ca 0.6 Sr 0.4 Ti 1-x Zr x o 3 (x=0) will analyze pure SrCO 3 , CaCO 3 、TiO 2 After preparation, it is uniformly mixed by ball milling, then dried, sieved, and then pre-calcined to obtain a block solid;

[0035] (2) After crushing the massive solid, ball milling is carried out again, and the product is sieved to obtain Ca 0.6 Sr 0.4 TiO 3 Powder;

[0036] (3) Ca will be obtained 0.6 Sr 0.4 TiO 3 For the powder, weigh 0.4-0.45g per portion, then pour it into the mold, apply a force of 600N, and demould the formed disc to obtain a sample with a good shape;

[0037] (4) Place the wafer in the rubber sleeve, use vacuum ...

Embodiment 2

[0044] The chemical formula of the linear dielectric ceramic material is: Ca 0.6 Sr 0.4 Ti 1-x Zr x o 3 , wherein x represents a mole percentage, and x=0.1.

[0045] The above Zr-doped Ca 0.6 Sr 0.4 TiO 3 A preparation method for a linear dielectric ceramic material, comprising the following steps:

[0046] (1) According to the chemical formula Ca 0.6 Sr 0.4 Ti 1-x Zr x o 3 (x=0.1) will analyze pure SrCO 3 , CaCO 3 、TiO 2 , ZrO 2 After preparation, it is uniformly mixed by ball milling, then dried, sieved, and then pre-calcined to obtain a block solid;

[0047] (2) After crushing the massive solid, ball milling is carried out again, and the product is sieved to obtain Ca 0.6 Sr 0.4 Ti 0.9 Zr 0.1 o 3 Powder;

[0048] (3) Ca will be obtained 0.6 Sr 0.4 Ti 0.9 Zr 0.1 o 3 For the powder, weigh 0.4-0.45g per portion, then pour it into the mold, apply a force of 600N, and demould the formed disc to obtain a sample with a good shape;

[0049] (4) Place the...

Embodiment 3

[0056] The chemical formula of the linear dielectric ceramic material is: Ca 0.6 Sr 0.4 Ti 1-x Zr x o 3 , wherein x represents a mole percentage, and x=0.2.

[0057] The above Zr-doped Ca 0.6 Sr 0.4 TiO 3 A preparation method for a linear dielectric ceramic material, comprising the following steps:

[0058] (1) According to the chemical formula Ca 0.6 Sr 0.4 Ti 1-x Zr x o 3 (x=0.2) will analyze pure SrCO 3 , CaCO 3 、TiO 2 , ZrO 2 After preparation, it is uniformly mixed by ball milling, then dried, sieved, and then pre-calcined to obtain a block solid;

[0059] (2) After crushing the massive solid, ball milling is carried out again, and the product is sieved to obtain Ca 0.6 Sr 0.4 Ti 0.8 Zr 0.2 o 3 Powder;

[0060] (3) Ca will be obtained 0.6 Sr 0.4 Ti 0.8 Zr 0.2 o 3 For the powder, weigh 0.4-0.45g per portion, then pour it into the mold, apply a force of 600N, and demould the formed disc to obtain a sample with a good shape;

[0061] (4) Place the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
energy densityaaaaaaaaaa
energy densityaaaaaaaaaa
energy densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-efficiency energy storage linear dielectric ceramic material. The preparation method of the material is as follows: firstly, SrCO 3 , CaCO 3 、TiO 2 and ZrO 2 As raw material, according to the chemical formula Ca 0.6 Sr 0.4 Ti 1‑x Zr x o 3 Proportioned materials are taken, and the powder is mixed by wet ball milling. The dried powder is pre-calcined at 1200°C for 2 hours, and then passed through secondary ball milling, sieving and molding, and finally sintered at 1390-1550°C for 2 hours. desired linear dielectric ceramic material. The preparation process of the ceramic material prepared by the present invention is simple, the raw material price is low, and the production cost is low. At room temperature, a linear electric hysteresis loop can be obtained, and the highest energy storage density can reach 2.05J / cm 3 , is undoped SrTiO 3 The energy storage density is 2.9 times, and the energy storage efficiency is guaranteed to be above 95%.

Description

technical field [0001] The invention belongs to the technical field of linear dielectric ceramic materials, and relates to a Zr-doped Ca 0.6 Sr 0.4 TiO 3 Linear dielectric ceramic material with high energy storage efficiency and preparation method thereof. Background technique [0002] With the rapid development of pulse power technology in the fields of hybrid electric vehicles, aerospace and oil drilling, the requirements of "high temperature, high energy density and high reliability" have been put forward for energy storage dielectric capacitors. However, the performance of energy storage dielectric capacitors mainly depends on the energy storage dielectric materials used. With the development of miniaturization of pulsed power sources, the development of solid-state energy storage dielectric materials has been paid more and more attention. Among them, the ceramic dielectric material has a high dielectric constant, but the breakdown strength is generally low, and in a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/49C04B35/622
CPCC04B35/49C04B35/622C04B2235/3208
Inventor 蒲永平王雯郭旭史瑞科杨梦蝶李经纬师裕
Owner SHAANXI UNIV OF SCI & TECH