A matte paint protection film

A technology of protective film and matte paint, applied in the direction of film/flake adhesives, coatings, polyurea/polyurethane coatings, etc. Protective film and other issues to achieve the effect of improving anti-fouling performance, good matte effect and good durability

Active Publication Date: 2021-04-30
HEFEI LUCKY SCI & TECH IND
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But this method is only suitable for UV-cured coatings, and the self-healing effect of existing UV-cured self-healing coatings is far from the effect of heat-cured self-healing coatings, and cannot be applied to automotive paint surfaces protective film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A matte paint protection film
  • A matte paint protection film
  • A matte paint protection film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] (1) Preparation of semi-finished paint protection film:

[0040] On a translucent polyester release film with a thickness of 30 μm, use known technology to obtain an assembly glue with a thickness of 10 μm, and then laminate it with a polyvinyl chloride film with a thickness of 100 μm, and roll it to obtain a semi-finished paint protection film for use. .

[0041] (2) Preparation of self-healing coating solution:

[0042]

[0043]

[0044] Add 30 kg of modified polyol resin [LCR-100, NATOCO], 1.5 kg of elastic organic particles [polybutyl acrylate, average particle size 1 μm, Sekisui Chemical], 0.5 kg of reactive leveling agent in the container [BYK-370, BYK], 0.2 kg of metal drier [organotin drier DY-12, Deyin Chemical] and 60 kg of toluene, stirred at high speed for 30 minutes. Add 6.7 kg of curing agent 1 [hexamethylene diisocyanate, Asahi Kasei] and 3.3 kg of curing agent 2 [isophorone diisocyanate, Evonik] 30 minutes before coating, stir at high speed for 10 ...

Embodiment 2

[0048] (1) Preparation of semi-finished paint protection film:

[0049] On a translucent polyester release film with a thickness of 38 μm, an assembly glue with a thickness of 20 μm was obtained by known technology, and then laminated with a thermoplastic polyurethane film with a thickness of 150 μm, and rolled to obtain a semi-finished paint protection film for use.

[0050] (2) Preparation of self-healing coating solution:

[0051]

[0052] Add 35 kg of modified polyol resin [HFC-PNS1, HARIMA], 3.0 kg of elastic organic particles [polyurethane, average particle size 5 μm, root resin], 1.0 kg of reactive leveling agent [Silok-359] into the container , Sloco], 0.27 kg of metal drier [organic bismuth drier B1610, Casol additive] and 51 kg of ethyl acetate, stirred at high speed for 30 min. Add 10.2 kg of curing agent 1 [trimethylhexamethylene diisocyanate, BASF] and 3.8 kg of curing agent 2 [dicyclohexylmethane-4,4'-diisocyanate, Wanhua] 30 minutes before coating, and stir ...

Embodiment 3

[0056] (1) Preparation of semi-finished paint protection film:

[0057] On a translucent polyester release film with a thickness of 50 μm, use known technology to obtain an assembly glue with a thickness of 30 μm, and then laminate it with a thermoplastic polyurethane film with a thickness of 200 μm, and roll it to obtain a semi-finished paint protection film for use.

[0058] (2) Preparation of self-healing coating solution:

[0059]

[0060] Add 40 kg of modified polyol resin [TRE-2-S2, ASIA], 4.5 kg of elastic organic particles [nylon, average particle size 8 μm, BASF], 1.5 kg of reactive leveling agent [Teck- 2110, Tiger], 0.35 kg of metal drier [rare earth drier B-18, Kasol additive] and 42 kg of acetone, stirred at high speed for 30 min. Add 13.6 kg of curing agent 1 [xylylene diisocyanate, mol] and 3.9 kg of curing agent 2 [cyclohexane dimethylene diisocyanate, Mitsui Takeda] 30 minutes before coating, stir at high speed for 10 minutes, and wait use.

[0061] (3) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

A matte paint protection film, the matte paint protection film comprises a transparent support, on an optical surface of the transparent support, a matte self-healing layer and a transparent protective film are sequentially arranged; on the transparent support On the other optical surface of the body, an assembly glue and a translucent release film are sequentially arranged, and the matte self-healing layer is formed by heating and curing after coating the self-healing coating liquid; the self-healing coating liquid contains elastic organic particles , modified polyol resin, curing agent and other components; the particle size of the elastic organic particles is 1 μm to 15 μm; the curing agent is composed of curing agent 1 and curing agent 2, and the mixing ratio is 2:1~ 5:1. The matte paint surface protective film provided by the invention has good matte effect and self-repairing effect, has yellowing resistance and antifouling properties, and can be applied to the field of paint surface protection on automobile surfaces.

Description

technical field [0001] The invention relates to the field of film technology, in particular to a paint protection film attached to the surface of an automobile. Background technique [0002] Car paint protection film, also known as "invisible car cover", is a layer of transparent protective film attached to the surface paint of the car to protect the original car paint of the car from damage. This product has strong toughness and self-healing function, which can effectively prevent scratches and sand hits, and also isolates the contact between the car paint and the air, and can prevent acid rain, asphalt, bird droppings, etc. from damaging the paint surface . At the same time, the paint protection film is high-definition and bright, which can improve and protect the color and luster of the car paint surface. [0003] In order to meet individual needs, the demand for matte paint protection film is now proposed. Generally, there are two methods for the production process of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/29C09D175/04C09D5/08C09D7/65C08J7/04C08L27/06
Inventor 刘玉磊王辉李钢锁范义胜胡鑫
Owner HEFEI LUCKY SCI & TECH IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap