polyisocyanate composition

A polyisocyanate and composition technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of difficult dispersion, carbon dioxide generation, etc., and achieve the effects of excellent hardness, less yellow tone, and good validity period

Active Publication Date: 2021-08-06
ASAHI KASEI KK
View PDF20 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the polyisocyanate used as a curing agent in the two-component urethane coating composition has the problem that it is not easy to disperse in water, and it is easy to react with water to generate carbon dioxide.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • polyisocyanate composition
  • polyisocyanate composition
  • polyisocyanate composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0270] Hereinafter, specific examples and comparative examples are given to describe the present embodiment in more detail, but the present embodiment is not limited to the following examples and comparative examples unless the gist is exceeded. In Examples and Comparative Examples, the physical properties and evaluation of the polyisocyanate composition were measured as follows. In addition, unless otherwise stated, "part" and "%" mean "part by mass" and "% by mass".

[0271]

[0272] [Physical properties 1] Non-volatile components

[0273] When diluting with a solvent using the polyisocyanate composition obtained in the Example and the comparative example as a sample, the non-volatile matter was computed by the method shown below. First, accurately weigh the mass of the aluminum cup, put about 1 g of the sample, and precisely weigh the mass of the cup before heating and drying. Next, the cup containing the sample was heated in a dryer at 105° C. for 3 hours. Next, after...

manufacture example 1

[0370] [Production Example 1] Production 1 of amine salt of sulfonic acid

[0371] 10 mass parts of 1-propanol was added and stirred to 20 mass parts of 2-hydroxyethanesulfonic acid 70 mass % aqueous solutions, and the solution was obtained. Furthermore, triethylamine was measured so that the molar ratio with respect to 2-hydroxyethanesulfonic acid might become 1, and it diluted with 10 mass parts of 1-propanol. Next, a dilute solution of triethylamine was added dropwise to the stirred 2-hydroxyethanesulfonic acid solution. Stirring was stopped 1 hour after the start of the dropwise addition, and dehydration and desolventization were performed in an evaporator to obtain triethylamine salt of 2-hydroxyethanesulfonic acid with a solid content of 99.8% by mass.

manufacture example 2

[0372] [Production Example 2] Production 2 of amine salt of sulfonic acid

[0373]Except for using N,N-diisopropylethylamine instead of triethylamine, N,N-diisopropylethylamine 2-hydroxyethanesulfonic acid with a solid content of 99.8% by mass was obtained in the same manner as in Production Example 1. Salt.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The polyisocyanate composition comprises: a polyisocyanate containing a sulfonic acid anion group in the molecule, and one or more tertiary ammonium cations selected from the amine compounds represented by the following general formula (1) and selected from the following general formula (1): One or more of the tertiary ammonium cations of the amine compound represented by formula (2); or include: a polyisocyanate containing a sulfonic acid anion group in the molecule, and, R 11 , R 12 and R 13 Two or more kinds of tertiary ammonium cations selected from the tertiary ammonium cations of the amine compound represented by the aforementioned general formula (1) whose total carbon numbers are different from each other.

Description

technical field [0001] This invention relates to polyisocyanate compositions. [0002] This application claims priority based on Japanese Patent Application No. 2016-200342 for which it applied to Japan on October 11, 2016, and takes in the content here. Background technique [0003] In recent years, from the viewpoint of environmental protection, the water-based conversion of room-temperature crosslinkable two-component urethane coating compositions conventionally used as solvent-based coatings has been desired. However, the polyisocyanate used as a curing agent in the two-component urethane coating composition has the problem that it is not easily dispersed in water and easily reacts with water to generate carbon dioxide. Therefore, the development of polyisocyanates having high emulsifiability and suppressing the reaction between isocyanate groups and water in a water-dispersed state has been advanced. [0004] Patent Document 1 discloses a reaction product of a polyiso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/28C08G18/08C09D175/04
CPCC08G18/0828C08G18/6229C08G18/706C08G18/792C09D175/04C08G18/28
Inventor 中岛和子
Owner ASAHI KASEI KK