Preparation method of large one-stone multi-surface ceramic board and large ceramic board

A ceramic and formula technology, applied in the field of ceramics, can solve problems such as difficulty in matching, poor decorative effect of large ceramic plates, and dislocation of patterns.

Active Publication Date: 2019-07-30
FOSHAN DONGPENG CERAMIC +2
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the adobe has a certain shrinkage after firing, the pattern of the ceramic slabs after paving is misplaced and difficult to match, which leads to poor decorative effects of the ceramic slabs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of large one-stone multi-surface ceramic board and large ceramic board
  • Preparation method of large one-stone multi-surface ceramic board and large ceramic board

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] A preparation method of one-stone multi-faced ceramic slab includes the following steps:

[0028] (1) Prepare the green body of the ceramic slab;

[0029] (2) Decorate in the form of inkjet printing on the blank: divide a large image into multiple small images at the input end of the inkjet printer, and expand the pattern edge of the small image and input the inkjet printer on the blank When printing, each small picture corresponds to a blank;

[0030] (3). Fired in a kiln to obtain a large ceramic slab with pattern and texture decoration;

[0031] (4) The sintered ceramic slab is edged to make the patterns of two adjacent ceramic slabs match.

[0032] In the decoration step of the present invention, the edges of the divided small images are expanded and then inkjet printing is performed, so that the pattern texture printed on the blank is also expanded, which makes the blanks with adjacent pattern textures There is a pattern texture that is repeatedly printed on the edge, and ...

Embodiment 1

[0057] A preparation method of one-stone multi-faced ceramic slab includes the following steps:

[0058] (1) Prepare the green body of the ceramic slab, and the green body adopts the existing cloth method to complete the cloth and then press into shape;

[0059] (2) Decorate in the form of inkjet printing on the blank: divide a large image into multiple small images at the input end of the inkjet printer, and expand the pattern edge of the small image and input the inkjet printer on the blank When printing, each small picture corresponds to a blank. The pattern expansion edge of the small picture expands toward the pattern that the small picture meets; the size of the inkjet printing pattern is the same as the size of the blank, and the pattern of the small picture expands The edge is printed on the edge of the blank by inkjet printing to form a pattern expansion edge; the preset grinding amount of one side of the ceramic plate is ⊿L, the pattern expansion side width on the blank i...

Embodiment 2

[0063] A preparation method of one-stone multi-faced ceramic slab includes the following steps:

[0064] (1) Prepare the green body of the ceramic slab, and the green body adopts the existing cloth method to complete the cloth and then is pressed into shape; the base glaze is applied on the green body;

[0065] (2) Decorate in the form of inkjet printing on the blank: divide a large image into multiple small images at the input end of the inkjet printer, and expand the pattern edge of the small image and input the inkjet printer on the blank When printing, each small picture corresponds to a blank. The pattern expansion edge of the small picture expands toward the pattern that the small picture meets; the size of the inkjet printing pattern is the same as the size of the blank, and the pattern of the small picture expands The edge is printed on the edge of the blank by inkjet printing to form a pattern expansion edge; the preset grinding amount of one side of the ceramic plate is ⊿...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a large one-stone multi-surface ceramic board. The preparation method comprises the following steps that (1) a blank body of the large ceramic board isprepared; (2) the blank body is decorated in an ink-jet printing mode, wherein a large picture is divided into multiple small pictures at the input end of an ink-jet printer, the edges of patterns ofthe small pictures are extended, input in the ink-jet printer and printed on the blank body, and each small picture corresponds to one blank body; (3) firing is conducted in a kiln, and the large ceramic board with pattern texture decoration is obtained; (4) the fired large ceramic board is subjected to edge polishing treatment, which is used for matching of the patterns of every two adjacent large ceramic boards. Correspondingly, the invention further discloses the large ceramic board obtained through the preparation method. After splicing of the large ceramic boards, the patterns can be matched, and after multiple large ceramic boards are laid, the pattern texture can extend in one or more surfaces, so that the pattern texture is casual, natural and high in three-dimensional effect.

Description

Technical field [0001] The invention relates to the technical field of ceramics, in particular to a method for preparing a one-stone multi-face ceramic slab and a ceramic slab. Background technique [0002] In the ceramic production process, waste residues are generated. At present, these waste residues are usually used in landfills or as low-quality raw materials for wall tiles, road transfers or concrete raw materials. There are defects that cannot be used in large quantities, and the added value of the final product is not high. And the performance is poor. High-quality ceramic tiles in the ceramic industry generally use high-quality mineral raw materials, and ceramic waste is difficult to use in high-quality ceramic products. [0003] Ceramic slabs have the advantages of simple and elegant decoration, fewer seams, avoiding dirt and dirt, and high construction and paving efficiency, and their market share in high-end household products will continue to increase. In the prior a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/10C04B35/622C04B35/626C04B41/52
CPCC04B35/10C04B35/62204C04B35/62605C04B41/52C04B2235/3201C04B2235/3206C04B2235/349C04B2235/96C04B41/5022
Inventor 李清莲周燕杨涛麦炳浩黄焱墉
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com