Color-variable art paint and preparation method thereof
An art paint, photochromic technology, applied in the field of color-changing art paint and its preparation, can solve the problems of harming direct contacts, single wall color, cobalt salt toxicity, etc., achieving good color transformation effect, beautifying the environment, and good stability. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0035] Example 1
[0036] A color-changing art paint, measured in parts by mass, comprising the following components:
[0037] 27 parts of deionized water, 0.7 part of thickener, 0.3 part of PH adjuster, 0.4 part of dispersant, 2 parts of defoamer, 0.2 part of wetting agent, 0.2 part of bactericide, 0.2 part of antifungal agent, 0.3 part of antifreeze , 0.7 parts of film-forming aids, 35 parts of acrylic emulsion, 7 parts of photochromic materials, and 25 parts of glass beads; wherein, the photochromic materials include silver bromide and copper oxide with a mass ratio of 3:2:2:3:4 , Nano molybdenum disulfide sheet, azo polyurethane, hexamethylene tetramine.
[0038] The preparation method of the above-mentioned color-changing art paint, comprising the following steps:
[0039] (1) mixing, dissolving, stirring, swelling, dispersing deionized water, thickener, pH regulator to obtain a mixed solution;
[0040] (2) in the mixed solution obtained in step (1), slowly add dispers...
Example Embodiment
[0045] Example 2
[0046] A color-changing art paint, measured in parts by mass, comprising the following components:
[0047] 23 parts of deionized water, 0.7 part of thickener, 0.3 part of PH adjuster, 0.4 part of dispersant, 1.5 part of defoamer, 0.2 part of wetting agent, 0.2 part of bactericide, 0.2 part of antifungal agent, 0.3 part of antifreeze , 0.85 parts of film-forming aids, 40 parts of acrylic emulsion, 10 parts of photochromic materials, and 27 parts of glass microbeads; wherein, the photochromic materials include silver bromide and copper oxide with a mass ratio of 3:2:2:2:4 , Nano molybdenum disulfide sheet, azo polyurethane, hexamethylene tetramine.
[0048] The preparation method of the above-mentioned color-changing art paint, comprising the following steps:
[0049] (1) mixing, dissolving, stirring, swelling, dispersing deionized water, thickener, pH regulator to obtain a mixed solution;
[0050] (2) in the mixed solution obtained in step (1), slowly add...
Example Embodiment
[0055] Example 3
[0056] A color-changing art paint, measured in parts by mass, comprising the following components:
[0057] 20 parts of deionized water, 0.7 part of thickener, 0.3 part of PH regulator, 0.4 part of dispersant, 3 parts of defoamer, 0.2 part of wetting agent, 0.2 part of bactericide, 0.2 part of antifungal agent, 0.5 part of antifreeze , 1.5 parts of film-forming aids, 40 parts of acrylic emulsion, 13 parts of photochromic materials, and 30 parts of glass beads; wherein, the photochromic materials include silver chloride and copper oxide with a mass ratio of 3:2:2:4:3 , Nano molybdenum disulfide sheet, azo polyurethane, hexamethylene tetramine.
[0058] The preparation method of the above-mentioned color-changing art paint, comprising the following steps:
[0059] (1) mixing, dissolving, stirring, swelling, dispersing deionized water, thickener, pH regulator to obtain a mixed solution;
[0060] (2) in the mixed solution obtained in step (1), slowly add disp...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap