Vulcanize-crosslinked halogenated rubber adhesive and preparation method thereof
A halogenated rubber, vulcanization and cross-linking technology, applied in the direction of halogen rubber derivative adhesives, etc., can solve the problems of reduced elasticity and toughness of adhesives, unsatisfactory performance, and matching problems
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] According to the formula (parts by weight): chlorinated trans-butadiene-isoprene copolymer rubber 100, antioxidant RD 0.1, benzene 300, dicumyl peroxide 0.5, chlorinated trans-butadiene- The isoprene copolymerized rubber was dissolved in benzene at 25°C with a stirring speed of 800rpm for 2 hours, during which anti-aging agent RD was added, then dicumyl peroxide was added to the above solution, and the solution was continued for 2 hours to obtain an adhesive. Wherein, the chlorine content of the chlorinated trans-butadiene-isoprene copolymer rubber is 45wt%, the butadiene content is 5mol%, the trans structure content is 88mol%, and the molecular weight is 10,000.
Embodiment 2
[0020] According to formula (parts by weight): chlorinated trans-butadiene-isoprene copolymer rubber 100, antioxidant 4010NA5, chloroform 500, sulfur 5, accelerator CBS 1.2, phenyl o-hydroxybenzoate 5, iron red 0.5, silica 10, chlorinated trans-butadiene-isoprene copolymer rubber and anti-aging agent 4010NA were dissolved in chloroform at 80°C with a stirring speed of 100rpm for 0.5h, and then sulfur was added to the above solution to promote agent, anti-ultraviolet agent phenyl-o-hydroxybenzoate, iron red pigment and silicon dioxide, and continue to dissolve under stirring at 300rpm for 0.5h to obtain an adhesive. Among them, the chlorine content of the chlorinated trans-butadiene-isoprene copolymer rubber is 82.5wt%, the butadiene content is 70mol%, the trans structure content is 92mol%, and the molecular weight is 20,000.
Embodiment 3
[0022] According to the formula (parts by weight): brominated trans-butadiene-isoprene copolymer rubber 100, antioxidant 264 3, methylene chloride 500, sulfur 0.5, accelerator ZDMC 5, 2-hydroxyl-4-methyl Oxybenzophenone 3.5, silica 20, brominated trans-butadiene-isoprene copolymer rubber and anti-aging agent 264 were dissolved in dichloromethane at 72°C with a stirring speed of 300rpm for 1.5h, and then Add sulfur, an accelerator, an anti-ultraviolet agent 2-hydroxy-4-methoxybenzophenone, and silicon dioxide to the above solution, and continue to dissolve for 0.5 h under stirring at 400 rpm to obtain an adhesive. Among them, brominated trans-butadiene-isoprene copolymer rubber has a bromine content of 52.5 wt%, a butadiene content of 5 mol%, a trans structure content of 92 mol%, and a molecular weight of 23,000.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap