A kind of black ceramic and preparation method thereof

A technology of black ceramics and ceramic bodies, applied in the field of ceramic materials, can solve the problems of product color fluctuation and high cost, and achieve the effect of stable black hair color, high density and easy control

Active Publication Date: 2022-03-15
浙江古婺窑火陶瓷文化有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the disadvantages of the need to add black high-temperature pigments or colored metal oxides in the preparation process of the existing traditional silicate black ceramics, resulting in fluctuations in product color and high costs, and to provide a new black ceramic preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of black ceramic and preparation method thereof
  • A kind of black ceramic and preparation method thereof
  • A kind of black ceramic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] This embodiment provides a method for preparing black ceramics, which includes the following steps: sintering a ceramic body and carbon black in a closed environment to obtain the black ceramics.

[0045]The invention utilizes the characteristics of high specific surface area and high activity of carbon black to sinter the ceramic body and carbon black at high temperature in a closed environment, and under the action of high-temperature self-infiltration of C element in carbon black, calcine to obtain pure black color ceramics.

[0046] What the inventor needs to explain is that carbon black is different from other carbon-containing substances (such as graphite), and its crystallization is very incomplete, with many defects and high activity. , heavy oil, fuel oil, etc.) are the products obtained by incomplete combustion or thermal decomposition under the condition of insufficient air. Carbon black, as a light, loose and extremely fine black powder, has a very large su...

Embodiment 1

[0069] The present embodiment provides a kind of preparation method of black ceramic, comprises the steps:

[0070] 1) Preparation of ceramic green body: in terms of mass fraction, the chemical composition is 70.5% SiO 2 , 19.08%Al 2 o 3 , 0.2% CaO, 0.6% MgO, 2.62% K 2 O, 0.75% Na 2 O, 0.25% Fe 2 o 3 And the ceramic green body with 6% loss on ignition is molded and dried, and then calcined at a low temperature of 750° C. to obtain a ceramic green body;

[0071] 2) Lay a layer of carbon black on the bottom of the sealable alumina crucible, that is, the first carbon black layer, and then place the ceramic green body obtained in step 1) on the first carbon black layer, and the ceramic green body The green body is located in the center of the crucible, and the central axis of the ceramic green body coincides with the central axis of the crucible;

[0072] 3) filling carbon black in the inner cavity of the ceramic green body and around the ceramic green body so that the carb...

Embodiment 2

[0080] The present embodiment provides a kind of preparation method of black ceramic, comprises the steps:

[0081] 1) Preparation of ceramic green body: in terms of mass fraction, the chemical composition is 70.5% SiO 2 , 19.08%Al 2 o 3 , 0.2% CaO, 0.6% MgO, 2.62% K 2 O, 0.75% Na 2 O, 0.25% Fe 2 o 3 And the ceramic green body with 6% loss on ignition is molded and dried, and then calcined at a low temperature of 750° C. to obtain a ceramic green body;

[0082] 2) Lay a layer of carbon black on the bottom of the sealable alumina crucible, that is, the first carbon black layer, and then place the ceramic green body obtained in step 1) on the first carbon black layer, and the ceramic green body The green body is located in the center of the crucible, and the central axis of the ceramic green body coincides with the central axis of the crucible;

[0083] 3) filling carbon black in the inner cavity of the ceramic green body and around the ceramic green body so that the carbon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of ceramic materials, in particular to a black ceramic and a preparation method thereof. The method for preparing black ceramics provided by the invention comprises the following steps: sintering a ceramic body and carbon black in a closed environment to obtain the black ceramics. The preparation method of black ceramics provided by the present invention is simple in process, easy in operation and easy to control, does not need to add any black high-temperature pigments or colored metal oxides before blank making, does not change the basic formula of ceramic blanks, and does not change the kiln structure And the firing atmosphere, only changing the firing process of the ceramics, can achieve the firing of black ceramics with pure color and high density. The black ceramics prepared by it are uniform without black spots and high in blackness. After refiring, the black hair color is stable and does not fade.

Description

technical field [0001] The invention relates to the technical field of ceramic materials, in particular to a black ceramic and a preparation method thereof. Background technique [0002] Black pottery is a kind of unglazed pottery, which is made of colloidal clay by reducing flame firing process. The firing temperature is about 900-1000°C. The firing process is more advanced and complicated, and it needs to master the temperature and the atmosphere in the kiln to be successful. However, the firing of black pottery has not been able to solve the problem of water rupture, so it can only make some seemingly complicated but Crafts that cannot be used. Compared with black pottery, black ceramics are more widely used in knives, watch cases, molds, Ceramic decoration and various ceramic structural parts and other fields. [0003] Ceramics include pure oxide ceramics (such as alumina or zirconia ceramics) and traditional silicate ceramics. Due to the different sintering methods, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/64C04B35/18
CPCC04B35/64C04B35/18C04B2235/6562C04B2235/6567C04B2235/424C04B2235/3208C04B2235/3206C04B2235/3201C04B2235/3272C04B2235/9661C04B2235/96C04B2235/3232C04B2235/5454
Inventor 罗婷吴军明顾幸勇李萍刘昆曹志敏
Owner 浙江古婺窑火陶瓷文化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com