A technology of gravel and real lacquer, which is applied to paints, coatings, and anti-corrosion coatings containing biocide, which can solve the problems of poor low-temperature stability and achieve the effects of lower film-forming temperature, strong three-dimensional effect, and strong decoration
Inactive Publication Date: 2020-01-17
西洞庭凯兴建材有限公司
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The invention provides a crushed stone lacquer and a preparation method thereof, aiming at solving the problem of poor low-temperature stability of the existing crushed stone lacquer
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] A kind of crushed stone lacquer provided by the embodiment of the present invention is composed of the following components in mass percentage: 20% of silicon acrylic emulsion, 76.2% of natural colored stone powder, 0.2% of hydroxyethyl cellulose, 2% of propylene glycol, alcohol Ester twelve 1%, thickener 0.5%, preservative 0.1%.
[0017] Among them, the solid content of silicone acrylic emulsion is 54.5%, the fineness of natural colored stone powder is 325 mesh, the viscosity of hydroxyethyl cellulose is 100,000, the thickener is polyurethane thickener, and the preservative is methyl p-hydroxybenzoate ester.
Embodiment 2
[0019] A crushed stone real lacquer provided in the embodiment of the present invention is composed of the following components in mass percentage: 15% of silicon-acrylic emulsion, 80% of natural colored stone powder, 0.1% of hydroxyethyl cellulose, 4.6% of propylene glycol, alcohol Ester twelve 0.1%, thickener 0.1%, preservative 0.1%.
[0020] Among them, the solid content of silicone acrylic emulsion is 50%, the fineness of natural colored stone powder is 400 mesh, the viscosity of hydroxyethyl cellulose is 150,000, the thickener is polyurethane thickener, and the preservative is methyl p-hydroxybenzoate ester.
Embodiment 3
[0022] A crushed stone real lacquer provided in the embodiment of the present invention is composed of the following components in mass percentage: 25% of silicon-acrylic emulsion, 70% of natural colored stone powder, 0.5% of hydroxyethyl cellulose, 1.9% of propylene glycol, alcohol Ester twelve 2%, thickener 0.5%, preservative 0.1%.
[0023] Among them, the solid content of silicone acrylic emulsion is 52%, the fineness of natural colored stone powder is 325 mesh, the viscosity of hydroxyethyl cellulose is 100,000, the thickener is polyacrylate thickener, and the preservative is p-hydroxybenzene Methyl formate.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention belongs to the field of building coating materials, and provides a macadam real paint and a preparation method thereof, wherein the macadam real paint comprises a silicone acrylic emulsion, natural colored stone powder, hydroxyethyl cellulose, propylene glycol, dodecyl alcohol ester, a thickener and a preservative. According to the invention, the silicone acrylic emulsion has good film-forming property, the hydroxyethyl cellulose can improve the surface viscosity of the macadam real paint and improve the fluidity of the macadam real paint, the propylene glycol can improve the frost resistance of the macadam real paint, the natural colored stone powder can endow the macadam real paint with gorgeous colors, the dodecyl alcohol ester can improve the film-forming property of thesilicone acrylic emulsion, reduce the lowest film-forming temperature of the silicone acrylic emulsion and enhance the coating adhesive force of the macadam real paint, the thickener can improve the surface viscosity of the macadam real paint and prevent the macadam real paint from precipitating in the storage process, and the preservative can prevent the macadam real paint from decaying or beinginfected with mould when the macadam real paint is stored in the container; and the macadam real paint has good color, good pattern, good stone-like effect after being used, and is strong in decoration.
Description
technical field [0001] The invention belongs to the field of architectural coatings, in particular to a gravel real paint and a preparation method thereof. Background technique [0002] Crushed stone real lacquer belongs to a kind of real stone varnish. Real stone varnish is a kind of paint with a decorative effect similar to marble or granite. It is applied to the exterior wall of a building and has the effect of imitating stone, so it is also called liquid stone. Compared with other types of coatings, real stone paint also has the advantages of strong decoration, wide application range, water-based environmental protection and good stain resistance. [0003] After the existing crushed stone lacquer is used, it is prone to strength reduction and dry cracking in a long-term low-temperature environment, and its performance in terms of stability, dry crack resistance and workability still needs to be improved. Contents of the invention [0004] The invention provides a crus...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more