Preparation method of polyvinylidene fluoride composite compound, polyvinylidene fluoride composite film, its preparation method and application

A polyvinylidene fluoride and composite membrane technology, which is used in its preparation, the preparation of polyvinylidene fluoride composite mixtures, and the field of polyvinylidene fluoride composite membranes, can solve the problems of incapable of anti-pollution materials and poor film-forming properties.

Active Publication Date: 2021-09-14
GUIYANG UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Metal-organic framework material MIL-100-Fe has good adsorption performance due to its polar functional groups and molecular pores in its structure, but its own poor film-forming property, so it cannot be directly used in the preparation of anti-pollution materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polyvinylidene fluoride composite compound, polyvinylidene fluoride composite film, its preparation method and application
  • Preparation method of polyvinylidene fluoride composite compound, polyvinylidene fluoride composite film, its preparation method and application
  • Preparation method of polyvinylidene fluoride composite compound, polyvinylidene fluoride composite film, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A preparation method of a polyvinylidene fluoride composite film, comprising the following steps:

[0045] (1) 0.21g trimesic acid and 0.675g FeCl3 Disperse in 50mL DMF (N,N'-dimethylformamide), react at 120°C for 20h, stop the reaction, cool to 20°C, wash off unreacted trimeric acid with ethanol, dry at 80°C, Crystal A is obtained, and the crystal A is ground with a mortar to obtain powder A, which is the metal organic framework material MIL-100-Fe.

[0046] (2) Add 0.5g of metal-organic framework material MIL-100-Fe and 8g of N-methylpyrrolidone into the reactor, ultrasonically disperse at room temperature for 2 hours, then add 1.5g of polyvinylidene fluoride into the reactor, and stir at 60°C 4h, the composite mixture was obtained.

[0047] (3) Vacuum defoaming and aging treatment of the composite mixture to obtain the modified casting solution.

[0048] (4) Apply the spin coating method (the spin coating speed is 200r / min, and the spin coating time is 20s) to coat...

Embodiment 2

[0057] A preparation method of a polyvinylidene fluoride composite film, comprising the following steps:

[0058] (1) 0.21g trimesic acid and 0.675g FeCl 3 Disperse in 50mL DMF (N,N'-dimethylformamide), react at 120°C for 20h, stop the reaction, cool to 20°C, wash off unreacted trimeric acid with ethanol, dry at 80°C, Crystal A is obtained, and the crystal A is ground with a mortar to obtain powder A, which is the metal organic framework material MIL-100-Fe.

[0059] (2) Add 1g metal-organic framework material MIL-100-Fe and 7.5g N-methylpyrrolidone into the reactor, ultrasonically disperse at room temperature for 2 hours, then add 1.5g polyvinylidene fluoride into the reactor, and stir at 60°C 4h, the composite mixture was obtained.

[0060] (3) Vacuum defoaming and aging treatment of the composite mixture to obtain the modified casting solution.

[0061] (4) Spin coating method (the spin coating speed is 1000r / min, and the spin coating time is 30s) is used to coat the mod...

Embodiment 3

[0068] A preparation method of a polyvinylidene fluoride composite film, comprising the following steps:

[0069] (1) 0.21g trimesic acid and 0.675g FeCl 3 Disperse in 50mL DMF (N,N'-dimethylformamide), react at 120°C for 20h, stop the reaction, cool to 20°C, wash off unreacted trimeric acid with ethanol, dry at 80°C, Crystal A is obtained, and the crystal A is ground with a mortar to obtain powder A, which is the metal organic framework material MIL-100-Fe.

[0070] (2) Add 1g metal-organic framework material MIL-100-Fe and 7g N-methylpyrrolidone into the reactor, ultrasonically disperse at room temperature for 2h, then add 2g polyvinylidene fluoride into the reactor, stir at 60°C for 4h, A compound mixture is obtained.

[0071] (3) Vacuum defoaming and aging treatment of the composite mixture to obtain the modified casting solution.

[0072] (4) Spin-coating method (spin-coating speed of 300r / min, spin-coating time of 90s) is used to coat the modified casting solution on ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The application provides a preparation method of a polyvinylidene fluoride composite mixture, a polyvinylidene fluoride composite film, a preparation method and an application thereof, belonging to the technical field of functional polymer materials. The preparation method of the polyvinylidene fluoride composite mixture is: dispersing the metal-organic framework in a polar organic solvent, then adding polyvinylidene fluoride, and dispersing at a temperature of 50-70°C for 4-10 hours to obtain a composite mixture . The preparation method of polyvinylidene fluoride composite film comprises the steps of sequentially defoaming, aging and film coating of polyvinylidene fluoride compound mixture. The polyvinylidene fluoride composite film prepared by the above method has good adsorption capacity and certain blood compatibility, and can be used as a blood contact material.

Description

technical field [0001] The present application relates to the technical field of functional polymer materials, in particular, to a preparation method of a polyvinylidene fluoride composite compound, a polyvinylidene fluoride composite film, its preparation method and its application. Background technique [0002] Metal-Organic Frameworks (MOFs) is an inorganic-organic composite material, which is composed of metal ions and multifunctional organic ligands to form a crystalline porous material with a periodic network structure through self-assembly. Due to the combination of the periodic network pore structure and the properties of the organic material framework, the biggest feature of the metal organic framework material is its high porosity and huge specific surface area. In recent years, through the design and synthesis of metal-organic framework materials with controllable functional groups in the molecular structure, the application fields of such materials have become mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/16C08L87/00C08J5/18B01D71/34B01D69/12B01D67/00A61L27/50A61L27/16
CPCA61L27/16A61L27/507B01D67/0002B01D69/12B01D71/34C08J5/18C08J2327/16C08J2487/00C08L2203/02
Inventor 覃慧陈舒忆王壹聂胜强成刚罗军陶泽志
Owner GUIYANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap