Soft polyester fibers and preparation method thereof

A polyester fiber, soft technology, applied in the field of polyester fiber, can solve problems such as unevenness of the stripes

Active Publication Date: 2020-05-08
JIANGSU HENGLI CHEM FIBER
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention provides a kind of soft polyester fiber and its preparation method, aiming to solve the problem of random "strip-like unevenness" when PBT / PTT side-by-side composite fiber is applied to knitted fabric products in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soft polyester fibers and preparation method thereof
  • Soft polyester fibers and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of preparation method of soft polyester fiber, its process is as follows:

[0046] According to the POY process, after distributing the PTT melt (intrinsic viscosity of 1.04dL / g) and PBT melt (intrinsic viscosity of 1.1dL / g) with a mass ratio of 50:50, from the same spinneret Hole m (circular) and spinneret hole n (circular) are extruded and subjected to relaxation heat treatment to obtain soft polyester fiber;

[0047] Among them, such as figure 1 As shown, the distribution means that the PBT melt is distributed through the distribution hole A, and the PTT melt is distributed into the spinneret hole m through the distribution hole B, and the PBT melt is distributed through the distribution hole C, and the PTT melt is distributed through the distribution hole Hole D is distributed to spinneret hole n; at the inlets of distribution hole A, distribution hole B, distribution hole C and distribution hole D, the apparent viscosity difference of PTT melt and PBT melt ...

Embodiment 2

[0054] A kind of preparation method of soft polyester fiber, its process is as follows:

[0055] According to the POY process, after distributing PTT melt (intrinsic viscosity 1.02dL / g) and PBT melt (intrinsic viscosity 1.2dL / g) with a mass ratio of 50:50, from the same spinneret Hole m (circular) and spinneret hole n (circular) are extruded and subjected to relaxation heat treatment to obtain soft polyester fiber;

[0056] Wherein, the distribution refers to distributing the PBT melt through the distribution hole A, while distributing the PTT melt through the distribution hole B to the spinneret hole m, passing the PBT melt through the distribution hole C, and simultaneously distributing the PTT melt through the distribution hole D is distributed into the spinneret hole n; at the entrance of distribution hole A, distribution hole B, distribution hole C and distribution hole D, the apparent viscosity of PTT melt and PBT melt differs by 4.6%;

[0057] Distribution hole A and d...

Embodiment 3

[0063] A kind of preparation method of soft polyester fiber, its process is as follows:

[0064] According to the POY process, after distributing PTT melt (intrinsic viscosity 1.02dL / g) and PBT melt (intrinsic viscosity 1.2dL / g) with a mass ratio of 50:50, from the same spinneret Hole m (circular) and spinneret hole n (circular) are extruded and subjected to relaxation heat treatment to obtain soft polyester fiber;

[0065] Wherein, the distribution refers to distributing the PBT melt through the distribution hole A, while distributing the PTT melt through the distribution hole B to the spinneret hole m, passing the PBT melt through the distribution hole C, and simultaneously distributing the PTT melt through the distribution hole D is distributed into the spinneret hole n; at the entrance of distribution hole A, distribution hole B, distribution hole C and distribution hole D, the apparent viscosity of PTT melt and PBT melt differs by 4.7%;

[0066] Distribution hole A and d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
stabilityaaaaaaaaaa
elastic recovery rateaaaaaaaaaa
Login to View More

Abstract

The present invention relates to soft polyester fibers and a preparation method thereof. According to a POY process, a PTT melt and a PBT melt are distributed and are extruded from spinneret holes m and n in the same spinneret plate, and relaxation heat treatment is performed to prepare the soft polyester fibers, wherein the PBT and PTT melts flow to the spinneret holes m through distribution holes A and B and flow to the spinneret holes n through distribution holes C and D; at inlets of the distribution holes, the apparent viscosity difference of the PTT and PBT melts is not more than 5%; thedistribution holes A and B are equal-height cylindrical holes, and the diameter ratio is (1.10-1.50) : 1; and the distribution holes C and D are equal-height cylindrical holes, and the diameter ratiois 1 : (1.10-1.50). The prepared soft polyester fibers consist of a plurality of PBT / PTT parallel composite monofilaments with two proportions, and the crimping directions of the monofilaments are inrandom distribution. The problem of strip unevenness of PBT / PTT parallel composite fibers in a knitted fabric is solved.

Description

technical field [0001] The invention belongs to the technical field of polyester fibers, and relates to a soft polyester fiber and a preparation method thereof. Background technique [0002] The softness of the fabric is a subjective feeling when people touch and pinch the fabric. Softness is a very important property for fibers. The fiber with good softness is fine and uniform, strong and elastic. The texture is soft, smooth and delicate to the touch, and the spun fabric has the characteristics of soft touch and elegant wearing. [0003] PBT / PTT composite fiber has fine and dense three-dimensional crimp, superior resilience, soft hand feeling and excellent dyeing performance. It is an ideal raw material for imitation wool and down, and is comfortable to wear. Due to the above-mentioned characteristics of PBT fiber, it has received widespread attention in the textile industry in recent years and has been widely used in various fields. It is especially suitable for making h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/22D01D5/32D01D10/02D01F8/14D01D5/08
CPCD01D5/082D01D5/22D01D5/32D01D10/02D01F8/14
Inventor 王丽丽王山水汤方明范红卫蒋丽波
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com