A kind of mofs-based gel electrolyte and its preparation and application

A technology of gel electrolyte and electrolyte, which is applied in instruments, nonlinear optics, optics, etc., can solve the problems of poor ion conductivity and mechanical properties, and achieve excellent discoloration performance, excellent mechanical properties, and stable work.

Active Publication Date: 2021-08-10
DONGHUA UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a MOFs-based gel electrolyte and its preparation method and application, so as to overcome the defects of poor ionic conductivity and mechanical properties of the gel electrolyte in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mofs-based gel electrolyte and its preparation and application
  • A kind of mofs-based gel electrolyte and its preparation and application
  • A kind of mofs-based gel electrolyte and its preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] (1) After dissolving 57.42g LiTFSI in 100mL PC, a 2mol / L LiTFSI / PC solution was obtained, and then 60mL of this solution was blended with 10mL [Emim][TFSI] to obtain a transparent electrolyte;

[0042] (2) 4.36g Zn(NO 3 ) 2 ·6H 2 0, 6.16g Hmim were dissolved in 300mL EtOH (molar ratio 1:5:700), respectively, to prepare solution A and solution B. After that, solution A was quickly poured into solution B, and after 45 minutes of magnetic stirring, the MOFs dispersion was obtained, and then centrifuged at 5000rpm / min for 12 minutes, and the supernatant was poured off to obtain the MOFs white pre-gel;

[0043] (3) Spread the MOFs pre-gel obtained in step (2) on a surface with a volume of 1.0 cm 3 In the groove, add 1.0mL transparent electrolyte obtained in step (1) dropwise on the surface of MOFs pre-gel, let it stand for 1h, and heat it at 80℃ for 14h with a vacuum degree of -0.10MPa to obtain the MOFs-based gel electrolyte .

[0044] The preparation process of the MO...

Embodiment 2

[0049] (1) 1.52g LiPF 6 After dissolving in 100mL EC, 0.1mol / L LiPF was obtained 6 / EC solution, after which 30mL of this solution was mixed with 10mL [Emim][BF 4 ] blending to obtain a transparent electrolyte;

[0050] (2) 5.82g Zn(NO 3 ) 2 ·6H 2 0 and 4.82g Hmim were dissolved in 400mL EtOH (three molar ratios were 1:3:700), respectively, to prepare solution A and solution B. After that, solution A was quickly poured into solution B, and after 90 minutes of magnetic stirring, the MOFs dispersion was obtained, and then centrifuged at 12,000 rpm / min for 4 minutes, and the supernatant was poured off to obtain the MOFs white pre-gel;

[0051] (3) Spread the MOFs pre-gel obtained in step (2) on a surface with a volume of 2.0 cm 3 Add 8.0mL of transparent electrolyte obtained in step (1) dropwise to the surface of MOFs pre-gel, let it stand for 3 hours, and heat at 90℃ for 8 hours with a vacuum degree of –0.06MPa to obtain the MOFs-based gel electrolyte. .

[0052] The app...

Embodiment 3

[0055] (1) 10.64g LiClO 4 After dissolving in 100mL PC, 1mol / L LiClO was obtained 4 / PC solution, then mix 50 mL of this solution with 5 mL of [Emim][BF 4 ] blending to obtain a transparent electrolyte;

[0056] (2) 2.911g Zn(NO 3 ) 2 ·6H 2 0, 6.427g Hmim were dissolved in 200mL EtOH (three molar ratios were 1:8:700), respectively, to prepare solution A and solution B. After that, solution A was quickly poured into solution B, and after magnetic stirring for 60 minutes, the MOFs dispersion was obtained, and then centrifuged at 8000rpm / min for 8 minutes, and the supernatant was poured off to obtain the MOFs white pre-gel;

[0057] (3) Spread the MOFs pre-gel obtained in step (2) on a surface with a volume of 2.0 cm 3 Add 4.0mL of the transparent electrolyte obtained in step (1) dropwise to the surface of the MOFs pre-gel, let it stand for 2 hours, and heat at 80°C for 12 hours with a vacuum of –0.08MPa to obtain the MOFs-based gel electrolyte. .

[0058] There is no big...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical conductivityaaaaaaaaaa
electrical resistanceaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a MOFs-based gel electrolyte and a preparation method and application thereof. The electrolyte components include: MOFs material and transparent electrolyte. The method includes: preparation of transparent electrolyte; preparation of MOFs pregel; preparation of MOFs-based gel electrolyte. The electrolyte overcomes the inherent defects of liquid and solid electrolytes, and has high transparency and ionic conductivity as well as good interfacial adhesion; the electrochromic devices assembled by the electrolyte, especially flexible devices, not only have good discoloration performance, but also It has excellent mechanical properties, is resistant to bending, can be sheared, can be drilled, and can work stably even when bending and discoloring synchronous operation, and has a very high practical application value.

Description

technical field [0001] The invention belongs to the field of electrochromic device electrolyte and its preparation and application, and in particular relates to a MOFs-based gel electrolyte and its preparation method and application. Background technique [0002] Electrochromic Devices (ECDs) based on rigid conductive glass have been industrialized in the fields of building energy-saving windows and anti-glare rearview mirrors. The flexible ECDs developed based on flexible conductive films are still in the research and development stage, but they have broad application prospects in flexible display, visual inspection, smart wearable and other fields (Energy Technol. 2018, 6, 33-45). Electrochromic devices generally have a layer-by-layer structure, including a conductive layer, an electrochromic layer, an electrolyte layer, an ion storage layer, and a counter electrode layer. Among them, the electrolyte layer, as the medium for ion transmission during the discoloration proce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G02F1/1506G02F1/1523G02F1/1516G02F1/153
CPCG02F1/1506G02F1/1523G02F1/153G02F1/1516
Inventor 王宏志白智元李耀刚侯成义张青红
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap