High titanium steel slab continuous casting method

A steel slab and continuous casting technology, applied in the field of metallurgy, can solve problems such as nozzle blockage, achieve the effect of avoiding oxidation and reducing secondary inclusions

Active Publication Date: 2021-11-23
CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The technical problem to be solved by the present invention is: the existing high-titanium steel slab continuous casting method cannot avoid the problem of nozzle blockage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Embodiment 1 carries out continuous casting to high titanium steel slab with the method of the present invention

[0040] Steel containing 0.1% titanium is produced, and the billet size is 1200mm×200mm.

[0041] (1) Air curtain retaining wall is used in the tundish, and the argon flow rate of the air curtain retaining wall is 10L / min; the liquid surface of the tundish is protected by argon gas, and the argon flow rate at the long nozzle and each stopper position is 20L / min to maintain positive pressure . From the ladle to the tundish, from the tundish to the crystallizer, a protective casing is used to protect the pouring process, and the protective casing is baked for 4 hours in advance; from the start of pouring to the stable casting speed, the liquid level of the crystallizer needs to be protected by argon gas, and the flow rate is 10L / min.

[0042] (2) The N content in the steel is 25ppm, cast at a high superheat (40°C), the pouring temperature is 1580°C, and the...

Embodiment 2

[0045] Embodiment 2 carries out continuous casting to high titanium steel slab with the method of the present invention

[0046] Steel containing 0.8% titanium is produced, and the billet size is 1400mm×230mm.

[0047] (1) The tundish adopts an air curtain retaining wall, and the argon gas flow rate of the air curtain retaining wall is 20L / min; the liquid surface of the tundish is protected by argon gas, and the argon gas flow rate at the long nozzle and each stopper position is 30L / min to maintain positive pressure . From the ladle to the tundish, from the tundish to the crystallizer, a protective sleeve is used to protect the pouring process, and the protective sleeve is baked for 5 hours in advance; during the period from the start of pouring to the stable casting speed, the liquid level of the crystallizer needs to be protected by argon gas, and the flow rate is 20L / min.

[0048] (2) The N content in the steel is 28ppm, cast at high superheat (50°C), the pouring tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of metallurgy, and in particular relates to a high-titanium steel slab continuous casting method. Aiming at the problem that the existing high-titanium steel continuous casting method cannot avoid nozzle clogging, the present invention provides a high-titanium steel slab continuous casting method, comprising the following steps: a. Air curtain retaining wall is used in the tundish, and argon gas is used on the liquid surface Protection, from the ladle to the tundish, from the tundish to the crystallizer, a protective casing is used to protect the pouring; before the first furnace is poured and the ladle is changed, a steel pipe is used to connect to the long nozzle; b. When the N content in the steel is ≤ 30ppm, use High superheat pouring process, casting speed ≤ 1.1m / min; c. Adopt the dynamic soft reduction technology at the end of solidification, and the secondary cooling adopts the secondary cooling system of strong cooling at the end of solidification. The invention can reduce secondary inclusions by 30-50%, and can also avoid a large amount of TiN generated in the tundish, thus avoiding the problem of nozzle blockage and increasing the number of continuous casting furnaces to more than 2 furnaces; the invention guarantees the quality of the slab Under the circumstances, it is of great significance to realize the continuous casting of high titanium steel.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and in particular relates to a high-titanium steel slab continuous casting method. Background technique [0002] High-titanium steel (Ti greater than 0.1%) has the characteristics of high strength, high toughness, and high wear resistance due to the precipitation of TiC, and has wide application prospects. However, the continuous casting production of high-titanium steel is currently a difficult problem at home and abroad. On the one hand, high-titanium steel is easy to liquidate the high-melting point compound TiN, which adheres to the inner wall of the nozzle during continuous casting. Usually, the nozzle will be blocked after one furnace is produced and continuous casting cannot be continued. In addition, during continuous casting, titanium in steel is easy to react with mold slag to form TiO 2 , and then deteriorate the physical properties of the mold flux, including melting point, viscos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/16B22D11/18B22D11/22
CPCB22D11/16B22D11/18B22D11/225
Inventor 谢鑫曾建华王谦周明佳
Owner CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD