Low-specific-pressure molded explosive and molding process thereof

A technology of explosives and specific pressure, which is applied in the field of explosives, can solve the problems of unsatisfactory safety, fracture and damage of explosive crystals, etc., and achieve the effect of significant blasting lethality

Active Publication Date: 2020-08-07
XIAN MODERN CHEM RES INST
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, although defects such as cracks and cavities are reduced in the high specific pressure forming process, it brings crystal fracture damage of explosives.
Therefore, the launch safety of HMX-based press-packed explosives cannot meet the requirements for high-speed launch of the anti-injury warhead of the rifled gun

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-specific-pressure molded explosive and molding process thereof
  • Low-specific-pressure molded explosive and molding process thereof
  • Low-specific-pressure molded explosive and molding process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1.1 The present invention is implemented with reference to the following mass percentage composition:

[0023]

[0024] 1.2 Preparation process

[0025] Step 1. Preparation of binder solution: Add 500ml of ethyl acetate to a 2L reaction kettle; add 80g of methyl vinyl silicone rubber and 15g of ethylene-vinyl acetate copolymer to ethyl acetate in sequence, at 50°C Stir at high temperature for 1 h until the methyl vinyl silicone rubber and ethylene-vinyl acetate copolymer are dissolved to obtain a binder solution.

[0026] Step 2. Heat the temperature of the kneading tank to 60°C, add 900g of HMX and 500ml of anhydrous ethyl acetate, stir for 15 minutes, add the solution obtained in step 1 and 5g of dioctyl sebacate, and heat up to 75°C , kneading for 20min. Discharge, obtain the explosive slurry after the insensitivity coating.

[0027] Step 3, granulation: naturally cool the explosive slurry obtained in step 2 to room temperature, volatilize the solvent under ven...

Embodiment 2

[0034] 2.1 The present invention is implemented with reference to the following mass percentage composition:

[0035]

[0036] 2.2 Preparation process

[0037] Step 1. Preparation of binder solution: Add 500ml of ethyl acetate to a 2L reaction kettle; add 55g of methyl vinyl silicone rubber and 20g of ethylene-vinyl acetate copolymer to ethyl acetate in turn, at a temperature of 60°C Stir under stirring for 1 h until the methyl vinyl silicone rubber and ethylene-vinyl acetate copolymer are dissolved to obtain a binder solution.

[0038] Step 2: Heat the temperature of the kneading tank to 60°C, add 920g of HMX and 500ml of anhydrous ethyl acetate, stir for 15 minutes, add the solution obtained in step 1 and 5g of dioctyl sebacate, and heat up to 85°C. Knead for 20min. Discharge, obtain the explosive slurry after the insensitivity coating.

[0039] Step 3, granulation: naturally cool the explosive slurry obtained in step 2 to room temperature, volatilize the solvent under...

Embodiment 3

[0046] 3.1 The present invention is implemented with reference to the following mass percentage composition:

[0047]

[0048] 3.2 Preparation process:

[0049] Step 1. Preparation of binder solution: Add 500ml of ethyl acetate to a 2L reaction kettle; add 80g of methyl vinyl silicone rubber and 30g of ethylene-vinyl acetate copolymer to ethyl acetate in turn, at a temperature of 50°C Stir under stirring for 1 h until the methyl vinyl silicone rubber and ethylene-vinyl acetate copolymer are dissolved to obtain a binder solution.

[0050] Step 2: Heat the temperature of the kneading tank to 60°C, add 880g of HMX and 500ml of anhydrous ethyl acetate, stir for 15 minutes, add the solution obtained in step 1 and 10g of dioctyl sebacate, and raise the temperature to 85°C. Knead for 20min. Discharge, obtain the explosive slurry after the insensitivity coating.

[0051] Step 3, granulation: naturally cool the explosive slurry obtained in step 2 to room temperature, volatilize t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-specific-pressure molded explosive and a molding process thereof. The low-specific-pressure molded explosive comprises the following components in percentage by mass: 88%-92% of HMX, 2%-3% of ethylene-vinyl acetate copolymer, 5.5%-8% of methyl vinyl silicone rubber and 0.5%-1% of dioctyl sebacate. The explosive molding powder prepared by the invention can be molded under low specific pressure, and the emission overload resistance of explosive charging is remarkably improved. The invention mainly relates to a low-specific-pressure molded explosive, which is mainlyused for charging bullets, and is particularly suitable for charging large-caliber linear bore cannon killing warheads.

Description

technical field [0001] The invention belongs to the field of explosives, and in particular relates to a low-specific-pressure molded explosive and a molding process thereof, which are mainly used for charging artillery shells, and are especially suitable for charging a large-caliber rifled artillery anti-injury warhead. Background technique [0002] Artillery can be divided into rifled guns and smoothbore guns according to the barrel structure. Among them, rifled guns can effectively ensure the stability of projectiles and increase the range of fire. Therefore, most modern artillery are rifled guns. However, when rifled guns (especially large-caliber guns) are fired in the bore, the explosives in the projectiles must bear extremely high axial launch overload (about 300MPa), and at the same time bear the combined effects of radial overload and tangential overload, so , general high-energy explosives are difficult to withstand such a high launch overload, and it is easy to cau...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C06B25/34C06B21/00C06B23/00
CPCC06B21/0066C06B23/005C06B23/009C06B25/34
Inventor 董军王晓峰王伟力席鹏邢江涛谭波杜茂华黄亚峰杨雄赵凯
Owner XIAN MODERN CHEM RES INST
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com