Gangue paste cementing material, preparation method thereof, gangue paste filling material and preparation method thereof

A technology of cementing material and gangue, which is applied in the field of mine filling, can solve the problems of high raw material cost and low strength, and achieve the effects of reduced production cost, high economic value, and improved coagulation strength and coagulation speed

Active Publication Date: 2020-09-22
河北充填采矿技术有限公司 +1
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems of low strength and high raw material cost of the existing gangue paste filling material, the present in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gangue paste cementing material, preparation method thereof, gangue paste filling material and preparation method thereof
  • Gangue paste cementing material, preparation method thereof, gangue paste filling material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0034] Example 1

[0035] A gangue gypsum body cement is composed of the following parts by mass:

[0036] 20 parts of Portland cement clinker, 2 parts of sulphoaluminate cement clinker, 5 parts of modified gypsum, 60 parts of mineral powder, 5 parts of limestone powder, 0.2 parts of sodium silicate, 2 parts of admixtures.

[0037] Among them, the fineness of Portland cement clinker is between 350-400 mesh;

[0038] The sulphoaluminate cement clinker is mixed with bauxite, limestone, gypsum and boric acid and then calcined at 1300℃, then ground to a specific surface area ≥460m 2 / kg, the mixing mass ratio of the bauxite, limestone, gypsum and boric acid is 30:45:8:1, and the content of alumina in the sulphoaluminate cement clinker is 29%;

[0039] The admixture is composed of sodium carboxymethyl cellulose, polyacrylamide, superplasticizer and polycarboxylate with a mass ratio of 2:1:1:1; the superplasticizer is composed of wood with a mass ratio of 2:1 It is composed of calcium sulfon...

Example Embodiment

[0044] Example 2

[0045] A gangue gypsum body cement is composed of the following parts by mass:

[0046] Portland cement clinker 25 parts, sulphoaluminate cement clinker 3 parts, modified gypsum 8 parts, mineral powder 65 parts, limestone powder 8 parts, sodium silicate 0.25 parts, admixture: 3 parts.

[0047] Among them, the fineness of Portland cement clinker is between 350-400 mesh;

[0048] The sulphoaluminate cement clinker is mixed with bauxite, limestone, gypsum and boric acid and then calcined at 1350℃, then ground to a specific surface area ≥460m 2 / kg, the mixing mass ratio of the bauxite, limestone, gypsum and boric acid is 36:50:15:1.5, and the content of alumina in the sulfoaluminate cement clinker is 32%;

[0049] The admixture is composed of sodium carboxymethyl cellulose, polyacrylamide, superplasticizer and polycarboxylate with a mass ratio of 2.5:1.5:1.5:1.5; the superplasticizer is composed of wood with a mass ratio of 5:3 It is composed of calcium sulfonate and so...

Example Embodiment

[0054] Example 3

[0055] A gangue gypsum body cement is composed of the following parts by mass:

[0056] 30 parts of Portland cement clinker, 4 parts of sulfoaluminate cement clinker, 10 parts of modified gypsum, 70 parts of mineral powder, 10 parts of limestone powder, 0.3 part of sodium silicate, 4 parts of admixture.

[0057] Among them, the fineness of Portland cement clinker is between 350-400 mesh;

[0058] Sulphoaluminate cement clinker is mixed with bauxite, limestone, gypsum and boric acid, then calcined at 1400℃, and then ground to a specific surface area ≥460m 2 / kg, the mixing mass ratio of the bauxite, limestone, gypsum and boric acid is 42:58:20:2, and the content of alumina in the sulfoaluminate cement clinker is 35%;

[0059] The admixture is composed of sodium hydroxymethyl cellulose, polyacrylamide, superplasticizer and polycarboxylate with a mass ratio of 3:2:2:2; the superplasticizer is composed of wood with a mass ratio of 3:2 It is composed of calcium sulfonate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of mine filling, and particularly discloses a gangue paste cementing material and a preparation method thereof, and a gangue paste filling material and a preparation method thereof. The gangue paste cementing material is prepared from the following components in parts by mass: 20 to 30 parts of Portland cement clinker, 2 to 4 parts of sulphoaluminate cement clinker, 5 to 10 parts of modified gypsum, 60 to 70 parts of mineral powder, 5 to 10 parts of limestone powder, 0.2 to 0.3 part of sodium silicate and 2 to 4 parts of additive. The gangue paste filling material is prepared from the following components in percentage by mass: 2.5 to 3 percent of gangue paste cementing material, 16 to 18.5 percent of gangue, 5 to 6 percent of fly ash and the balance of water. The gangue paste cementing material can replace cement to serve as a cementing material to play a role in a gangue paste filling material, the manufacturing cost of the gangue paste filling material is reduced, and the coagulation strength and the coagulation speed of the gangue paste filling material can be greatly improved.

Description

technical field [0001] The invention relates to the technical field of mine filling, in particular to a gangue paste cementing material and a preparation method thereof, a gangue paste filling material and a preparation method thereof. Background technique [0002] Gangue paste filling mining is to process solid waste such as gangue, fly ash, slag, low-quality soil, and urban garbage near the coal mine into a slurry with no critical flow rate and no need for dehydration. The slurry is transported underground to fill the goaf. [0003] The cement in the current gangue paste filling is mostly cement. In the cost of gangue paste filling and mining, the cementing material accounts for more than 45% of the total filling cost, which makes the filling cost of gangue paste filling mining generally high. , causing a certain economic pressure on the mine, seriously restricting the application and development of filling mining technology. Although other cementing materials have recen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/26C04B7/32
CPCC04B28/26C04B7/32C04B2111/00637C04B2201/50C04B7/02C04B22/143C04B18/142C04B14/28C04B24/383C04B24/2652C04B2103/302C04B18/12C04B18/08
Inventor 贾靖卢志敏杨洪增秦大健郝永超王学伟王英董小娟周金艳曾瑞萍刘艳高泽刘子萌沙漠菊张燕宋佳
Owner 河北充填采矿技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap