Shaping Color Pavement Coatings

A color and coating technology, applied in the field of shaping color pavement coatings, can solve the problems of inability to combine the advantages of inorganic and organic anti-slip materials, short impact resistance construction period, etc., to achieve good adhesion fastness and increase adhesion fastness. , the effect of good impact resistance

Active Publication Date: 2020-11-20
苏州大乘环保新材有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problem existing in the prior art that the advantages of both inorganic and organic non-slip materials cannot be combined, the object of the present invention is to provide a shaping color road coating, which has good wear resistance, impact resistance Good and short construction period

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Shaping Color Pavement Coatings
  • Shaping Color Pavement Coatings
  • Shaping Color Pavement Coatings

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-6

[0066] Embodiments 1-6 all relate to a kind of shaping colored road paint, including component A, component B and component C.

[0067] The raw material ratio of component A is shown in Table 2.

[0068] Table 2. Raw material ratio table of component A in embodiment 1-6 (by mass percentage)

[0069]

[0070] Weigh the raw materials according to the ratio in Table 2, stir and mix evenly to obtain component A.

[0071] The component B raw material ratio (by mass percentage) of embodiment 1-6 is identical, specifically:

[0072] AEH-2014 Environment-friendly Floor Coating Emulsion 90wt%

[0073] BYK022 1wt%

[0074] Hytrel G5544 (Shore hardness 55D) 9wt%;

[0075] Weigh AEH-2014 environment-friendly floor paint emulsion, BYK022 and Hytrel G5544 (Shore hardness 55D) according to the proportion, stir and mix evenly to obtain component B.

[0076] The raw material ratio (by mass percentage) of the component C of embodiment 1-6 is identical, specifically:

[0077] CIMENT FON...

Embodiment 7-8

[0089] Examples 7-8 are all based on Example 4, and the only difference from Example 4 is the raw material ratio of component B, as shown in Table 3.

[0090] Table 3. Raw material ratio table of component B in embodiment 7-8 (by mass percentage)

[0091]

[0092] Weigh the raw materials according to the ratio in Table 3, and mix them evenly to obtain Component B. In other embodiments, the AEH-2014 environment-friendly floor coating emulsion can also be replaced by other commercially available commercial emulsions such as DOW MAINCOTE AEH-20 water-based acrylic epoxy hybrid emulsion or self-made acrylic epoxy hybrid emulsion; as a toughening agent The added Hytrel G5544 (Shore hardness 55D) can also be replaced by acrylonitrile rubber particles and TPU particles, but the effect is slightly worse than that of thermoplastic polyester elastomer (TPEE).

Embodiment 9-12

[0094] Examples 9-12 are all based on Example 7, and differ from Example 7 only in that the raw material ratio of component C is different, see Table 4 for details.

[0095] Table 4. Raw material ratio table of component C in embodiment 9-12 (by mass percentage)

[0096]

[0097] The mesh numbers of emery used in Examples 9-12 are 80 mesh, 70 mesh, 60 mesh, and 60 mesh in turn; the mesh numbers of quartz powder used in Embodiment 9-12 are 120 mesh, 80 mesh, 100 mesh, and 100 mesh in turn.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
wear resistanceaaaaaaaaaa
power levelaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of ground coating materials, and particularly discloses a shaping colored pavement coating. The shaping colored pavement coating comprises a component A, a componentB and a component C, wherein the component A is prepared from a cross-linking agent, water, a coloring agent, barium sulfate, quartz powder, a dispersion stabilizer, a leveling agent, a thickener andan antifoaming agent I; the component B is prepared from a waterborne acrylic epoxy hybrid emulsion, a defoaming agent II and a toughening agent; and the component C is prepared from high-alumina cement, Portland cement, anhydrite, carborundum, quartz powder, glass powder, a powder water reducing agent, hectorite and a thickening agent II. The shaping colored pavement coating has the advantages of good wear resistance, good impact resistance and short construction period.

Description

technical field [0001] The invention relates to the field of ground coating materials, more specifically, it relates to a shaping colored road coating. Background technique [0002] At present, anti-skid materials on the ground mainly include organic and inorganic systems. Organic anti-slip materials are mainly epoxy resin or polyurethane polymer materials. After construction, the surface is smooth and clean, but the fire resistance is poor and easy to delaminate; inorganic anti-slip materials are mainly gypsum-based or cement-based self-leveling materials, and gypsum-based water-resistant Poor, acidic or neutral, there is a risk of corrosion to iron parts, cement-based self-leveling materials have poor fluidity and lack of elasticity, and cannot meet high standards of purification and aesthetic requirements. [0003] Therefore, how to develop a ground anti-slip material that combines the advantages of the above-mentioned organic and inorganic anti-slip materials is a hot s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/16C04B111/20C04B111/34C04B111/50
CPCC04B28/16C04B2111/00508C04B2111/0075C04B2111/20C04B2111/2038C04B2111/343C04B2111/503C04B2201/05C04B7/32C04B7/02C04B14/324C04B14/06C04B14/22C04B14/104C04B24/281C04B14/368C04B14/305C04B14/062C04B24/282C04B24/125C04B2103/0068C04B24/42C04B24/283
Inventor 张福恒单秀军张尊杰卢相志
Owner 苏州大乘环保新材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap