A kind of bacterial enzyme mixed preparation containing Stenotrophomonas maltophilia and its application

A technology of Stenotrophomonas and maltophilia, applied in the field of microorganisms, to achieve the effects of simple process, good synergistic degradation effect, and low treatment cost

Active Publication Date: 2022-02-01
JIANGNAN UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many studies on the degradation of polyethylene terephthalate (PET) by multiple enzymes, but there are few studies on the synergistic degradation of polyethylene terephthalate (PET) by bacterial enzymes (mixed preparations)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bacterial enzyme mixed preparation containing Stenotrophomonas maltophilia and its application
  • A kind of bacterial enzyme mixed preparation containing Stenotrophomonas maltophilia and its application
  • A kind of bacterial enzyme mixed preparation containing Stenotrophomonas maltophilia and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Example 1: Screening and identification of Stenotrophomonas pavanii

[0061] 1. Screening of Stenotrophomonas pavanii

[0062] Specific steps are as follows:

[0063] 1. Ordinary screening

[0064] Taking the soil from the Taohuashan landfill in Wuxi City as a sample, take 1g of soil and add 9mL of normal saline, shake and enrich for 30min at 35°C and 180rpm; then take 1mL of the supernatant and dilute to 10 -4 、10 -5 、10 -6 , respectively take 200μL and dilute to 10 -4 、10 -5 、10 -6 The diluted solution was evenly spread on the inorganic salt solid medium containing 2g / L polyethylene terephthalate (PET), and placed in a 35°C incubator for constant temperature cultivation until colonies grew; the experimental results showed that after many Daily culture, no bacterial colonies appeared on the separation plate, this method can not effectively isolate the bacterial strain with the ability to degrade polyethylene terephthalate (PET).

[0065] 2. "PET induction cultu...

Embodiment 2

[0079] Embodiment 2: the preparation of bacterial enzyme mixed preparation

[0080] Specific steps are as follows:

[0081] (1) Activated strains: Spread Stenotrophomonas maltophilia JWG-G1 on an LB solid medium plate and culture at 37°C and 150rpm for 1 day to obtain a single colony;

[0082] (2) Preparation of seed solution: scrape the single colony obtained in step (1) and inoculate it into a glass test tube of 5 mL liquid LB medium, and cultivate it at 30° C. and 150 rpm for 12 hours to obtain the seed solution;

[0083] (3) Expansion cultivation: the seed liquid obtained in step (2) (viable bacteria number 1 × 10 8 CFU / mL) was transferred to LB liquid medium at a volume ratio of 1%, and cultivated to OD at 30°C and 150rpm 600 =1.0, obtain fermented liquid;

[0084] (4) Preparation of bacterial agent: the fermented liquid obtained in step (3) is centrifuged at 3600rpm for 10min, the supernatant is discarded, and then the inorganic salt liquid medium is added until the n...

Embodiment 3

[0086] Embodiment 3: the degradation ability of Stenotrophomonas maltophilia JWG-G1 to the intermediate phthalate (BHET) of polyethylene terephthalate in different addition amounts

[0087] With the bacterial agent Stenotrophomonas maltophilia JWG-G1 (viable bacteria number 2 * 10) that step (4) in the embodiment 2 obtains 9 CFU / mL) were added to the 2mg The reaction system was obtained in the inorganic salt liquid of BHET; the reaction system was placed at 37° C. and 150 rpm to react for 15 hours, and the amount of MHET and TPA generated and the remaining amount of BHET were measured by HPLC.

[0088] The analysis results are shown in Table 1. With the increase of the addition amount of Stenotrophomonas maltophilia JWG-G1, the degradation rate of BHET gradually increased; when the addition amount of Stenotrophomonas maltophilia JWG-G1 was 20%, The degradation rate of BHET reached the maximum value (37%); after that, the degradation rate of BHET remained unchanged with the in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a bacterial enzyme mixed preparation containing Stenotrophomonas maltophilia and its application, belonging to the technical field of microorganisms. The invention provides a brand-new method for degrading polyethylene terephthalate and polyethylene terephthalate intermediates. By combining specific bacterial strains and specific biological enzymes, a biodegradable biodegradable compound with specific degradation applications is prepared. The bacterial enzyme mixed preparation, the mixed preparation is a compound of Stenotrophomonas maltophilia and cutinase; adopt the bacterial enzyme mixed preparation provided by the invention to degrade polyethylene terephthalate and polyethylene terephthalic acid Ethylene glycol ester intermediate, its degradability is far better than adopting bacterium or enzyme to handle alone, and described bacterium enzyme mixed preparation is in high crystallinity polyethylene terephthalate (PET) and its intermediate ethyl phthalate The glycol ester (BHET) has a significant synergistic effect in the degradation process, and has good promotion and application value in the field of plastic degradation technology.

Description

technical field [0001] The invention relates to a bacterial enzyme mixed preparation containing Stenotrophomonas maltophilia and its application, belonging to the technical field of microorganisms. Background technique [0002] With the rapid development of the economy, the accumulation of plastic waste exceeds 320 million tons per year, and 60% of the plastic waste is polyethylene terephthalate (PET) plastic products. Since plastics are difficult to degrade, the global annual recycling rate of plastic products is only 14%, which makes plastic waste continue to accumulate in the environment and poses a serious threat to the ecology. Therefore, the degradation of polyethylene terephthalate (PET) is very critical to the control of plastic waste. [0003] Compared with traditional physical and chemical degradation technology, biodegradation technology is a technology that directly degrades plastics through degradable plastic strains. Due to its advantages of green, pollution-f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C12N1/20C12N9/18A62D3/02A62D101/28
CPCC12N1/20C12N9/18A62D3/02C12Y301/01074A62D2101/28
Inventor 吴敬颜正飞陈晓倩黄青松顾冷涛
Owner JIANGNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap