Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

The control method of slab center segregation

A control method and billet technology, applied in the field of iron and steel metallurgy, can solve problems such as low homogeneity of steel products, achieve the effects of improving center segregation, improving homogeneity, and reducing casting temperature

Active Publication Date: 2021-09-03
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to overcome the problem of low homogeneity of steel products in the prior art, and provide a method for controlling slab center segregation, which effectively reduces the temperature of molten steel in the continuous casting process , so as to improve the center segregation problem and improve the homogeneity of the slab

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] This embodiment is that a steelmaking plant adopts the method invented by the present technology to produce 160mm×160mm section SWRH82B hard wire products.

[0041] The specific execution process is: casting speed Vc=1.8m / min; casting cross-sectional area S=0.16*0.16=0.0256m 2 ; The enthalpy value H of the original temperature of the molten steel in the tundish Tc =1261.2kJ / kg; enthalpy value H of the target temperature of molten steel in the tundish Tm =1258.0kJ / kg; alloy steel wire radius r=0.005m; enthalpy value H of alloy steel wire when the molten steel in the tundish is at the target temperature Tsm =H Tm =1258.0(kJ / kg), the enthalpy value H at the initial temperature of the alloy steel wire Tsc = 50 kJ / kg.

[0042] Substituting into the calculation formula of wire feeding speed, the calculated wire feeding speed Vs is 1.50m / min. At the same time, the casting temperature at the position of the strand in the continuous casting production can be reduced from 1479...

Embodiment 2

[0046] This embodiment is that a steelmaking plant adopts the method invented by the present technology to produce 160mm×160mm section SWRH82B hard wire products.

[0047] The specific execution process is: casting speed Vc=1.7-1.8m / min; casting cross-sectional area S=0.16*0.16=0.0256m 2 ; The enthalpy value H of the original temperature of the molten steel in the tundish Tc =1270.1kJ / kg; enthalpy value H of the target temperature of molten steel in the tundish Tm =1261.2kJ / kg; alloy steel wire radius r=0.005m; enthalpy value H of steel wire when the molten steel in the tundish is at the target temperature Tsm =H Tm =1261.2 (kJ / kg), the enthalpy value H at the initial temperature of the alloy steel wire Tsc = 50 kJ / kg.

[0048] Substituting into the calculation formula of wire feeding speed, the calculated wire feeding speed Vs is 3.93-4.16m / min. The casting temperature at the position of the strand can be reduced from 1498°C to 1479°C, and the liquidus temperature is 147...

Embodiment 3

[0052] This embodiment is that a steelmaking plant adopts the method invented by the present technology to produce 160mm×160mm section SWRH82B hard wire products.

[0053] The specific execution process is: casting speed Vc=1.8-1.9m / min; casting cross-sectional area S=0.16*0.16=0.0256m 2 ; The enthalpy value H of the original temperature of the molten steel in the tundish Tc =1270.1kJ / kg; enthalpy value H of the target temperature of molten steel in the tundish Tm =1261.2kJ / kg; alloy steel wire radius r=0.005m; enthalpy value H of alloy steel wire when the molten steel in the tundish is at the target temperature Tsm =H Tm =1263.2(kJ / kg), the enthalpy value H at the initial temperature of the alloy steel wire Ts c=50kJ / kg.

[0054] Substituting into the calculation formula of wire feeding speed, the calculated wire feeding speed Vs is 4.16-4.39m / min. The casting temperature at the position of the strand can be reduced from 1498°C to 1481°C, and the liquidus temperature is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
radiusaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of iron and steel metallurgy, in particular to a method for controlling segregation at the center of a slab. The method specifically includes the following steps: (1) formulating an alloy steel wire of the same type as the target pouring steel; Calculate the enthalpy value of the molten steel in the tundish; (3) calculate the heat consumed to achieve thermal balance according to the target temperature of the molten steel in the tundish; (4) feed the alloy steel wire described in (1) into the molten steel to supplement the heat. The invention effectively reduces the casting temperature of molten steel in the continuous casting process, thereby improving the problem of central segregation and improving the homogeneity of the cast slab.

Description

technical field [0001] The invention relates to the field of iron and steel metallurgy, in particular to a method for controlling segregation at the center of a slab. Background technique [0002] With the rapid development of society, iron and steel materials are the most widely used metal materials, and their quality performance requirements are getting higher and higher, which puts forward higher requirements for the quality of steel product blanks, including the chemical composition uniformity, purity and Density, in which the control of chemical composition uniformity is also called segregation control. Segregation control has always been the focus and difficulty of steelmaking research. The uniformity of chemical composition directly affects the control of product structure and performance. For example, as an important power transmission component, gear steel is required to have high crush resistance, pitting corrosion resistance, good impact resistance, bending resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/18B22D1/00C21C7/00
CPCB22D1/00B22D11/18C21C7/0006
Inventor 李红光陈天明陈亮郭奠荣
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com