Template-free one-step synthesis regulation and control method of calcium carbonate/silicon dioxide nano tube

A template-free, nanotube technology, applied in the direction of silicon dioxide, calcium carbonate/strontium/barium, calcium/strontium/barium compounds, etc., can solve the problems affecting the large-scale synthesis of hollow nanotubes, affecting the quality of synthetic nanotubes, etc. Achieve the effect of good popularization and application value, low cost and simple process conditions

Active Publication Date: 2020-11-20
FUZHOU UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These limitations largely hinder the large-scale synthesis of hollow nanotubes and often affect the quality of the synthesized nanotubes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Template-free one-step synthesis regulation and control method of calcium carbonate/silicon dioxide nano tube
  • Template-free one-step synthesis regulation and control method of calcium carbonate/silicon dioxide nano tube
  • Template-free one-step synthesis regulation and control method of calcium carbonate/silicon dioxide nano tube

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] CaCO 3 / SiO 2 One-step synthesis of nanotubes:

[0032] (1) Na 2 SiO 3 and Na 2 CO 3 Dissolve in deionized water to form mixed solution A, Na in mixed solution A 2 SiO 3 The concentration is 3mM, Na 2 CO 3 At a concentration of 10mM, the CaCl 2 Dissolved in deionized water to form solution B, CaCl in solution B 2 The concentration is 10mM.

[0033] (2) Put 5mL of solution A and 5mL of solution B in a water bath for 10 min, set the temperature to 30°C. During the heat preservation process, solution B was added dropwise to solution A through a peristaltic pump, the titration rate was set at 1 mL / min, and the titration was completed and left to stand for 30 min.

[0034] (3) The white precipitate was obtained by centrifugation, which was washed twice with deionized water, then washed twice with dilute hydrochloric acid, and finally washed twice with deionized water. The samples were dried in a freeze dryer for 12 h.

[0035] figure 1 It is the XRD pattern of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of nano material preparation, and discloses a template-free one-step synthesis regulation and control method of a CaCO3 / SiO2 nano tube. The spontaneous growth of the CaCO3 / SiO2 nano tube is realized by regulating and controlling the concentration of Na2SiO3. The CaCO3 / SiO2 nano tube is synthesized in one step by using cheap, green, non-toxic and easilyavailable raw materials and adopting a coprecipitation method. The prepared composite material can be applied to efficient loading of metal ions. The preparation process is economical, simple, convenient and efficient, and no surfactant or template is needed.

Description

technical field [0001] The invention belongs to the technical field of nanomaterial preparation, in particular to a CaCO 3 / SiO 2 Template-free one-step synthesis of nanotubes. Background technique [0002] Due to their unique properties, nanomaterials have attracted extensive attention in the fields of adsorption, energy storage, and catalysis. Among these nanomaterials, inorganic nanoparticles with a hollow structure have become a hot topic in the field of nanomaterials research because of their unique structural characteristics. Among these different types of inorganic nanomaterials, nano-SiO 2 Materials are widely used in catalysis, sensing, drug delivery, and template synthesis due to their unique morphology, high surface area, adjustable pore structure, easily modified surface properties, and high biocompatibility. In the past two decades, SiO with various structures 2 Materials have been rapidly developed, including ordered mesoporous frameworks, nanopores, nanor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01F11/18C01B33/18B82Y40/00B82Y30/00
CPCC01F11/181C01B33/18B82Y40/00B82Y30/00C01P2004/13C01P2004/80
Inventor 于岩曹若丹庄赞勇
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com