External wall flexible putty powder with light reflection capability and preparation method thereof

A technology of light reflection and putty powder, which is applied in the direction of filling slurry, etc., can solve the problems of inability to provide heat insulation functions, etc., and achieve the effect of solving heat insulation and energy-saving effects, and improving durability

Inactive Publication Date: 2021-03-16
北京三棵树新材料科技有限公司
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, such materials are generally exterior wall latex paint or exterior wall real stone paint, and the thickness of the coating is relatively thin (micron), which cannot provide long-lasting and effective heat insulation function.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • External wall flexible putty powder with light reflection capability and preparation method thereof
  • External wall flexible putty powder with light reflection capability and preparation method thereof
  • External wall flexible putty powder with light reflection capability and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A flexible putty powder for external walls with light reflection function, which is prepared by mixing components according to the following mass and fraction ratios:

[0022]

[0023] A flexible putty powder for external walls with light reflection function is prepared by the following method: add white cement and half of the heavy calcium powder into the stirring tank, and then add titanium dioxide and modified silicon dioxide while stirring, which can be recycled Disperse latex powder, cellulose ether, bentonite, metakaolin and starch ether, then stir at a stirring rate of 2000rmp for 5 minutes, then add hollow glass microspheres and the remaining half of heavy calcium powder, and continue stirring for 3 minutes to obtain the product.

Embodiment 2

[0025] A flexible putty powder for external walls with light reflection function, which is prepared by mixing components according to the following mass and fraction ratios:

[0026]

[0027] A flexible putty powder for external walls with light reflection function is prepared by the following method: add white cement and half of the heavy calcium powder into the stirring tank, and then add titanium dioxide and modified silicon dioxide while stirring, which can be recycled Disperse latex powder, cellulose ether, bentonite, metakaolin and starch ether, then stir at a stirring rate of 3000rmp for 3 minutes, then add hollow glass microspheres and the remaining half of heavy calcium powder, and continue stirring for 3 minutes to obtain the product.

Embodiment 3

[0029] A flexible putty powder for external walls with light reflection function, which is prepared by mixing components according to the following mass and fraction ratios:

[0030]

[0031]

[0032] A flexible putty powder for external walls with light reflection function is prepared by the following method: add white cement and half of the heavy calcium powder into the stirring tank, and then add titanium dioxide and modified silicon dioxide while stirring, which can be recycled Disperse latex powder, cellulose ether, bentonite, metakaolin and starch ether, then stir for 4 minutes at a stirring rate of 2500rmp, then add hollow glass microspheres and the remaining half of heavy calcium powder, and continue stirring for 2 minutes to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to external wall flexible putty powder with a light reflection function and a preparation method thereof. The putty powder is prepared by mixing the following components in partsby mass: 20.0-35.0 parts of white cement, 10.0-50.0 parts of hollow glass beads, 5.0-25.0 parts of titanium dioxide, 5.0-12.0 parts of silicon dioxide powder, 0.1-60.0 parts of ground calcium carbonate powder, 3.0-7.0 parts of redispersible latex powder, 0.3-0.5 part of cellulose ether, 0.3-1.0 part of bentonite, 2.0-7.0 parts of metakaolin and 0.01-0.2 part of starch ether. The putty powder disclosed by the invention is outer wall flexible putty with relatively high ultraviolet reflection, sunlight reflection ratio, near-infrared reflection ratio and hemispherical reflectivity.

Description

technical field [0001] The invention relates to a flexible putty for exterior walls, in particular to a flexible putty powder for exterior walls with light reflection function and a preparation method thereof. Background technique [0002] The exterior wall putty is suitable for exterior wall decoration projects and is an important part of the entire coating system, providing good base level flatness and bonding strength for the entire decorative layer. Among them, the flexible putty for exterior walls has excellent flexibility, and is widely used in places with high requirements for flexibility of the base layer, such as exterior wall insulation and decoration projects. [0003] In recent years, there are serious fire safety hazards and hidden dangers of falling off and hurting people due to the dry-hanging insulation systems (such as rock wool insulation and decorative composite boards, XPS extruded boards, polystyrene particle boards, etc.) commonly used in external wall ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 张少玉刘月龙蒋克飞
Owner 北京三棵树新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap