Preparation method of 3Y-TZP ceramic paste and preparation process of complete-implant fixed prosthesis

A 3Y-TZP, prosthesis technology, applied in dental preparations, dental prostheses, additive processing, etc., can solve the problems of bur loss, poor surface accuracy, and difficult to reuse cutting dust, and achieve high strength and toughness. The effect of improving installation accuracy and fast curing speed

Pending Publication Date: 2021-07-02
江苏京科智镕新材料科技有限公司
View PDF14 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many problems in this technology: 1. The required shape is obtained by cutting from prefabricated ceramic blocks. The raw material utilization rate of this technology itself is low and the cost is high; 2. The cutting dust is difficult to reuse, which is easy to cause environmental pollution. Seriously affect the health of processing personnel; 3. Affected by the bur, the detailed processing ability is insufficient and the surface accuracy is poor; 4. The bur is seriously worn out, which increases t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of 3Y-TZP ceramic paste and preparation process of complete-implant fixed prosthesis
  • Preparation method of 3Y-TZP ceramic paste and preparation process of complete-implant fixed prosthesis
  • Preparation method of 3Y-TZP ceramic paste and preparation process of complete-implant fixed prosthesis

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0043] Specific embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings.

[0044] The preparation method of the 3Y-TZP ceramic paste applied to stereolithography comprises the following steps:

[0045] S1: Take a certain amount of 3Y-TZP ceramic powder, dispersant, defoamer and leveling agent respectively, and the selected 3Y-TZP ceramic powder is a spherical or spherical powder with a particle size D50 of 400-600nm , through the selection of the particle size, the strength requirement when preparing teeth can be met;

[0046] S2: Add the 3Y-TZP ceramic powder, the dispersant, the defoamer and the leveling agent in step S1 to the photosensitive resin premix respectively, wherein the dispersant is first added to the photosensitive In the resin material, mix evenly, and then gradually add 3Y-TZP ceramic powder, the specific addition amount is, add 50% of the total amount of 3Y-TZP ceramic powder for the first time, mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of 3Y-TZP ceramic paste and a preparation process of an upper structure of an implant prosthesis, wherein the preparation method of the 3Y-TZP ceramic paste comprises the steps: adding 3Y-TZP ceramic powder, a dispersing agent, a defoaming agent and a flatting agent into a photosensitive resin premixed solution, fully ball-milling to form ceramic slurry, then adding a photoinitiator, ball-milling again, then adding a rheological additive, and mixing to form the 3Y-TZP ceramic paste. The preparation process of the upper structure of the implant prosthesis comprises the steps of acquiring dentition data of a patient, designing, printing the upper structure of the implant prosthesis, degreasing, sintering, applying facing porcelain and carrying out heat treatment. The 3Y-TZP ceramic paste can be used for 3D printing of the upper structure of the implant prosthesis to replace a traditional cutting process, environmental pollution is avoided, material loss is reduced, manufacturing precision is improved, and product quality is improved.

Description

Technical field: [0001] The invention belongs to the technical field of denture production, and in particular relates to a preparation method of a 3Y-TZP (yttrium oxide stabilized zirconia) ceramic paste applied to stereolithography and a production process of an implant restoration superstructure. Background technique: [0002] Due to its good mechanical properties, chemical properties, aesthetic properties and biocompatibility, zirconia is increasingly used in the processing of the superstructure of implant restorations. At present, the processing method of the upper structure of the zirconia implant restoration is mainly CAD / CAM cutting and machining of the upper structure bracket of the implant restoration, and then the surface is decorated with feldspathic veneer porcelain to form an implant with simulated color, shape and function. Superstructure of the restoration. At present, there are many problems in this technology: 1. The required shape is obtained by cutting fr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/48C04B35/622C04B35/638A61K6/818A61K6/822B33Y10/00B33Y70/10
CPCC04B35/48C04B35/622C04B35/638A61K6/818A61K6/822B33Y10/00B33Y70/10C04B2235/3225C04B2235/6026C04B2235/6562C04B2235/6567C04B2235/6565C04B2235/661C04B2235/96
Inventor 不公告发明人
Owner 江苏京科智镕新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap