A kind of water-based UV light-curing coating and preparation method thereof

A light-curing coating, water-based technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of coating film cracking, affecting the coating molding effect, etc., to reduce cracking, good hanging ability, and improve convenience. Effect

Active Publication Date: 2022-05-24
漳州市和兴涂料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, during the pre-drying stage, the surface layer of the paint loses water rapidly, which easily leads to cracking of the paint film, thus affecting the molding effect of the paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based UV light-curing coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] A water-based UV light-curing coating, comprising 80kg of water-based aliphatic polyurethane acrylate oligomer emulsion, 8kg of film-forming aid, 2kg of photoinitiator, 1kg of leveling agent, 2kg of wetting agent, 1kg of defoamer, and 3kg of glycerin , reinforced fiber 10kg, deionized water 8kg.

[0058] Reinforcing fibers include 6.25kg of wood fibers and 3.75kg of glass fibers. The average diameter of wood fibers is 25 μm, and the average length of wood fibers is 200 μm; the average diameter of glass fibers is 10 μm, and the average length is 400 μm.

[0059] Embodiment 1 adopts the following method to prepare:

[0060] Activation of wood fibers: The wood fibers were soaked in a pH 13 sodium hydroxide solution for 24 hours.

[0061] Preparation of conditioner: leveling agent, wetting agent, defoaming agent, glycerin and 70% of the deionized water of the formula are mixed to obtain a mixed solution, and the wood fiber of the formula is taken out from the sodium hydro...

Embodiment 2

[0068] The difference from Example 1 is that the amount of reinforcing fibers used in this application is different. The wood fiber used in this example is 6.76 kg, and the glass fiber is 3.24 kg.

Embodiment 3

[0070] The difference from Example 1 is that the amount of reinforcing fibers used in this application is different. The wood fiber used in this example is 5.41 kg, and the glass fiber is 4.59 kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The application relates to the field of photocurable coatings, and specifically discloses a water-based UV photocurable coating and a preparation method thereof. The water-based uv light-curing coating, by weight, includes the following components: 70-90 parts of water-based aliphatic urethane acrylate oligomer emulsion, 6-10 parts of film-forming aid, 1-3 parts of photoinitiator, modified 1-4 parts of auxiliary agent, 3-5 parts of co-solvent, 10-12 parts of reinforced fiber, 6-10 parts of deionized water; the preparation method is: according to the proportion, modifying auxiliary agent, co-solvent and 70% of the formula Mix with deionized water, add reinforcing fiber, stir evenly, then add water-based aliphatic urethane acrylate oligomer emulsion, stir evenly, and mix in the photoinitiator, film-forming aid and deionized water of the remaining formula, Adjust the pH and viscosity to obtain the finished product. The water-based UV photocurable coating of the present application has the advantage of not being easy to crack.

Description

technical field [0001] The application relates to the field of light-curing coatings, and more particularly, it relates to a water-based UV light-curing coating and a preparation method thereof Background technique [0002] Light-curing coatings, also known as photosensitive coatings, use ultraviolet light as the energy for curing coatings, also known as UV-curing coatings. It does not require heating and cures rapidly to form films on flammable substrates such as paper, plastic, leather and wood. Water-based UV light-curing coatings combine the advantages of water-based and UV-curing technologies, solve the inherent shortcomings of low hardness and low adhesion of water-based coatings, and realize water-based environmental protection, low cost and high-efficiency applications. [0003] In the drying process of water-based light-curing coatings, first use hot air, infrared, microwave, etc. to dry the water, and pre-dry the coating; [0004] However, during the pre-drying s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C09D175/14C09D7/20C09D7/65C09D7/61C09D7/80
CPCC09D175/14C09D7/20C09D7/65C09D7/61C09D7/70C09D7/80C08L2205/16C08L97/02C08K7/14
Inventor刘个辉张志海刘水泉
Owner漳州市和兴涂料有限公司