Oil-removing and boiling-shrinking method and application of PTT and common polyester blended fabric

A blended fabric, oil-cooked technology, applied in the field of textiles, can solve the problems of easy occurrence of dead folds, unsuitable for PTT and ordinary polyester blended fabrics, etc., to achieve high bulkiness and abrasion resistance, excellent dyeability, good stretch The effect of resilience

Active Publication Date: 2021-09-03
PACIFIC (PANYU) TEXTILES LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] But above-mentioned method is not applicable to PTT and ordinary polyester blended fabric, and PTT and ordinary polyester blended fabric are prone to deadfold problem after finishing by above-mentioned method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil-removing and boiling-shrinking method and application of PTT and common polyester blended fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for deoiling and shrinking PTT and ordinary polyester blended fabrics, comprising: putting PTT and PET fiber blended fabrics into (penetrating agent) and (deoiling agent) with an initial temperature of 40°C, and setting the system at 0.5°C / Raise the temperature to 90°C in one minute, raise the temperature to 110°C at 1°C / min, keep it warm for 10 minutes, cool down to 50°C at 1°C / min, wash with water at 50°C for 8 minutes, drain, and complete the degreasing of the PTT and ordinary polyester blended fabrics Boil and shrink.

Embodiment 2

[0029]A method for deoiling and shrinking PTT and ordinary polyester blended fabrics, comprising: putting PTT and PET fiber blended fabrics into (penetrating agent) and (deoiling agent) with an initial temperature of 35°C, and setting the system at 0.4°C / Raise the temperature to 85°C in 1 minute, raise the temperature to 105°C at 0.8°C / min, keep it warm for 5 minutes, cool down to 40°C at 0.8°C / min, wash with water at 40°C for 5 minutes, drain, and complete the degreasing of the PTT and ordinary polyester blended fabrics Boil and shrink.

Embodiment 3

[0031] A method for deoiling and shrinking PTT and ordinary polyester blended fabrics, comprising: putting PTT and PET fiber blended fabrics into (penetrating agent) and (deoiling agent) with an initial temperature of 45 ° C, and the system is adjusted according to 0.6 ° C / Raise the temperature to 95°C in 1.2°C / min, raise the temperature to 115°C at 1.2°C / min, keep warm for 10 minutes, cool down to 60°C at 1.2°C / min, wash with water at 60°C for 10 minutes, drain, and complete the degreasing of the PTT and ordinary polyester blended fabrics Boil and shrink.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an oil-removing and boiling-shrinking method and application of a PTT and common polyester blended fabric. The oil-removing and boiling-shrinking method comprises the following steps of putting the PTT and common polyester blended fabric into a penetrating agent and an oil-removing agent, heating a system to 85-95 DEG C according to a speed of 0.4-0.6 DEG C / min, heating to 105-115 DEG C according to a speed of 0.8-1.2 DEG C / min, keeping the temperature for 5-15 minutes, and cooling to 40-60 DEG C to complete oil-removing and boiling-shrinking of the PTT and common polyester blended fabric. A textile fabric obtained by adopting the oil-removing and boiling-shrinking method has good stretching resilience, excellent dyeing property, high bulkiness and wear resistance, and has important research value.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a method for deoiling and shrinking PTT and ordinary polyester blended fabrics and its application. Background technique [0002] The existing dyeing and finishing general process is followed by pre-relaxation, setting, dyeing and finishing steps; in the process of spinning, drawing and weaving of textile fibers, in order to increase the smoothness of fibers, reduce the friction between fibers and between fibers and machines, To improve fiber cohesion, protect fiber strength, and reduce yarn breakage rate, a large amount of spinning oil should be added during the weaving process. In order to ensure the dyeing performance of the fiber and prevent the appearance of color flowers, color lakes and silicone oil spots, it is necessary to add a degreaser to the fabric before dyeing to remove the oil and oil stains on the cloth surface. PTT is commonly known as elastic poly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06B3/10
CPCD06B3/10
Inventor 曾广勇蔡清杰李明辉李成炳王海彬
Owner PACIFIC (PANYU) TEXTILES LTD