Preparation method of rust conversion agent

A rust transfer agent and the fourth technology, applied in the field of rust transfer agent preparation, can solve the problems of unpredictable coating effect, environmental damage, complicated procedures, etc., and achieve favorable chelation, excellent anti-corrosion performance, and good water solubility. sexual effect

Pending Publication Date: 2021-10-08
合肥蓝海新材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, after rust occurs, there are generally two methods of mechanical derusting and chemical derusting, the process is complicated, and it will cause certain damage to the environment.
Especially for the existing steel-based buildings, only manual rust removal can be used, and the rust removal effect is difficult to meet the requirements, resulting in the failure of the subsequent coating effect to meet expectations
[0003] Rust coating is currently a way to solve the above problems. In recent years, different types of rust conversion coatings have appeared. For parts with serious corrosion, rust conversion coatings cannot penetrate, and the film-forming sealing performance after conversion is not good enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of rust transfer agent, comprising the following steps:

[0027] The first step: add 6 parts by weight of deionized water and 6 parts by weight of ethanol into the mixing tank, mix and stir evenly, the stirring time is 5 minutes, and the stirring speed is 1500r / min;

[0028] The second step: add 1 weight part of tannic acid again, and stir while adding, and stir until the solid matter is completely dissolved;

[0029] Step 3: Add 0.3 parts by weight of isopropanol and 1 part by weight of phytic acid in sequence, and keep stirring until the solution is clear to obtain liquid A;

[0030] The 4th step: in the lacquer emulsion of 6 weight parts, add the rice husk flavone of 0.2 weight part, the phytic acid of 0.2 weight part, the citric acid of 0.2 weight part, fully stir and mix, in the described 4th step, stirring time is 15 Minutes, stirring speed is 2000r / min, makes B liquid;

[0031] Step 5: Slowly add the liquid A prepared in the third step to t...

Embodiment 2

[0033] A preparation method of rust transfer agent, comprising the following steps:

[0034] The first step: add 18 parts by weight of deionized water and 18 parts by weight of ethanol into the mixing tank, mix and stir evenly, the stirring time is 6 minutes, and the stirring speed is 1500r / min;

[0035] The second step: add 2 parts by weight of tannic acid, and stir while adding, and stir until the solid matter is completely dissolved;

[0036] Step 3: Add 0.4 parts by weight of isopropanol and 2 parts by weight of phytic acid in sequence, and keep stirring until the solution is clear to obtain liquid A;

[0037] The 4th step: in the lacquer emulsion of 18 weight parts, add the citric acid of the rice husk flavone of 0.3 weight part, the phytic acid of 0.4 weight part, 0.3 weight part, fully stir and mix, in the described 4th step, stirring time is 19 Minutes, stirring speed is 2000r / min, makes B liquid;

[0038] Step 5: Slowly add the liquid A prepared in the third step to...

Embodiment 3

[0040] A preparation method of rust transfer agent, comprising the following steps:

[0041] The first step: add 20 parts by weight of deionized water and 22 parts by weight of ethanol into the mixing tank, mix and stir evenly, the stirring time is 6 minutes, and the stirring speed is 1500r / min;

[0042] The second step: add 2 parts by weight of tannic acid, and stir while adding, and stir until the solid matter is completely dissolved;

[0043] The third step: add 1 weight part of isopropanol and 3 weight parts of phytic acid in sequence, and keep stirring until the solution is clear to obtain liquid A;

[0044] The 4th step: in the lacquer emulsion of 23 weight parts, add the citric acid of the rice husk flavone of 0.4 weight part, the phytic acid of 0.4 weight part, 0.3 weight part, fully stir and mix, in the described 4th step, stirring time is 20 Minutes, stirring speed is 2000r / min, makes B liquid;

[0045] Step 5: Slowly add the liquid A prepared in the third step to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a rust conversion agent. The preparation method comprises the following steps: 1, adding 6-30 parts by weight of water and 6-30 parts by weight of ethanol into a mixing barrel, and uniformly mixing and stirring; 2, adding 1-5 parts by weight of tannic acid, and stirring while adding until solids are completely dissolved; 3, sequentially adding 0.3-1.5 parts by weight of isopropanol and 1-5 parts by weight of phytic acid, and continuously stirring until the solution is clear to prepare a solution A; and 4, adding 0.2-1 part by weight of flavonoid substances, 0.2-1 part by weight of phytic acid and 0.2-1 part by weight of biological organic acid into 6-30 parts by weight of Chinese lacquer emulsion, and fully stirring and mixing the materials to prepare a solution B. The rust conversion agent is high in invasion performance, permeates into the deep part of a rust layer and is chelated with iron rust, a paint film and metal crystal grains, so that a uniform and compact passivation reaction film and a cross-linked coating film which are extremely high in chelating force are formed; and further oxidation corrosion is prevented.

Description

technical field [0001] The invention relates to the technical field of antirust coatings, in particular to a preparation method of a rust transfer agent. Background technique [0002] Steel will corrode under natural conditions, which not only affects its appearance, but also causes major safety accidents. In the prior art, anticorrosion coatings are usually used to treat steel base materials, and strict surface derusting treatment is carried out before coating the steel base materials. Moreover, after rust occurs, two methods of mechanical derusting and chemical derusting are generally used at present, the process is complicated, and it will cause certain damage to the environment. Especially for existing steel-based buildings, only manual derusting can be used, and the derusting effect is difficult to meet the requirements, resulting in the failure of the subsequent coating effect to meet expectations. [0003] Rust coating is currently a way to solve the above problems....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/50
CPCC23C22/50
Inventor 孙皋飞
Owner 合肥蓝海新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products