A kind of glass ceramics and preparation method thereof

A technology of glass ceramics and glass, which is applied in the field of glass ceramics and its preparation, and can solve the problems that it is difficult to obtain glass ceramics with a microscopic hierarchical structure.

Active Publication Date: 2021-12-24
WUHAN UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the above-mentioned technical deficiencies, provide a glass ceramic and its preparation method, solve the technical problem that it is difficult to obtain a glass ceramic with a microscopic hierarchical structure in the prior art, and further improve the mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glass ceramics and preparation method thereof
  • A kind of glass ceramics and preparation method thereof
  • A kind of glass ceramics and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] This specific embodiment also proposes a kind of preparation method of glass-ceramic, comprises the following steps:

[0030] S1. Raise the temperature of the precursor glass to T1 at a rate of 1-10°C / min and keep it warm for 1-4h. T1 is 540-580°C;

[0031] S2. Cool the precursor glass at a rate of 1-20°C / min to T2 and keep it warm for 1-4h, where T2 is 480-560°C, T1>T2;

[0032] S3, repeat steps S1-S2, continue to raise the temperature of the precursor glass to T3 and keep it warm for 1-4h, T3 is 560-650°C, T3>T1>T2;

[0033] S4. Continue to raise the temperature of the precursor glass treated in step S3 to 700-800° C. and keep it warm for 0.1-4 hours to obtain the glass-ceramic.

[0034] In some embodiments, before step S4, it further includes raising the temperature of the precursor glass to T4 and keeping it warm for 1-4 hours, where T4 is 610-690° C., and T4>T3.

Embodiment 1

[0037] The present embodiment proposes a kind of glass-ceramic, is made by following steps:

[0038] S1. Raise the temperature of the precursor glass to 580°C at a rate of 1°C / min and keep it warm for 1h;

[0039] S2. Lowering the temperature of the precursor glass to 480° C. at a rate of 1° C. / min and keeping it warm for 4 hours;

[0040] S3. Repeat steps S1-S2 once, continue to raise the temperature of the precursor glass to 600° C. and keep it warm for 1 hour;

[0041] S4. Continue to raise the temperature of the precursor glass to 750° C. and keep it warm for 2 hours to obtain the glass-ceramic.

[0042] The fracture toughness of the prepared glass ceramics is 2.2Mpa·m 1 / 2 , with a haze of 0.12, combined with figure 1 , the glass-ceramic has two micro-level structures; the micro-level structure includes a higher level structure formed by three-dimensional connected skeleton pillars, and the diameter of the higher level structure is about 50-150nm; the micro-level struct...

Embodiment 2

[0044] The present embodiment proposes a kind of glass-ceramic, is made by following steps:

[0045] S1. Raise the temperature of the precursor glass to 550°C at a rate of 5°C / min and keep it warm for 2 hours;

[0046] S2. Lowering the temperature of the precursor glass to 490° C. at a rate of 5° C. / min and keeping it warm for 3 hours;

[0047] S3. Repeat steps S1-S2 once, continue to raise the temperature of the precursor glass to 560° C. and keep it warm for 4 hours;

[0048] S4. Continue to raise the temperature of the precursor glass to 700° C. and keep it warm for 0.1 h to obtain the glass-ceramic.

[0049] The fracture toughness of the prepared glass ceramics is 1.0Mpa m 1 / 2 , with a haze of 0.2; combined with figure 2 , the glass-ceramic has more than two micro-level structures; the micro-level structure includes a higher-level structure formed by three-dimensional connected skeleton pillars, and the diameter of the higher-level structure is about 30-200nm; The mic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a glass ceramic and a preparation method thereof, belonging to the technical field of glass materials. The glass-ceramic, consisting of 40‑80% SiO 2 , 5‑25%Al 2 o 3 , 1‑15%Li 2 O, 0.5‑25%Na 2 O, 0.1‑1%K 2 O, 0-5%B 2 o 3 . The present invention also proposes a method for preparing glass ceramics, including: S1, heating the precursor glass to T1 and keeping it warm, T1 is 540-580°C; S2, cooling the precursor glass to T2 and keeping it warm, T2 is 480-560°C , T1>T2; S3, repeat step S1-S2, continue to heat the precursor glass to T3 and keep it warm, T3 is 560-650°C, T3>T1>T2; S4, continue to process the precursor in step S3 The glass is heated to 700-800° C. and kept warm to obtain the glass ceramics. The glass-ceramic has a microscopic hierarchical structure and excellent mechanical properties.

Description

technical field [0001] The invention relates to the technical field of glass materials, in particular to a glass ceramic and a preparation method thereof. Background technique [0002] As mobile electronic devices such as notebook computers, portable navigators, smart phones, etc. tend to become lighter and more powerful, people rely more and more on them. The increase in the frequency of use further puts forward higher requirements for packaging or casing materials of electronic devices, that is, making the packaging or casing materials lighter and thinner, and at the same time making the packaging or casing materials harder and stronger. [0003] Glass ceramics containing a large number of crystals (i.e., glass-ceramic) can greatly improve the flexural strength and fracture toughness of the material by extending the growth path of microcracks. Glass ceramics are usually crystallized and heat-treated on the precursor glass (mother glass), so that various crystals of unifor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C10/00C03B32/02
CPCC03C10/0027C03C10/0018C03B32/02
Inventor 陆平陶海征
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com