A technology of dopamine and dopamine hydrochloride, applied in separation methods, chemical instruments and methods, other chemical processes and other directions, can solve the problems of small adsorption capacity, no removal, and no adsorption selectivity of adsorbents, and achieves large adsorption capacity. Secondary pollution, good aldehyde removal effect

Pending Publication Date: 2022-01-14
SUZHOU IND PARK ANZEWEN ENVIRONMENTAL PROTECTION TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adsorption is now widely used to remove formaldehyde, but the adsorption capacity of the adsorbent is small,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formaldehyde removal material containing dopamine and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] Example 1

[0027] This embodiment provides a method of preparing a formaldehyde material having a dopamine, a preparation process schematic view figure 1 .

[0028] The preparation method includes the steps of:

[0029] Method for preparing formaldehyde materials containing dopamine, including the following steps:

[0030] S1, first, 6 parts of dopamine in a total of 6 parts, and the concentration is 5% hydrochloric acid, and the dopamine is becoming a hydrochloride after stirring for 4 h;

[0031] S2, the dopamine described in S1 is configured to 2% concentration of aqueous solution of 50 parts of distilled water;

[0032] S3, 40 parts of the carrier is impregnated in a dopamine solution for modification treatment to obtain the final product;

[0033] S4, the final product described in S3 was provided under an inert gas condition, and the initial temperature was 20 ° C, the temperature of the temperature was 5 ° C / min, and then the temperature was 90 ° C, i.e., the form...

Example Embodiment

[0034] Example 2

[0035] Method for preparing formaldehyde materials containing dopamine, including the following steps:

[0036] S1, 10 parts of dicamine first in the number of parts of 20 parts, the concentration of 17% hydrochloric acid, and the mixture is stirred into dopamine;

[0037] S2, a dopamine described in S1 is configured to 8% concentration of aqueous solution of 70 parts of distilled water;

[0038] S3, 50 parts of the carrier is impregnated in a dopamine solution for modification treatment to obtain the final product;

[0039] S4, the final product described in S3 was provided under an inert gas condition, and the initial temperature was 25 ° C, the heating rate was 7 ° C / min, and then the temperature was 115 ° C, i.e., the formaldehyde material.

Example Embodiment

[0040] Example 3

[0041] Method for preparing formaldehyde materials containing dopamine, including the following steps:

[0042] S1, 1 of 15 parts of dicamine is 20 parts by weight, and the concentration is 36% hydrochloric acid. After stirring for 6 h, it becomes a dopamine of hydrochloride;

[0043] S2, the dopamine described in S1 is configured to 25% concentration aqueous solution of 90 parts of distilled water;

[0044] S3, 60 parts of the carrier is impregnated in a dopamine solution for modification treatment to obtain the final product;

[0045] S4, the final product described in S3 was provided under an inert gas condition, and the initial temperature was 30 ° C, the temperature of the temperature was 9 ° C / min, and then the temperature was dried at a temperature of 140 ° C, i.e., the formaldehyde material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a formaldehyde removal material containing dopamine and a preparation method of the formaldehyde removal material, belonging to the field of formaldehyde removal. The formaldehyde removal material comprises the following raw material components in parts by weight: 6 to 15 parts of dopamine, 6 to 20 parts of acid, 40 to 60 parts of a carrier and 50 to 90 parts of distilled water. Specifically, the formaldehyde removal material comprises the following raw material components in parts by weight: 6 parts of the dopamine, 6 parts of the acid, 40 parts of the carrier and 50 parts of the distilled water; or 15 parts of the dopamine, 20 parts of the acid, 60 parts of the carrier and 90 parts of the distilled water. The carrier can be any one or a mixture of more than one selected from the group consisting of activated carbon, aluminum oxide, silica gel, a porous molecular sieve, diatomite, ceramic and the like. The prepared dopamine-containing formaldehyde removal material can quickly remove formaldehyde at room temperature, and is good in formaldehyde removal effect, large in adsorption capacity and free of secondary pollution.

Description

technical field [0001] The invention belongs to the field of preparation of formaldehyde-removing materials, and relates to a dopamine-containing formaldehyde-removing material and a preparation method thereof. Background technique [0002] People spend more than 80% of their time indoors on average every day, and the relationship between indoor air quality and human health is quite close. In recent years, the problem of indoor environmental pollution has become increasingly prominent, endangering human health and reducing human immunity. The most prominent pollutant in indoor environmental pollution is formaldehyde. Floor leather, floor tiles, chemical fiber carpets, plastic wallpapers, thermal insulation materials, urea-formaldehyde resin adhesives, and fiberboards and plywoods made of adhesives are commonly used indoors. Made of furniture, etc. can release formaldehyde. [0003] The current methods for removing formaldehyde are adsorption, photocatalysis, and noble meta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/22B01D53/04B01J20/30
CPCB01J20/22B01J20/14B01J20/16B01J20/205B01J20/20B01J20/0203B01D53/04B01D2257/93B01D2258/06
Inventor 余习文钟芳
Owner SUZHOU IND PARK ANZEWEN ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap