Tin-plated copper alloy conductor production process and tin-plated structure

A conductor production, tinned copper technology, applied in hot-dip plating process, metal material coating process, coating, etc., can solve the economic loss of enterprises, inconvenient soft wire, affecting the solderability of wires and signal transmission, etc. , to achieve the effect of reheating and reuse

Pending Publication Date: 2022-03-15
常熟市普华电工材料有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing tin-plated copper conductors have relatively poor performance in high temperature resistance and corrosion resistance, which will cause economic losses to enterprises during use
And the existing tin-plated copper conductor is easy to oxidize, which affects the solderability and signal transmission of the wire, and it is inconvenient to install the soft wire in the tinning machine during tinning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tin-plated copper alloy conductor production process and tin-plated structure
  • Tin-plated copper alloy conductor production process and tin-plated structure
  • Tin-plated copper alloy conductor production process and tin-plated structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A tinned copper alloy conductor production process, the specific steps are as follows:

[0040] Step 1, the grinding machine removes the surface oxide of the copper-aluminum rare-earth alloy billet, and obtains the copper-aluminum rare-earth alloy ingot;

[0041] Step 2: Stretch the aluminum alloy ingot with a water tank-type drawing machine, spray drawing oil synchronously during stretching, and the drawing speed is 400m / min, and obtain a busbar with a wire diameter of 2.05mm;

[0042] Step 3, the wire drawing machine draws the bus bar to obtain wire rods, and the diameter of the wire rods is 0.8mm;

[0043]Step 4. Put the wire rod in a heating furnace for softening treatment. The temperature of the heating furnace is controlled at 490°C. The heating furnace is combined with steam for anti-oxidation isolation. The softening speed is 200m / min to obtain soft wire;

[0044] Step 5. The soft wire is transported to the tinning machine, and the tinning machine evenly smears...

Embodiment 2

[0047] A tinned copper alloy conductor production process, the specific steps are as follows:

[0048] Step 1, the grinding machine removes the surface oxide of the copper-aluminum rare-earth alloy billet, and obtains the copper-aluminum rare-earth alloy ingot;

[0049] Step 2: Stretch the aluminum alloy ingot with a water tank-type drawing machine, spray drawing oil synchronously during stretching, and the drawing speed is 400m / min, and obtain a busbar with a wire diameter of 2.05mm;

[0050] Step 3, the wire drawing machine draws the bus bar to obtain wire rods, and the diameter of the wire rods is 0.8mm;

[0051] Step 4. Put the wire rod in a heating furnace for softening treatment. The temperature of the heating furnace is controlled at 510°C. The heating furnace is combined with steam for anti-oxidation isolation. The softening speed is 200m / min to obtain soft wire;

[0052] Step 5. The soft wire is transported to the tinning machine, and the tinning machine evenly smear...

Embodiment 3

[0056] Embodiment 3 is a further improvement to Embodiment 1.

[0057] Such as Figure 1-7 As shown, a tin-plating structure of a tin-plated copper alloy conductor production process, the tin-plating structure is the tinning machine in step five, the tin-plating structure includes a box body 1, and a V-shaped liquid collecting plate 5 is fixedly connected in the box body 1 The left and right ends of the top of the box body 1 are respectively connected with an outgoing wire guide structure 2 and an incoming wire guide structure 7 for guiding wires. The outgoing wire guide structure 2 and the incoming wire guide structure 7 have the same structure. The outgoing wire guide structure 2 includes guide rollers 21, rotating The shaft 22 and the rotating shaft 22, the supporting plate 23 are installed on the top of the box body 1, the inner wall of the supporting plate 23 is connected with the rotating shaft 22 through the bearing rotation, and the guiding roller 21 is evenly and fixe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a tinned copper alloy conductor production process and a tinned structure, and relates to the technical field of conductors, the tinned copper alloy conductor production process specifically comprises the following steps: step 1, removing surface oxides of a copper-aluminum-rare earth alloy blank by a polisher to obtain a copper-aluminum-rare earth alloy ingot; secondly, the aluminum alloy cast ingot is stretched through a water tank type drawing machine, drawing oil is sprayed synchronously during stretching, the drawing speed is 400 m / min, a bus is obtained, and the diameter of the bus is 2.05 mm; 3, a wire drawing machine carries out wire drawing treatment on the bus to obtain a wire rod, and the wire diameter of the wire rod is 0.8 mm; through the mode, the copper-aluminum rare earth alloy is replaced by the copper alloy wire, under the corrosion resistance of the copper element in the copper-aluminum rare earth alloy and the synergistic effect of the copper element and the aluminum element, the conductivity is not reduced while the surface oxidation resistance is improved, the weldability and the signal transmission of the wire are ensured, and meanwhile, the copper alloy wire has the advantages of being simple in structure and low in cost. And the soft wire can be conveniently mounted in the tinning structure during tinning.

Description

technical field [0001] The invention relates to the technical field of conductors, in particular to a tinned copper alloy conductor production process and a tinned structure. Background technique [0002] At present, the copper braided wires used in the market are generally TR-type annealed copper wires. This kind of copper braided wires uses a large amount of copper wires for braided wires for shielding. Although it has a good shielding effect, it consumes a lot of copper materials. Production costs are high. [0003] In order to reduce costs, tinned copper conductors are now used instead of copper wires. However, the existing tin-plated copper conductors have relatively poor performances such as high temperature resistance and corrosion resistance, and will cause economic losses to enterprises during use. Moreover, the existing tinned copper composite conductor is easy to oxidize, which affects the solderability and signal transmission of the wire, and it is inconvenient...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00C23C2/08C23C2/38
CPCB23P15/00C23C2/08C23C2/38
Inventor 朱雪江顾震江
Owner 常熟市普华电工材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap