Preparation method of efficient soft porcelain flexible face brick

A flexible veneer and soft porcelain technology, applied in the field of building materials, can solve the problems of low production efficiency of soft porcelain, long curing time, uneven curing, etc., so as to improve curing efficiency and production efficiency, reduce curing efficiency, and improve curing efficiency. Effect

Pending Publication Date: 2022-04-01
万卓(江苏)新材料有限公司
View PDF18 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present disclosure aims at the problems of low production efficiency of soft porcelain in the prior art, especially a series of problems such as long curing time, high energy consumption, uneven curing, etc., and provides a method for preparing high-efficiency soft porcelain flexible decorative tiles, the method Improve curing efficiency and production efficiency by changing the traditional curing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of efficient soft porcelain flexible face brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0055] The technical solutions in the embodiments of the present invention will be clearly and completely described below. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0056] In this embodiment, a kind of soft ceramic flexible veneer material and its preparation method are specifically provided. The preparation method includes the pretreatment of raw materials, including a certain amount of coupling agent and 1-3 parts of carbon black. Mix, obtain the composition of carbon black and coupling agent, wherein the mass ratio of coupling agent and carbon black is 1:2-3;

[0057] Since carbon black material is a good absorbing agent, it can absorb microwave significantly during microwave treatment, and rapid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a curing method of a high-efficiency soft porcelain flexible facing brick. The curing method comprises the following steps: 1, preparing a mixed emulsion; 2, preparing mixed powder; 3, adding the mixed emulsion into the mixed powder, adding 5-15 parts of water, and stirring to obtain soft porcelain slurry; 4, injecting the slurry in the step 3 into a mold; and 5, curing. Wherein the curing step comprises microwave curing treatment, meanwhile, due to the fact that a certain temperature exists on the outer layer of the soft porcelain slurry, the whole curing process is carried out inside and outside the soft porcelain slurry at the same time, and in order to further improve the curing efficiency, a wave absorbing agent is further added into the soft porcelain slurry, and the curing efficiency is improved.

Description

technical field [0001] The application relates to a building material, in particular to a green and environment-friendly building material, and more specifically to a preparation method of a high-efficiency soft porcelain flexible facing brick and the facing brick. Background technique [0002] Among the building materials, decorative bricks are an important branch, which can be widely used in wall facades and interior walls to decorate buildings. Common ones include imitation stone, imitation brick and so on. Soft porcelain facing brick is a new type of facing material. The preparation method is simple, the process is environmentally friendly, and it has strong machinability. It has a huge demand in the field of flexible facing materials, and soft porcelain facing bricks can greatly improve the aesthetics and grade. However, since it is obtained by forming and processing water-based polymer emulsion and inorganic substances such as cement, soil, quartz sand or mineral powd...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B40/02C04B28/00C04B14/02C04B20/02
Inventor 邓琪
Owner 万卓(江苏)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap