Non-linear infrared inorganic optical crystal and its preparing process

A technology of nonlinear optics and crystal materials, applied to the growth of polycrystalline materials, active dielectric materials, chemical instruments and methods, etc., can solve the problems of laser damage, small bandwidth of semiconductor materials, etc., and achieve air stability and good thermal stability Effect

Inactive Publication Date: 2003-02-12
WUHAN UNIV
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The semiconductor material has a small bandwidth, although the nonlinear optical coefficient is large, it is also easy to cause laser damage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-linear infrared inorganic optical crystal and its preparing process
  • Non-linear infrared inorganic optical crystal and its preparing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 0.81g (4mmol) CsBr and 1.46g (4mmol) CdI 2 Mix in about 3ml of double-distilled water, stir at 100°C for 3 hours, cool to room temperature naturally, and gradually precipitate a large number of colorless rod-shaped crystals. Suction filtration, and dry the product under an infrared lamp. Example 2: CsCdBr 3 single crystal growth

Embodiment 2

[0017] 0.81g (4mmol) CsBr and 1.46g (4mmol) CdI 2 Mix in about 3ml of double-distilled water, stir at 100°C for 3 hours, cool to room temperature naturally, and gradually precipitate a large number of colorless rod-shaped crystals. Suction filtration, and dry the product under an infrared lamp. Example 2: CsCdBr 3 single crystal growth

[0018] CsCdBr 3 The aqueous solution was placed in a 35°C incubator. Add small transparent seeds with no obvious defects. After 1 to 2 months, the hexagonal column-shaped transparent single crystal that grows into a larger size is the desired crystal material.

[0019] The obtained compound has been determined by X-ray single crystal structure, and its crystal structure arrangement is shown in the accompanying drawing. It can be seen that the anionic groups of this compound are in octahedral configuration, and form a one-dimensional chain structure in the form of coplanarity. The bond length analysis shows that the six Cd-Br bond length...

Embodiment 3

[0021] CsCdBr 3 Preparation: equimolar amounts of CsBr and CdI 2 Dissolve in double distilled water, reflux until the solution becomes transparent, filter, cool naturally, separate the precipitate and dry to obtain CsCdBr 3 .

[0022] CsCdBr 3 Single crystal growth: the resulting CsCdBr 3 Put it in a container, add twice-distilled water, heat to dissolve, put it in a constant temperature bath at 60°C, add a small transparent seed crystal without obvious defects, and after 15 days, it will grow into a larger-sized hexagonal column-shaped transparent single crystal. required crystal material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A CsCdBr3 crystal with central asymmetric structure, full transparency in visual and infrared region and high two-order non-linearity optical coefficient is prepared through dissolving CsBr and CdI2 in secondary distilled water, refluxing until solution becomes transparent, filtering, natural cooling to educe out CsCdBr3, adding secondary distilled water, thermal dissoving, putting in a thermostat at 30-60 deg.C, adding selected crystal seeds and growing for 15 days to obtain the hexaprismatic crystals.

Description

technical field [0001] The invention relates to an infrared inorganic nonlinear optical crystal material and a preparation method thereof, belonging to the field of inorganic chemistry and the field of optical materials. Background technique [0002] Nonlinear optical effects originate from the interaction between laser and medium. When the laser propagates in a medium with non-zero second-order polarizability, nonlinear optical effects such as frequency doubling, sum frequency, difference frequency, and parametric amplification will occur. Using the second-order nonlinear optical effect of crystals, nonlinear optical devices such as second-harmonic generators, frequency converters, and optical parametric oscillators can be made, which have important applications in many fields, such as laser technology and national defense. value. Inorganic nonlinear optical materials play a leading role in the practical research of second-order nonlinear optical materials. According to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C30B7/00C30B29/12H01S3/16
CPCC30B7/00
Inventor 任鹏秦金贵杨雪梅刘涛陈创天吴以成
Owner WUHAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap