Aqueous dispersion of polyamide rubber elastic body and method of producing the same
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Example
Example 1
[0052]A 500-ml separable flask was charged with 16 g of a polyether ester block amide copolymer (trade name: Pebax 2533SA01, melting point 134° C., manufactured by Arkema, Ltd.), 123 g of toluene and 61 g of isopropyl alcohol, and the copolymer was dissolved at 80° C. under stirring for 4 hours. To the resulting organic phase solution was added an aqueous solution prepared by dissolving 5.3 g of sodium polyoxyalkylene lauryl ether sulfate (trade name: Trax ET-314, 30 wt % active ingredient, manufactured by NOF Corporation) in 100 g of water. The resulting mixture was stirred and mixed for 2 minutes by means of a homomixer (trade name: TK Homomixer Type M, manufactured by Tokushu Kika Kogyo Co., Ltd.) to give an emulsion. The number of revolutions and temperature during stirring and mixing were set at 12,000 rpm and 40° C., respectively. The resulting emulsion was heated to 40 to 70° C. at a reduced pressure of 40 to 90 kPa thereby distilling off toluene and isopropyl alcoho...
Example
Example 2
[0053]An aqueous dispersion of polyamide rubber elastic body was obtained in the same manner as in Example 1 except that an aqueous solution prepared by dissolving 4.3 g of sodium polyoxyalkylene lauryl ether sulfate (trade name: Trax ET-314, wt % active ingredient, manufactured by NOF Corporation) and 0.3 g of polyvinyl alcohol (trade name: Gosenol GH-20, manufactured by Nippon Synthetic Chemical Industry Co., Ltd.) in 100 g of water was added to the organic phase solution.
Example
Example 3
[0054]An aqueous dispersion of polyamide rubber elastic body was obtained in the same manner as in Example 1 except that 2.0 g of sodium dioctylsulfosuccinate (trade name: Rapisol A-80, 80 wt % active ingredient, manufactured by NOF Corporation) was used in place of 5.3 g of sodium polyoxyalkylene lauryl ether sulfate (trade name: Trax ET-314, 30 wt % active ingredient, manufactured by NOF Corporation).
PUM
Property | Measurement | Unit |
---|---|---|
Percent by mass | aaaaa | aaaaa |
Percent by mass | aaaaa | aaaaa |
Particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap