Dedicated printing ink for electroplating products and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An ink and product technology, applied in the formulation of special ink for electroplating products and its preparation field, can solve the problems of few ink varieties, not resistant to alcohol scrubbing, high price, and achieve the effect of good adhesion
Inactive Publication Date: 2008-11-12
王崇高 +1
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] At present, there are not only few types of inks specially used for electroplating products on the market, but also the prices are very high.
In addition, this kind of ink also has the defect that it is not resistant to alcohol scrubbing.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] Weigh 10 grams of xylene, 5 grams of acetone, 10 grams of cyclohexanone, 5 grams of isopropanol, 1 gram of dispersant, 1 gram of wetting agent, 3 grams of nano-titanium dioxide, 4 grams of nano-scale colloidal calcium carbonate, ultrafine talc 2 grams of powder, 5 grams of high wear-resistant superfine carbon black, 3 grams of Hualan, stir at high speed for 45 minutes, then add 50 grams of single-component polyurethane resin, 1 gram of defoamer, continue to disperse for 2 hours before grinding After 3 hours, filter and fill to obtain the special ink for electroplating products.
Embodiment 2
[0019] Weigh 16 grams of xylene, 15 grams of ethyl acetate, 4 grams of butyl acetate, 1 gram of dispersant, 1 gram of wetting agent, 3 grams of nano-titanium dioxide, 5 grams of nano-zinc oxide, and 8 grams of titanium dioxide, and stir at high speed for 45 minutes , then add 46 grams of acrylic resin and 1 gram of defoamer therein, continue to disperse for 2 hours and then grind for 3 hours, filter and fill to obtain the special ink for electroplating products.
Embodiment 3
[0021] Weigh 7 grams of xylene, 15 grams of acetone, 8 grams of cyclohexanone, 1 gram of dispersant, 1 gram of wetting agent, 8 grams of nano-scale colloidal calcium carbonate, 2 grams of titanium dioxide, and 7 grams of chrome yellow, and stir at high speed for 45 minutes , then add 25 grams of epoxy resin and 1 gram of defoamer to it, continue to disperse for 2 hours and then grind for 3 hours, filter and fill to obtain component A of special ink for electroplating products; in addition, 25 grams of polyamide resin It is packaged separately and used as the B component of the special ink for electroplating products. Before use, the A and B components need to be mixed in proportion (the ratio is: A / B=3 / 1).
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The present invention belongs to the field of chemical industry, and relates to a special-purpose printing ink containing nano material, adhesive, solvent, pigment and adjuvant for electroplated product and its preparation method. Said invention is characterized by that firstly, the nano material, pigment and partial adjuvant are dispersed in solvent, then the adhesive and partial adjuvant are dispersed in said above-mentioned solvent, and then the above-mentioned mixture is undergone the process of grinding treatment so as to obtain the invented special-purpose printing ink for electroplated product.
Description
Technical field [0001] The invention belongs to the technical field of chemical industry, and relates to a formula of special ink for electroplating products and a preparation method thereof. Background technique [0002] At present, there are not only few types of inks specially used for electroplating products on the market, but also the prices are very high. In addition, this kind of ink also has the defect that it is not resistant to alcohol scrubbing. Invention content: [0003] The purpose of the present invention is to provide a special ink for electroplating products, the electroplating products include metal electroplating parts and plastic electroplating parts. [0004] In order to achieve the above purpose, a special ink for electroplating products of the present invention is mainly composed of adhesives, solvents, pigments, nano fillers and additives. The specific ratio is (percentage by weight): (1) adhesives account for 20-50% of the total ink; (2) pigments...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More