Alcohol-acid type wrinkled resin and preparing method

An alkyd, wrinkle technology, applied in the direction of coating, can solve the problems of wrinkle paint increasing safety hazards, easy powdering of paint film, easy to form glue and other problems, achieving good protection and decoration, energy saving, good hardness Effect

Inactive Publication Date: 2007-11-14
NANJING CHANGJIANG PAINT
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use of tung oil requires high-temperature refining, and the process requirements are very strict. If there are no trained workers, it will easily become gelatinous.
At the same time, there are many shortcomings in the wrinkle paint made of tung oil, such as the paint film is very easy to pulverize and yellow.
Furthermore, the use of wrinkle paint needs to be diluted with benzene, which also increases the safety hazard for the use of wrinkle paint.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] 1. Formula: maleic anhydride 50kg, dicyclopentadiene 50kg, linolenic acid 40kg, 95% glycerin 20kg, phthalic anhydride 20kg, adduct 10kg, xylene 5kg, dilute solvent 200#30kg.

[0053] 2. Preparation of raw material adducts:

[0054] (1) The reaction kettle is a reaction kettle equipped with a stirrer, a thermometer, a condensation device, and a temperature control device

[0055] (2) Add maleic anhydride into the reaction kettle, heat and melt, and add dicyclopentadiene dropwise at a temperature of 175-185°C.

[0056] (3) After 1.5 hours of heat preservation reaction, measure the melting point of the adduct, and when the melting point is greater than 60° C., cool down and discharge, and set aside.

[0057] 3. Preparation of alkyd wrinkle resin:

[0058] (1) The reaction kettle is a reaction kettle equipped with a stirrer, a thermometer, a reflux device, and a temperature control device.

[0059] (2) The reaction temperature is controlled between 195 and 205°C.

[006...

Embodiment 2

[0063] 1. Formula: 60kg maleic anhydride, 40kg dicyclopentadiene, 40kg linolenic acid, 25kg 95% glycerin, 20kg phthalic anhydride, 10kg adduct, 3kg xylene, and dilute solvent 200#20kg.

[0064] 2. Preparation of raw material adducts:

[0065] (1) The reaction kettle is a reaction kettle equipped with a stirrer, a thermometer, a condensation device, and a temperature control device

[0066] (2) Add maleic anhydride into the reaction kettle, heat and melt, and add dicyclopentadiene dropwise at a temperature of 190-200°C.

[0067] (3) After the heat preservation reaction for 1 hour, measure the melting point of the adduct, and when the melting point is greater than 60° C., cool down and discharge, and set aside.

[0068] 3. Preparation of alkyd wrinkle resin:

[0069] (1) The reaction kettle is a reaction kettle equipped with a stirrer, a thermometer, a reflux device, and a temperature control device.

[0070] (2) The reaction temperature is controlled between 220 and 230°C. ...

Embodiment 3

[0074] 1. Formula: maleic anhydride 55kg, dicyclopentadiene 45kg, linoleic acid 35kg, 95% glycerin 18kg, phthalic anhydride 18kg, adduct 6kg, xylene 8kg, dilute solvent 200#10kg.

[0075] 2. Preparation of raw material adducts:

[0076] (1) The reaction kettle is a reaction kettle equipped with a stirrer, a thermometer, a condensation device, and a temperature control device

[0077] (2) Add maleic anhydride to the reaction kettle, heat and melt, and add dicyclopentadiene dropwise at a temperature of 160-170°C.

[0078] (3) After holding the reaction for 2 hours, measure the melting point of the adduct, and when the melting point is greater than 60° C., cool down and discharge, and set aside.

[0079] 3. Preparation of alkyd wrinkle resin:

[0080] (1) The reaction kettle is a reaction kettle equipped with a stirrer, a thermometer, a reflux device, and a temperature control device.

[0081] (2) The reaction temperature is controlled between 170 and 180°C.

[0082] (3) Add ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a kind of alkyd wrinkles resin. The alkyd wrinkles resin comprises linolenic acid, 95% glycerine, phthalic anhydride, adduct, xylene, and diluted solvent. The present invention also discloses the preparation method of the said alkyd wrinkles resin. The present invention avoids the general existing process of high-temperature refining tung oil and many defects of winkles paint brought by adding tung oil, and makes the process of synthesizing winkles paint resin simply and easy to operate, and also saves energy. The resin-prepared winkles paint synthesized by using the present invention, has no necessary to be diluted with benzene before using, which makes it more secure and more environmentally friendly for the use of winkles paint, and meets the overall trend of current development of paints.

Description

technical field [0001] The invention belongs to the technical field of organic synthesis, and in particular relates to a novel resin and a preparation method thereof. Background technique [0002] As a kind of art paint, wrinkle paint is the same as the commonly used hammer paint and orange paint. It has a wide range of uses. It can be used on metal surfaces such as instruments, meters, hardware, security doors, etc., and has a good protective and decorative effect. According to the prior art, the resins for wrinkle paints mainly include phenolic resins and alkyd resins, and the wrinkle paints prepared by these two types of resins all need to add tung oil. The use of tung oil requires high-temperature refining, and the process requirements are very strict. If there are no trained workers, it will easily become glue. Simultaneously, there are many disadvantages in the wrinkle paint made of tung oil, such as very easy chalking and yellowing of the paint film. Furthermore, in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/48C09D5/28
Inventor 温静卫王仁祥邱绕生
Owner NANJING CHANGJIANG PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka