Supersonic spray coating method of crystallizer copper plate

A crystallizer copper plate, supersonic spraying technology, applied in the direction of coating, molten spraying, metal material coating process, etc., can solve the problems of frequent copper plate replacement, low performance and price, low bonding strength, etc.

Active Publication Date: 2008-11-12
XIXIA LONGCHENG SPECIAL MATERIALS CO LTD
View PDF1 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the bonding strength of spraying has not been high, and it is easy to fall off, which easily affects the use effect of the crystallizer copper plate
The crystallizer copper plate produced by t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Supersonic spray coating method of crystallizer copper plate
  • Supersonic spray coating method of crystallizer copper plate
  • Supersonic spray coating method of crystallizer copper plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The supersonic spraying method of the crystallizer copper plate is carried out according to the following steps: first, the surface of the mold copper plate is cleaned and sandblasted with the conventional cleaning process; ° guards, such as figure 1 , 2 , The angle between the copper plate working surface and the guard plate shown in 3 can be 90 °, 135 ° or 180 °; then the nickel-based alloy powder spray coating such as NiCrBSi alloy powder is packed into the supersonic flame spraying equipment, and the crystallization is carried out according to the conventional procedure The surface of the copper plate of the crystallizer is sprayed; finally, after spraying the copper plate of the crystallizer, it is kept at 800°C-950°C for 0.5-3 hours for melting and diffusion vacuum heat treatment, so that the coating and the base material produce a miscible diffusion layer, which is formed by the original mechanical bonding. It is transformed into interpenetrating and miscible me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a supersonic spraying method for crystal implement copper plates, which is characterized in that the operation of the method is carried out according to the following steps that: firstly, cleaning and sand blasting treatments are carried out to the surface of a crystal implement copper plate through a conventional cleaning process; secondly, four peripheries of thecrystal implement copper plate are provided with protective plates at an angle of between 90 and 180 degrees with a working surface of the copper plate; thirdly, nickel-base alloy powder spraying paint is put into a supersonic flame spraying device so as to spray the surface of the crystal implement copper plate through a conventional process; fourthly, after spraying, the crystal implement copper plate is insulated at a temperature of between 800 and 950 DEG C for 0.5 to 3 hours for melting-diffusing vacuum heat treatment, and then is cooled through nitrogen, argon or helium; fifthly, the cooled crystal implement copper plate is subject to aging treatment at a temperature of between 400 and 500 DEG C for 1 to 3 hours. The supersonic spraying method is simple in the whole spraying process and uniform in spraying thickness, saves spraying material, and is strong in coating binding capacity and is wearproof.

Description

technical field [0001] The invention belongs to the technical field of spraying, and in particular relates to a supersonic spraying method for a crystallizer copper plate. Background technique [0002] In the known technology, in the past, the crystallizer copper plate was plated with Cr, NiFe, NiCo, CoNi, Ni or Ni+Cr in order to improve the wear resistance of the working surface, so as to improve the service life of the copper plate. Spray wear-resistant coating on the copper plate of the crystallizer, as the patent of the authorized announcement date on November 28, 2007, the authorized announcement number CN 100351420C discloses a method for supersonic flame spraying the copper plate of the crystallizer, which is characterized in that it includes the following method steps: first use The conventional cleaning process cleans and blasts the surface of the crystallizer copper plate; secondly, take 50%-95% of nickel-based alloy particles according to the total mass percentage...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23F17/00C23C4/06C23C4/02C23C4/18C21D9/00C23C4/129
Inventor 朱书成王希彬曹国超吕艳伍李仿
Owner XIXIA LONGCHENG SPECIAL MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap