Toner bottle for electrostatic latent image developing
A toner bottle and toner technology, applied in the direction of developer, electric recording process using charge pattern, equipment for electric recording process using charge pattern, etc., can solve problems such as unstable toner supply
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0035] There is no particular limitation on the production method of the toner of the present invention. In addition, conventionally known resins or colorants can also be used as the binder resin or colorant for toner.
[0036] The shape distribution of the toner particles suitable for the present invention preferably uses a shape distribution having a ratio of the major axis to the minor axis described below. In this way, good cleanability and transferability, excellent halftone (Ha-ft-n) images can be obtained, and stable high-quality images can be obtained.
[0037] (preferable toner particle shape)
[0038] Preferable toner particle shapes used in the present invention are, for example, defined as follows.
[0039] exist Figure 7 shows toner particles having the following shape: 1) At least one projected surface profile of each toner particle is sandwiched by two parallel lines in a contacting manner at points A1 and A2 The closed curve of the toner particle is the ma...
Embodiment
[0168] Hereinafter, the embodiments of the present invention will be specifically described by way of examples, but the present invention is not limited thereto.
[0169] 1. Toner Preparation
[0170] The toner is manufactured as follows.
[0171] (1) Production of colored particles 1
[0172] (Manufacture of resin microparticles A1)
[0173] In the reaction container that stirrer, temperature sensor, cooling pipe, nitrogen introduction device are installed, add 8 mass parts sodium lauryl sulfate and 3000 mass parts ion-exchanged water, stir with the stirring speed of 230rpm under nitrogen flow , allowing the internal temperature to rise to 80°C. After completion of the temperature rise, a polymerization initiator solution obtained by dissolving 10 parts by mass of potassium persulfate in 200 parts by mass of ion-exchanged water was added, and the temperature was adjusted to 80°C.
[0174] Next, a polymerizable monomer mixed solution containing the following compound was d...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com