Method for making high-filtering and electrostatic resistance overlay film compound punched felt

A manufacturing method and composite needle technology, which can be used in non-woven fabrics, textiles, papermaking, fiber processing, etc., and can solve problems such as electrostatic dust collection and unsatisfactory filtering effects

Active Publication Date: 2009-04-15
中材科技膜材料(山东)有限公司
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high-filtration, antistatic film-coated composite needle-punched felt manufacturing method to solve the problems of unsatisfactory filtering effect and electrostatic dust absorption in existing filter materials in actual use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention will be further described below in conjunction with specific examples.

[0029] In the chopped fiber layer of the composite needle felt, the composition of each fiber is shown in Table 1 according to the weight ratio:

[0030] The weight ratio (%) of each fiber in the composite mat of table 1

[0031] Example serial number

1

2

3

4

5

6

7

8

glass fiber

95

90

85

80

75

65

60

50

P84 fiber

5

10

10

13

10

15

10

15

Kermel fiber

0

0

5

7

15

20

30

35

[0032] The manufacturing steps of the composite felt are: weigh various chopped fibers in different proportions, spread the chopped fibers evenly on the conveyor belt, loosen them with an opener, and comb them into a loose fiber layer with a uniform thickness by a carding machine. Then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a manufacturing method of a high-filtration anti-static tectorial membrane composite needled felt, which is characterized in that the composite needled felt is formed by that after being treated with anti-static processing, a composite needled felt plain felt is treated with hot pressing draping with a polyfluortetraethylene microporous membrane. The composite needled felt has good anti-static performance, high filtration efficiency and strong folding endurance, and the service life of the composite needled felt is greatly prolonged.

Description

technical field [0001] The invention relates to a method for manufacturing a high-filtration, antistatic film-coated composite needle-punched felt, which belongs to the field of glass fiber filter materials used for manufacturing industrial flue gas filter products. Background technique [0002] At present, the traditional needle-punched filter materials at home and abroad adopt non-woven needle-punched technology and composite technology, and most of them have a three-dimensional interlaced structure, which can give full play to the dust-catching function of the fiber, and the dust-catching effect is stable; the needle-punched felt has no or only a small amount (with Base cloth) twisted warp and weft yarns have small pores, large porosity, uniform distribution, and a total porosity of 70-80%, which is 1.6-2 times that of general woven filter materials, so it has good air permeability and resistance Low. However, the filtration efficiency of ordinary needle felt filter mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/46D06M15/263D06M15/256D06M13/50D06M101/30D04H1/4382
Inventor 严荣楼费传军时志权项朝卫沈庆月朱平章君荣
Owner 中材科技膜材料(山东)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap