Desulfurization gypsum basic steel slag composite gelled material and preparation method thereof
A technology of composite cementitious material and desulfurization gypsum, which is applied in the field of desulfurized gypsum-based steel slag composite cementitious material and its preparation, can solve the problems of low utilization rate of steel slag and desulfurized gypsum, and achieves the advantages of large-scale production, improved utilization rate, alkalinity moderate effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0036] The desulfurized gypsum-based steel slag composite cementitious material is made of the following raw materials in weight percentage:
[0037] Take the specific surface area as 3800-4000cm 2 / g, the fineness is 300 mesh desulfurization gypsum 850g, the specific surface area is 3000-4500cm 2 / g, fineness is 300 mesh steel slag 150g, stimulator 20g, described stimulant is formed by mixing sodium silicate, kaolin, aluminum potassium sulfate accounting for respectively 20%, 30%, 50% of the percentage of stimulator weight.
[0038] Prepared as follows:
[0039] (1) Grind the steel slag in a Ф500×500mm test mill for 2-4 hours, and sieve it for later use; sieve the desulfurized gypsum to remove large particles, and set it aside for later use;
[0040] (2) Utilize the building gypsum consistency meter to measure the water consumption of the standard consistency of the cementitious material, measure the water of the standard consistency water consumption with a graduated cylin...
Embodiment 2
[0044] The desulfurized gypsum-based steel slag composite cementitious material is made of the following raw materials in weight percentage:
[0045] 650g of desulfurized gypsum, 350g of steel slag, and 1g of activator. The activator is formed by mixing sodium silicate, kaolin, and potassium aluminum sulfate accounting for 20%, 30%, and 50% of the weight of the activator respectively.
[0046] The preparation method is the same as in Example 1 except that the curing method is changed to the standard curing with a temperature of 20±2°C and a humidity of 95%.
Embodiment 3
[0048] The desulfurized gypsum-based steel slag composite cementitious material is made of the following raw materials in weight percentage:
[0049] Desulfurization gypsum 900g, steel slag 100g, activator 10g, described activator is formed by mixing sodium silicate, aluminum sulfate, kaolin, and aluminum potassium sulfate respectively accounting for 9%, 30%, 30%, and 31% of the percentage by weight of the activator become.
[0050] The preparation method is the same as in Example 1 except that the curing method is changed to natural curing in the air (temperature 20±2°C) for 1 day, and then put into a curing box for standard curing (temperature 20±2°C, humidity 95%).
PUM
Property | Measurement | Unit |
---|---|---|
specific surface area | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com