Method for manufacturing crystal glaze color paintings

A manufacturing method and technology of crystalline glaze are applied in the field of manufacturing crystalline glaze color paintings, which can solve the problems of increasing the difficulty of making crystalline glaze color paintings, inability to convert them, etc., and achieve the effects of bright and colorful colors, blue luster and high definition.

Inactive Publication Date: 2012-05-09
吴渭阳
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Underglaze blue and white paintings are painted on three-dimensional crystal glazes. The blue and white pigments must be completely integrated into the glaze during firing. It is difficult to make, so no one has fully applied underglaze blue and white and underglaze five colors to crystal glaze, so it is impossible to transform the traditional decoration glaze of crystal glaze into a deeper artwork-crystal glaze painting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of manufacture method of crystalline glaze painting, comprises the following steps:

[0026] 1) Decorate ceramics with underglaze multicolored pigments;

[0027] 2) Put the ceramics in the kiln and burn them to 900°C, so that the underglaze multicolored pigments are firmly fixed on the surface of the ceramics and do not lose color due to glazing;

[0028] 3) Apply or spray transparent glaze on the surface of the pattern painted with underglaze multicolored pigments, and apply three-dimensional crystal glaze on other parts of the ceramic surface;

[0029] 4) The ceramics are heated up to 1000°C in an oxidizing atmosphere, and then cooled naturally, and the transparent glaze and the three-dimensional crystal art glaze are fired and solidified.

[0030] The speed of heating in the kiln in the above step 4): 2.5 hours to uniformly heat up to 1100° C., and cool naturally.

[0031] The three-dimensional crystal glaze uses the following ores and compounds as raw mater...

Embodiment 2

[0036] A kind of manufacture method of crystalline glaze painting, comprises the following steps:

[0037] 1) Decorate ceramics with underglaze multicolored pigments;

[0038] 2) Put the ceramics in the kiln and burn them to 900°C, so that the underglaze multicolored pigments are firmly fixed on the surface of the ceramics and do not lose color due to glazing;

[0039] 3) Apply or spray transparent glaze on the surface of the pattern painted with underglaze multicolored pigments, and apply three-dimensional crystal glaze on other parts of the ceramic surface;

[0040] 4) The ceramics are heated up to 1000°C in an oxidizing atmosphere, and then cooled naturally, and the transparent glaze and the three-dimensional crystal art glaze are fired and solidified.

[0041] 5) Painting with underglaze blue and white pigments on the three-dimensional crystal glaze;

[0042] 6) Raise the temperature to 1320°C in an oxidizing atmosphere, quickly cool down to 1130°C, then keep the tempera...

Embodiment 3

[0053] A kind of manufacture method of crystalline glaze painting, comprises the following steps:

[0054] 1) Decorate ceramics with underglaze multicolored pigments;

[0055] 2) Put the ceramics in the kiln and burn them to 900°C, so that the underglaze multicolored pigments are firmly fixed on the surface of the ceramics and do not lose color due to glazing;

[0056] 3) Apply or spray transparent glaze on the surface of the pattern painted with underglaze multicolored pigments, and apply three-dimensional crystal glaze on other parts of the ceramic surface;

[0057] 4) The ceramics are heated up to 1000°C in an oxidizing atmosphere, and then cooled naturally, and the transparent glaze and the three-dimensional crystal art glaze are fired and solidified.

[0058] 5) Painting with underglaze blue and white pigments on the three-dimensional crystal glaze;

[0059] 6) Raise the temperature to 1300°C in an oxidizing atmosphere, quickly cool down to 1130°C, then keep the tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for manufacturing crystal glaze color paintings, comprising the following steps: 1) glozing on ceramics by under-glaze colored pigment; 2) placing the ceramics in a kiln and burning to 900 DEG C to lead the under-glaze colored pigment to be fastened on the surface of the ceramics without color runaway due to glazing; 3) applying or spraying transparent glaze on pattern surface painted with under-glaze colored pigment, and applying tri-dimensional crystal glaze on other parts of the surface of the ceramics; and 4) boosting the temperature of the ceramics to 1000DEG C under oxidation atmosphere, then lowering the temperature naturally, and glaze firing the transparent glaze and the tri-dimensional crystal glaze. Compared with the prior art, the invention hasthe beneficial effects that the manufactured crystal glaze color paintings have colorful pictures, glossy color, high definition, tri-dimensional and glittering and translucent crystal flower due to infusing green flower pigment into the tri-dimensional crystal glaze, and can radiate dazzling rays with light rotation; the color thereof is bright and colorful, harmonious and beautiful.

Description

technical field [0001] The invention relates to a method for manufacturing a crystal glaze color painting. Background technique [0002] The crystal glaze color painting is to use the technique of isolation to integrate the underglaze multicolored painting into the three-dimensional crystal glaze, and at the same time add blue and white elements to make the expression of the crystal glaze color painting richer and more tasteful. This kind of production method is unprecedented, its technical difficulty is extremely high, and at the same time it requires the producer to have deep artistic skills. Because the three-dimensional crystal glaze is a kind of artistic glaze that contains artificial crystals in the glaze and presents crystal flowers of various colors, it is brilliant and unique. The conditions for the formation of artificial crystals of three-dimensional crystalline glazes, the firing conditions, and the thickness of the glaze are mutually restrained but complement e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86C04B33/34
Inventor 吴渭阳吴泽腾吴泽帆
Owner 吴渭阳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com