Method for Producing V-belts Using High-Pressure Penetrating Single-sided Rubber Cloth

A technology of triangular belts and adhesive cloths, applied in applications, belts, household appliances, etc., can solve the problems of wrapping cloth and rubber materials that are prone to heat, delamination and chipping, non-compliant V-belts without static electricity, and affecting comprehensive performance and quality. Achieve the effects of improving comprehensive product quality, improving vulcanization process performance, and guaranteeing comprehensive quality and performance

Inactive Publication Date: 2011-12-28
河北凯隆固异特橡胶股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, the double-sided adhesive cloth is generally used as the outsourcing cloth, and the V-belt produced by the traditional processing technology of the ordinary V-belt is unstable and noisy during operation, and the covering cloth and rubber are easy to generate heat and delaminate. Chips, the service life is short, which affects the overall performance and quality of the belt, and generally does not meet the special requirements of the V-belt running without static electricity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for Producing V-belts Using High-Pressure Penetrating Single-sided Rubber Cloth
  • Method for Producing V-belts Using High-Pressure Penetrating Single-sided Rubber Cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Embodiment 1: the method for producing V-belts using high-pressure permeable single-sided rubber cloth comprises the following steps:

[0047] (1) The equipment of raw and auxiliary materials:

[0048] Consists of the following raw materials in parts by mass ratio:

[0049] EPDM rubber 80; AR rubber 20;

[0050] Nano Zinc Oxide 2.5; Hard Acid 1;

[0051] Antiaging agent D 1.5; Antiaging agent 4010 1;

[0052] Accelerator TMTD 1.5; Accelerator M 0.5;

[0053] Vulcanizing agent 1.5; Nano white carbon black 35;

[0054] Binder 3; Dispersant 1;

[0055] Active agent 1; Softener 3.5;

[0056] Plasticizer 3;

[0057] Diameter and weft density 3×3 pieces of cloth 100 meters;

[0058] The V-belt core is type A.

[0059] (2) Processing of wipe glue:

[0060] ①Plastication of raw rubber:

[0061] Step 1: After the prepared raw rubber is crushed and held on the roll on the open mill, it is thinned 8 times under the conditions of the roll temperature of 45°C and the roll...

Embodiment 2

[0084] The method for producing a V-belt by using a high-pressure permeable single-sided adhesive cloth comprises the following steps:

[0085] (1) The equipment of raw and auxiliary materials:

[0086] Consists of the following raw materials in parts by mass ratio:

[0087] EPDM 65; AR rubber 30;

[0088] Nano Zinc Oxide 4; Hard Acid 0.5;

[0089] Antiaging agent D 2; Antiaging agent 4010 1;

[0090] Accelerator TMTD 1; Accelerator M 0.5;

[0091] Vulcanizing agent 2; Nano white carbon black 40;

[0092] Binder 1; Dispersant 1;

[0093] active agent 2; softener 3;

[0094] Plasticizer 3;

[0095] Diameter and weft density 3×3 pieces of cloth 100 meters;

[0096] The V-belt core is type A.

[0097] (2) Processing of wipe glue:

[0098] ①Plastication of raw rubber:

[0099] Step 1: After the prepared raw rubber is crushed and held on the roll on the mill, under the conditions of the roll temperature of 55°C and the roll pitch of 2mm, pass through the thinner 8 times ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for producing V-belts by using high-pressure permeable single-sided rubber-rubbing cloth. The raw and auxiliary materials include EPDM rubber, raw rubber, and nano-zinc oxide. Cloth treatment and vulcanization treatment of the V-belt, the product is obtained. The V-belt processed by the invention runs smoothly and has no noise, no delamination and chipping phenomenon, long running life, and no static electricity in the V-belt operation, which meets the special requirements of the V-belt.

Description

technical field [0001] The invention relates to a processing method for a V-belt, in particular to a method for producing a V-belt by using a high-pressure permeable single-sided adhesive cloth. Background technique [0002] In the prior art, the double-sided adhesive cloth is generally used as the outsourcing cloth, and the V-belt produced by the traditional processing technology of the ordinary V-belt is unstable and noisy during operation, and the covering cloth and rubber are easy to generate heat and delaminate. Chips, the service life is short, which affects the comprehensive performance and quality of the belt, and generally does not meet the special requirements of the V-belt running without static electricity. Contents of the invention [0003] The purpose of the present invention is to overcome the above deficiencies and provide a processing method for high-pressure permeable single-sided adhesive cloth and V-belt, which can solve the technological performance pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29D29/00C08L23/16C08L7/00C08K13/02C08K3/36C08K3/22B29B7/56B29B7/72B29B7/28B29C35/04
Inventor 王淑霞林昱彤林栋梁
Owner 河北凯隆固异特橡胶股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com