Water-base fast-drying high gloss ambient crosslinking nail paint resin and preparation method thereof

A room temperature cross-linking, high-gloss technology, applied in the field of biopharmaceuticals, can solve problems such as human health effects and nail damage, and achieve the effects of protecting human health, short drying time, and ensuring paint film thickness

Inactive Publication Date: 2010-08-25
BEIJING CARL RES INST FOR CHEM IND
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing nail paint ingredients are all organic chemicals, which contain harmful chemical sub

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] Below in conjunction with the examples, the present invention is further described, the following examples are illustrative, not limiting, and the protection scope of the present invention cannot be limited by the following examples.

[0032] A water-based fast-drying high-gloss room temperature crosslinking nail varnish resin, its composition and parts by weight are respectively:

[0033] 17-20 parts of n-butyl acrylate

[0034] 4-7 parts of n-butyl methacrylate

[0035] 11-14 parts of methyl methacrylate

[0036] 1-2 parts of styrene

[0037] 2-3 parts of methacrylic acid

[0038] 2-3 parts of diacetone acrylamide

[0039] 2-3 parts of adipic acid dihydrazide

[0040] Ammonium persulfate 0.5-1 part

[0041] Emulsifier OP-10 0.4-0.8 parts

[0042] Emulsifier sodium lauryl sulfate 0.5-1 part

[0043] 1-2 parts of ammonia water

[0044] 42-58 parts of deionized water.

[0045] A kind of preparation method of water-based quick-drying high-gloss room temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a water-base fast-drying high gloss ambient crosslinking nail paint resin and a preparation method thereof. The composition components comprise n-butyl acrylate, n-butyl methacrylate, methyl methacrylate, styrene, methacrylic acid, diacetone acrylamide, adipic dihydrazide, ammonium persulfate, emulsifier OP-10, emulsifier sodium dodecyl sulfate, ammonia and deionized water. After the resin is prepared into water-base nail paint (also called nail polish), the content of volatile organic compounds is less than 20 gram per liter, the nail paint does not contain harmful substances, such as triphenyl, formaldehyde and the like, has no poison and no smell, is harmless to human bodies and has no pollution to the environment, short drying time, strong adhesion and water resistance, high brightness of the paint film, bright color and strong color retention, as the solid content of the resin is high, the paint film thickness of thin painting is guaranteed, the surface is full and smooth, and the resin is an environmental-friendly product which can protect human health and is a substitute of nitro-nail paint which is commonly used in market currently.

Description

technical field [0001] The invention belongs to the field of biopharmaceuticals, in particular to a water-based fast-drying high-gloss room temperature cross-linked nail paint resin and a preparation method thereof. Background technique [0002] It is people's nature to love beauty, and nail armor is also a popular fashion today, so nail paint has also become a fashion product. But the existing nail varnish ingredients are all organic chemicals, which contain harmful chemical substances such as triphenyl and formaldehyde, which not only damage the nails, but also affect human health. [0003] Through searching, two relevant patents were found. The first is a method for preparing water-soluble nail polish (CN1785154). Gelatin is used as a raw material to prepare a gelatin aqueous solution with a mass volume concentration of 15%-25%, and at the same time, lauryl sulfuric acid with a mass volume concentration of 0.001% is added Ammonium, stir evenly at 75-85°C to form a gelat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/81A61Q3/02
Inventor 王亮陈力
Owner BEIJING CARL RES INST FOR CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap