Water-base fast-drying high gloss ambient crosslinking nail paint resin and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A room temperature cross-linking, high-gloss technology, applied in the field of biopharmaceuticals, can solve problems such as nail damage and human health effects, and achieve the effects of short drying time, protection of human health, strong adhesion and water resistance
Inactive Publication Date: 2011-07-20
BEIJING CARL RES INST FOR CHEM IND
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the existing nail paint ingredients are all organic chemicals, which contain harmful chemical substances such as triphenyl and formaldehyde, which not only damage the nails, but also affect human health.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0031] Below in conjunction with the examples, the present invention is further described, the following examples are illustrative, not limiting, and the protection scope of the present invention cannot be limited by the following examples.
[0032] A water-based fast-drying high-gloss room temperature crosslinking nail varnish resin, its composition and parts by weight are respectively:
[0033] 17-20 parts of n-butyl acrylate
[0034] 4-7 parts of n-butyl methacrylate
[0035] 11-14 parts of methyl methacrylate
[0036] 1-2 parts of styrene
[0037] 2-3 parts of methacrylic acid
[0038] 2-3 parts of diacetone acrylamide
[0039] 2-3 parts of adipic acid dihydrazide
[0040] Ammonium persulfate 0.5-1 part
[0041] Emulsifier OP-10 0.4-0.8 parts
[0042] Emulsifier sodium lauryl sulfate 0.5-1 part
[0043] 1-2 parts of ammonia water
[0044] 42-58 parts of deionized water.
[0045] A kind of preparation method of water-based quick-drying high-gloss room temperature ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The present invention relates to a water-base fast-drying high gloss ambient crosslinking nail paint resin and a preparation method thereof. The composition components comprise n-butyl acrylate, n-butyl methacrylate, methyl methacrylate, styrene, methacrylic acid, diacetone acrylamide, adipic dihydrazide, ammonium persulfate, emulsifier OP-10, emulsifier sodium dodecyl sulfate, ammonia and deionized water. After the resin is prepared into water-base nail paint (also called nail polish), the content of volatile organic compounds is less than 20 gram per liter, the nail paint does not contain harmful substances, such as triphenyl, formaldehyde and the like, has no poison and no smell, is harmless to human bodies and has no pollution to the environment, short drying time, strong adhesion and water resistance, high brightness of the paint film, bright color and strong color retention, as the solid content of the resin is high, the paint film thickness of thin painting is guaranteed, the surface is full and smooth, and the resin is an environmental-friendly product which can protect human health and is a substitute of nitro-nail paint which is commonly used in market currently.
Description
technical field [0001] The invention belongs to the field of biopharmaceuticals, in particular to a water-based fast-drying high-gloss room temperature cross-linked nail paint resin and a preparation method thereof. Background technique [0002] It is people's nature to love beauty, and nail armor is also a popular fashion today, so nail paint has also become a fashion product. But the existing nail varnish ingredients are all organic chemicals, which contain harmful chemical substances such as triphenyl and formaldehyde, which not only damage the nails, but also affect human health. [0003] Through searching, two relevant patents were found. The first is a method for preparing water-soluble nail polish (CN1785154). Gelatin is used as a raw material to prepare a gelatin aqueous solution with a mass volume concentration of 15%-25%, and at the same time, lauryl sulfuric acid with a mass volume concentration of 0.001% is added Ammonium, stir evenly at 75-85°C to form a gelat...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.