Terylene short fiber oil

A technology of polyester staple fiber and oil agent, which is applied in fiber treatment, fiber type, textile and papermaking, etc., and can solve the problems of poor use effect and high cost

Inactive Publication Date: 2010-12-29
蔡云进
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing spinning and spinning oil used in the process of spinning polyester before and after spinning has defects such as poor use effect and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of oily agent for polyester staple fibers, which is made by mixing the following components by weight:

[0017] T-500 potassium lauryl phosphate 70 parts

[0018] Lauryl polyoxyethylene ether 20 parts

[0019] Glycerin 10 parts.

Embodiment 2

[0021] A kind of oily agent for polyester staple fibers, which is made by mixing the following components by weight:

[0022] T-500 potassium lauryl phosphate 62 parts

[0023] Lauryl polyoxyethylene ether 30 parts

[0024] 8 parts of glycerin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses terylene short fiber oil which is prepared by mixing T-500 potassium lauryl phosphate, lauryl polyoxyethylene ether and glycerol. The invention has the advantages of good use effect, long preservation time and low production cost and can be used as the fore-spinning and post-spinning uniform oil of terylene fibers.

Description

Technical field: [0001] The invention relates to a polyester staple fiber oil agent. Background technique: [0002] The spinning and spinning oil used in the existing polyester spinning process has defects such as poor use effect and high cost. Invention content: [0003] The object of the present invention is to provide a polyester staple fiber oil agent with good application effect. [0004] Technical solution of the present invention is: [0005] A polyester staple fiber oil is characterized in that it is made by mixing the following components by weight: [0006] T-500 Lauryl Phosphate Potassium Salt 60~80 parts [0007] Lauryl alcohol polyoxyethylene ether 10 to 30 parts [0008] 5-10 parts of glycerin. [0009] Described polyester staple fiber oil preparation is made by mixing the ingredients of the following parts by weight: [0010] T-500 potassium lauryl phosphate 70 parts [0011] Lauryl polyoxyethylene ether 20 parts [0012] Glycerin 10 parts. [0013]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/292D06M13/165D06M13/148D06M101/32
Inventor 蔡云进
Owner 蔡云进