Enhanced conductive nylon material and preparation method thereof

A nylon and raw material technology, which is applied in the field of nylon composite materials with conductive metal powder and its preparation, can solve the problems of high cost and difficult processing, and achieve the effects of simple processing, smooth surface and cost advantage.

Inactive Publication Date: 2012-01-04
NANJING HONGRUI PLASTIC PROD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to solve the disadvantages of high cost and difficult processing in current conductive plastics, and utilize the characteristics of easy processing and dispersion of glass fibers in plastics to propose a method of attaching glass fibers to metal powder for the second time, The method of blending and granulating with plastics to prepare thermoplastic conductive plastics has the characteristics of simple production process, uniform dispersion of metal powder, less addition, controllable conductivity, and smooth product surface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Enhanced conductive nylon material and preparation method thereof
  • Enhanced conductive nylon material and preparation method thereof
  • Enhanced conductive nylon material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031]

[0032] Soak the glass fiber in the mixture of coupling agent, silicone oil and copper powder for 2 hours, take it out, and dry it at room temperature for 24 hours. In the mixed solution, aminopropyltriethoxysilane accounts for 5%, silicone oil accounts for 20%, copper powder Accounted for 75%. This step is the first time the metal powder is attached to the surface of the fiberglass.

[0033] At the main feeding port of the twin-screw extruder, mix 6.1kg of PA6, 20g of antioxidant 1010, and 20g of antioxidant 168 evenly and then add them to the extruder, and pass the glass fiber with copper powder attached at a uniform speed through the aluminum treated with silicone oil. Powder (this step is the second time to attach the metal powder to the surface of the glass fiber. When the aluminum powder is treated with silicone oil, the ratio is 10% for the silicone oil and 90% for the aluminum powder.), feed it into the extruder from the side feeding port, By adjusting the ...

Embodiment 2

[0036]

[0037] Prepare copper powder mixture, 3% of aminopropyl triethoxysilane, 2% of isopropyl tri(dioctyl ichthyloxy) titanate, 5% of silicone oil, and 90% of copper powder. Soak the glass fiber in the mixture of coupling agent, silicone oil and copper powder for 2 hours, take it out, and dry it at room temperature for 24 hours. This step is the first time the metal powder is attached to the surface of the fiberglass. Then use silicone oil to treat the aluminum powder, the ratio is 5% for silicone oil and 95% for aluminum powder.

[0038] Mix 5.3kg of PA666, 20g of antioxidant 1010, and 20g of antioxidant 168 at the main feeding port of the twin-screw extruder, and then add them to the extruder, and pass the glass fiber with copper powder attached at a uniform speed through the silicone oil-treated aluminum powder (this step is the second time to attach the metal powder to the surface of the glass fiber), add it to the extruder from the side feeding port, adjust the sc...

Embodiment 3

[0041]

[0042] Soak the glass fiber in the mixture of coupling agent, silicone oil and copper powder for 2 hours, take it out, and dry it at room temperature for 24 hours. In the mixed solution, aminopropyltriethoxysilane accounts for 5%, silicone oil accounts for 10%, copper powder Accounted for 85%. This step is the first time the metal powder is attached to the surface of the fiberglass.

[0043] Mix 3.6kg of PA6, 50g of antioxidant 1010, and 50g of antioxidant 168 at the main feeding port of the twin-screw extruder, and then add them to the extruder, and pass the glass fiber with copper powder attached at a uniform speed through the aluminum treated with silicone oil. Powder (this step is the second time to attach the metal powder to the surface of the glass fiber. When the aluminum powder is treated with silicone oil, the ratio is 5% for the silicone oil and 95% for the aluminum powder.), feed it into the extruder from the side feeding port, By adjusting the extruder...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to an enhanced conductive nylon material and a preparation method thereof. The enhanced conductive nylon material comprises the following raw materials in percentage by weight: 40 to 70 percent of nylon, 10 to 40 percent of glass fibers, 10 to 40 percent of metal powder, 0.1 to 5 percent of coupling agent, 0.1 to 0.5 percent of antioxidant and 0.5 to 5 percent of silicone oil. The invention provides a method for thermoplastic conductive plastics by attaching the metal powder to the glass fibers twice and mixing the glass fibers, the metal powder and plastics for pelleting by utilizing the characteristics of easy machining and dispersion of the glass fibers in the plastics, and the prepared thermoplastic conductive plastics have the characteristics of simple and convenient production process, uniform dispersion of the metal powder, small addition amount, controlled conductivity and smooth surfaces of products.

Description

technical field [0001] The invention belongs to the technical field of thermoplastic conductive plastics, in particular to a conductive nylon composite material added with metal powder and a preparation method thereof. Background technique [0002] With the rapid development of science and technology, people's requirements for preventing electrostatic hazards and electromagnetic radiation are increasing. Due to the increasingly wide application of polymer materials such as plastics and rubber in various industries, in many applications, conductive or electromagnetic shielding requirements are also put forward for plastic products, such as electronic and electrical industries, semiconductor industries, mining machinery industries, especially And the defense industry. [0003] In order to solve these problems, people took the early stage of coating conductive paint or electroplating metal layer on the surface of plastic products. However, this method uses a large number of v...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/00C08L77/02C08L77/06C08K13/06C08K9/12C08K9/06C08K9/04C08K3/08C08K7/14H01B1/22
Inventor 张明张静志支长勇李志嘉韦嘉
Owner NANJING HONGRUI PLASTIC PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com