Prepreg mould-pressing composite material moulding process

A composite material and molding process technology, which is applied in the field of article decoration and composite material molding technology, can solve the problems of chromatic aberration and composite materials are prone to pinholes, etc., and achieve the effect of uniform resin distribution and avoid chromatic aberration

Active Publication Date: 2011-02-02
上海晋飞碳纤科技股份有限公司 +1
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is that problems such as pinholes and chromatic aberrations are likely to occur on the surface of the composite material prepared by the existing molding process, and a composite material molding process is provided to solve this problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Prepreg mould-pressing composite material moulding process
  • Prepreg mould-pressing composite material moulding process
  • Prepreg mould-pressing composite material moulding process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0047] The operating time of each step of the process of the present invention is the order below to introduce the operation process of the process:

[0048] Before preparing samples, prepare materials and molds first, cut the prepreg fabric according to the design requirements, clean the mold, and apply the HR956 mold release agent produced by Xiamen Haoer Chemical Co., Ltd. The prepreg fabric used It is the P3252S-15 / 33 prepreg fabric produced by Toray TORAYA Company, and the forming temperature of the fabric is 150°C.

[0049] Since the mold is divided into the lower mold 1 and the upper mold 5 in this embodiment, and all the operation processes of the process described in this embodiment in the upper mold are included in the operation process of the process in the lower mold 1, therefore, this embodiment The embodiment only introduces the operation flow of the process in the lower mold 1 .

[0050] Such as figure 2 As shown, the composite material described in this embo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of material preparation and relates to a prepreg mould-pressing composite material moulding process. The prepreg mould-pressing composite material moulding process aims to solve the problems that pinholes and aberration are generated on the surface of the composition material prepared by the conventional moulding process easily and the like. The invention provides a composite material moulding process. The composite material moulding process at least increases a step of adding a protective film on the surface of the composite material so as to solve the problems at the very least.

Description

technical field [0001] The invention belongs to the technical field of material preparation, and relates to a composite material forming process. The forming process of the present invention at least adds a step of adding a protective film on the surface of the composite material so as to achieve the purpose of assisting the forming of the composite material. The composite material of the present invention Generally refers to the composite material produced by the prepreg molding process, which is mainly used for article decoration. Background technique [0002] The prepreg molding process has been widely used, and it has the characteristics of stable product performance, low resin content, strong designability, and easy operation. However, the surface of the formed product is prone to problems such as pinholes and chromatic aberration, and the appearance effect is poor. It is often necessary to repair the product in the post-processing process. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/34
Inventor 罗剑岚朱家强孙昊赵鹏飞王明周新乐
Owner 上海晋飞碳纤科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com